$(Ba_{0.6-x}Sr_{0.4}Ca_{x})TiO_{3}$ (x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their stuctural and dielectric properties were investigated with variation of composition ratio and an amount of $Al_{2}O_{3}$ (0.5, 1.0, 1.5. 2.0, 3.0 wt%) doping content. As a result of the X-ray diffraction BSCT specimens showed dense and homogeneous structure without presence of the second phase. The sintered density was decreased with increase an $Al_{2}O_{3}$ doping content. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing an amount of $Al_{2}O_{3}$ doping content. The dielectric loss is minimum for BSCT doped with 1.5wt% $Al_{2}O_{3}$ content. The tunability was decreased with increasing an Ca content and is about 4.2% for BSCT(50/40/10) doped with 2.0wt% $Al_{2}O_{3}$ content.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.402-405
• /
• 2001

(Ba$\_$0.6-x/Sr$\_$0.4/Ca$\_$x/)TiO$_3$(x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their structural and dielectric properties were investigated with variation of composition ratio and an amount of Al$_2$O$_3$(0.5, 1.0, 1.5, 2.0, 3.0 wt%) doping content. As a result of the X-ray diffraction BSCT specimens showed dense and homogeneous structure without presence of the second phase. The sintered density was decreased with increase an Al$_2$O$_3$ doping content. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing an amount of Al$_2$O$_3$ doping content. The dielectric loss is minimum for BSCT doped with 1.5wt% Al$_2$O$_3$ content. The tunability was decreased with increasing an Ca content and is about 4.2% for BSCT(50/40/10) doped with 2.0wt% Al$_2$O$_3$ content.

• 마이크로전자및패키징학회지
• /
• 제2권1호
• /
• pp.29-34
• /
• 1995

Glass 물질을 첨가하여 저온소결한(Ba, Sr, Ca) TiO3 세라믹 유전체의 전기 및 기계 적 특성을 조사하였다. PbO-ZnO-B2O3 계 glass를 첨가하여 소결온도를 135$0^{\circ}C$ to 105$0^{\circ}C$ With 4wt% of glass material the sintered specimen at 115$0^{\circ}C$ for 2hrs showed a dielectric constant over 8000 with low dissipation factor. As fired ceramic capacitor satisfied the Z5U( +10~ +85$^{\circ}C$; +22% ~-56%) specifications of the EIAs. The mechanical hardness and toughness of glass reacted ceramics slightly decreased but it hows higher hardness and toughness values than Lead perovskite dielectrics.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.284-285
• /
• 2007

본 논문에서는 저소음 및 저 신호 왜곡 특성을 가지는 내환원성 유전체 원료를 개발하기 위하여 $(Ca_{0.7}Sr_{0.3})(Zr_{0.97}Ti_{0.03})O_3$에 $CaTiO_3$, $SrTO_3$, $BaTiO_3$를 첨가하여 이에 따른 유전 특성을 조사하였다. 첨가량의 조절 및 glass frit 첨가를 통하여 환원성 분위기에서도 유전율 80 ~ 100, 절연저항 (R*C) 500[ohm-F] 이상의 유전특성을 얻었다. 본 연구결과로 얻어진 유전재료를 적용하면 무소음 및 저 신호 왜곡 특성을 가지면서도 고 신뢰성의 MLCC를 제작할 수 있을 것으로 예상된다.

• 암석학회지
• /
• 제26권4호
• /
• pp.327-339
• /
• 2017

경기육괴 북서부에 분포하는 백악기 명성산화강암은 암체의 대부분을 차지하는 담홍색의 흑운모 몬조 화강암과 상대적으로 소량 산출되는 백색의 흑운모 알칼리화강암으로 이루어져 있다. 낮은 Sr 함량과 높은 Ba 함량, REE 다이아그램에서 보여지는 부(-)의 Eu 이상치, 스파이더 다이아그램에서 나타나는 부(-)의 Sr 이상치, Sr과 Rb 사이에 나타나는 부의 관계, Sr과 Ba 그리고 Sr과 $Eu/Eu^*$ 사이에 나타나는 정(+)의 관계는 사장석과 K-장석의 정출이 마그마 분화과정에 있어 중요한 역할을 하였음을 지시한다. 명성산화강암은 I, S, A형 화강암을 분류하는 분류도에서 I & S 형 화강암 영역에 도시되는데, 흑운모 몬조화강암은 분화되지 않은 I & S 형 화강암 영역에, 흑운모 알칼리화강암은 분화된 I & S 형 화강암 영역에 도시됨으로 흑운모 알칼리화강암이 흑운모 몬조화강암보다 더 분화되어 생성된 화강암임을 알 수 있다. A/CNK vs A/NK 다이아그램에서 고알루미나 영역에 도시되는 명성산화강암의 근원암의 성질을 알아보기 위하여 Rb/Sr vs Rb/Ba 도와 $Al_2O_3/TiO_2$ vs $CaO/Na_2O$ 도에 도시한 결과 명성산화강암은 점토가 결핍된 근원암인 사질암과 잡사암 사이의 조성을 갖는 변성퇴적암류로부터 유래하였거나 이에 상응하는 화성암으로부터 유래하였으며, 전암 저어콘 포화 온도를 계산해 본 결과 $740-799^{\circ}C$ 온도 조건에서 용융되어 생성되었음을 알 수 있다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.685-688
• /
• 2003

