• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.84.1-84.1
• /
• 2007

• Journal of the Korean Ceramic Society
• /
• v.28 no.11
• /
• pp.935-941
• /
• 1991

Effects of calcination process and ZrO2 addition on the electrical properties of [(Ba0.82Sr0.08Ca0.1)O]m(Ti1-$\chi$Zr$\chi$)O2 ceramics have been investigated. With the variation of A/B-site ratio m of the dielectric formulations, sintering behavior and the resistivity after sintering in a reducing atmosphere have been affected by the calcination process. When the dielectric formulations of m=1.01 were sintered in a reducing atmosphere, the room-temperature resitivity of 109 {{{{ OMEGA }}.cm was obtained for samples processed with two-step calcination, which was much lower than 1012 {{{{ OMEGA }}.cm of samples calcined once. It was confirmed that high resistivity of Ca-doped BaTiO3 ceramics, after sintering in a reducing atmosphere, is maintained by acceptor-like behavior of CaTi" which is formed by Ca substitution to Ti-site. It was also found out that the critical amount of B-site Ca substitution for reduction inhibition of BaTiO3 is around 0.005 mol. With the increasing amount of ZrO2 addition to dielectric formulations, Curie peak was depressed and Curie temperature was lowered due to the enhanced diffuse phase transition.tion.

• Transactions on Electrical and Electronic Materials
• /
• v.4 no.2
• /
• pp.24-28
• /
• 2003

(Ba,Sr,Ca)TiO$_3$ powders, prepared by the sol-gel method, were mixed with organic binder and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. All the BSCT thick films, sintered at 1420$^{\circ}C$, showed the typical XRD patterns of a perovskite polycrystalline structure. The average grain sizes decreased with increasing amounts of ZrO$_2$, and the BSCT(40/40/20) thick films doped with 2wt% MnO$_2$ showed a value of 8$\mu\textrm{m}$. The thickness of thick films by four-cycle on printing/drying was approximately 951$\mu\textrm{m}$. The relative dielectric constant decreased with increasing Ca content and MnO$_2$ doping amount. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) thick films doped with 2.0wt% ZrO$_2$ were 772, 0.184％ and 15.62%, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.165-166
• /
• 2008

$(Ba_{0.6},Sr_{0.3},Ca_{0.1})TiO_3$ powders, which were prepared by sol-gel method using a solution of Ba-acetate, Sr-acetate and Ca-acetate and Ti iso-propoxide, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen-printing techniques on high purity alumina substrates. The structural and dielectirc properties were investigated for various $Pr_2O_3$ and $Y_2O_3$doping contents. As a result of thermal analysis of $(Ba_{0.6},Sr_{0.3},Ca_{0.1})TiO_3$ powders, the exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All BSCT thick films, sintered at $1420^{\circ}C$ for 2h, showed the typical XRD patterns of perovskite polycrystalline structure. The average grain size of the specimens decreased with amount of $Pr_2O_3$ and $Y_2O_3$ contents.

• Korean Journal of Crystallography
• /
• v.7 no.2
• /
• pp.165-174
• /
• 1996

The effects of Ba2+, Sr2+, and Ca2+-substitutions for Pb2+ at Pb(Zr0.52Ti0.48)O3 composition were studied for thier dielictric, piezoelectric, and aging properties. For relative dielectric constants and electromechanical coupling factors, the Ba2+-substituted composition was the highest and the Ca2+-substityed composition was the lowest. In the case of mechanical quality factors, the opposite behavior occurred. Time dependence of frequency for various ion-substituted compositions is similar to that of non-substituted composition. The piezoelectric properties after aging at high temperature was the worse than that after aging at room temperature.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.6
• /
• pp.460-465
• /
• 2001

(Ba$_{0.6-x}$Sr$_{0.4}$Ca$_{x}$)TiO$_3$(x=1.10,0.15,0.20) specimens were fabricated by the solid state reaction method and then the structural and dielectric properties as a function of he composition ratio and sintering temperature were studied. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around 102$0^{\circ}C$ due to the formation of the polycrystalline perovskite phase. The BSCT(50/40/10) specimen sintered at 150$0^{\circ}C$ showed the highest average grain size(18.25${\mu}{\textrm}{m}$). The Curie temperature and dielectric constant at room temperature decreased with increasing Ca content. The dielectric constant and dielectric loss of the BSCT(50/40/10) specimen, sintered at 145$0^{\circ}C$, were about 4324 and 0.972% at 1KHz, respectively.ively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.338-341
• /
• 2002

$(Ba_{1-x}Sr_{0.4}Ca_x)TiO_{3}$ (x=0.10, 0.15, 0.20) powders were prepared by the sol-gel method and BSCT thick films were fabricated by the screen-printing method. Their structural and dielectric properties were investigated with variation of composition ratio and $Al_{2}O_{3}$ doping contents