[ $(Ba,Sr,Ca)TiO_3$ ] powders, prepared by the sol-gel method, were mixed with an organic vehicle and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. The grain size decreased with increasing amounts of $MnO_2$, and the BSCT(50/40/10) thick film doped with 1wt% $MnO_2$ showed a value of 6.5mm. The thickness of thick films by four-cycle on printing/drying was approximately 100mm. The relative dielectric constant, dielectric loss and tunability of the BSCT(S0/40/10) thick films doped with 1.0wt% $MnO_2$ were 1296, 0.61% and 11.18%, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.21-22
• /
• 2007

내환원성을 가지는 (Ca,Sr)(ZrTi)$O_3$계 C0G 원료와 코어 쉘 구조를 가지는 $BaTiO_3$계 X7R 원료를 적용하여 고압용 적층 칩 캐패시터를 제작하여 내부전극 형상 및 원료에 따른 신뢰성 밑 전기적 특성을 연구하였다. C0G 특성의 원료는 X7R 원료에 비해 단위 두께당 내전압이 감소하는 경향이 적었으며 내전압 특성도 우수하게 나타났다. 또한, 내부 전극 설계에 있어 floating에 따른 영향은 C0G, X7R 특성 원료 모두 향상된 전기적 특성과 신뢰성을 가짐을 확인 할 수 있었다.

• 자원환경지질
• /
• 제40권1호
• /
• pp.47-66
• /
• 2007

봉화 북지리 마애여래좌상(국보 201호)은 흑운모 화강암으로 구성되고 NE-SW EW 및 NS 방향의 3개 절리조가 규칙적으로 나타난다. 이들은 마애여래좌상의 여러 부분을 심각하게 파손하는 기계적 풍화를 일으켰다. 이 화강암의 풍화암에서 주원소의 화학조성을 이용한 풍화지수는 토양층에서 $59{\sim}61$로 사장석이 용해되고 흑운모가 변질되어 카올린 광물의 생성이 활발한 방향으로 풍화작용이 진행되었다. 풍화도가 커질수록 주원소의 $SiO_2$, MnO는 약간 증가하는 반면에 $TiO_2,\;{Fe_2O_3}^t,\;MgO,\;CaO,\;K_2O$는 감소하는 경향을 보인다. $Al_2O_3$에 대한 미량원소의 변화량을 보면 모든 전이원소와 Rb, Y는 풍화도가 커질수록 증가하며, 반면에 Li, Sr, Ba은 감소를 나타낸다. REE의 패턴은 LREE에서 거의 일정하게 나타나지만 HREE에서 풍화도가 커질수록 증가하는 경향을 보인다. 특히 CaO, $K_2O$, Sr과 Ba의 감소는 장석들이 지하수에 용해되면서 유출된 결과이다. 마애여래좌상에서 훼손은 풍화에 의해 3방향의 절리, 착색현상, 입상분해, 미생물서식 등으로 나타난다. 풍화의 윈인은 주로 변형작용, 수분, 기온변화, 생물서식 등이다. 이 중에 수분이 화강암 내의 절리를 따라 스며들어 광물을 용해하고 분해할 뿐만 아니라 식물을 서식케 하고 결빙을 일으킨다. 북동 및 남북 절리조는 외곽부에서 내부로 연결되기 때문에 이 절리들은 빗물이 쉽게 마애여래좌상 내부로 스며들게 하여 앞으로 문화재를 훼손하는데 큰 영향을 미칠 것으로 생각된다.

• 한국화재소방학회논문지
• /
• 제19권2호
• /
• pp.75-80
• /
• 2005

적충형 PTC 서미스터의 특성연구를 위해 $(0.90Ba+0.05Sr+0.05Ca)TiO_3+0.01TiO_3+0.01SiO_2+0.0008MnO_2+0.0018Nb_2O_5$와 같은 실험조성식을 설정한 후 표면실장(SMD) 적층형 PTC 시편을 제작하였다. 그 결과 상온 비저항 값을 크게 낮출 수 있고 용도에 따라 전류용량을 크게 할 수 있었으나 적층화로 인해 peak 비저항이 크게 낮아지고 열용량이 커짐으로써 스위칭(switching)시간이 늦어지는 점을 확인하였다. 전압-전류 특성에서는 적층수가 증가할수록 초기 최대전류값이 증가하며 큐리점에 대응하여 저항값이 급격히 커지는 전이전압(전계)도 증가함을 보였다. 그러나 인가전압(전계)을 증가시킬 경우 peak 비저항값을 높일 수 있어 스위칭시간을 줄일 수 있다 이 소자는 화재감지기의 센서로 활용될 수 있다.

• Transactions on Electrical and Electronic Materials
• /
• 제8권4호
• /
• pp.149-152
• /
• 2007

[ $(Ba_{0.6}Sr_{0.3}Ca_{0.1})TiO_3$ ](BSCT) thick films doped with 0.1 mol% $MnCO_3\;and\;Yb_2O_3(0.1{\sim}0.7mol%)$ were fabricated by the screen printing method on the alumina substrates. And the structural and electrical properties as a function of $Yb_2O_3$ amount were investigated. The exothermic peak was observed at around $680^{\circ}C$ due to the formation of the poly crystalline perovskite phase. The lattice constants of the BSCT thick film doped with 0.7 mol% is 0.3994 nm. The specimen doped with 0.7 mol% $Yb_2O_3$ showed dense and uniform grains with diameters of about $4.2{\mu}m$. The average thickness of all BSCT thick films was approximately $70{\mu}m$. Relative dielectric constant and dielectric loss of the specimen doped with 0.7 mol% $Yb_2O_3$ were 2823 and 3.4%, respectively. The Curie temperature of the BSCT thick films doped with 0.1 mol% $Yb_2O_3$ was $46^{\circ}C$.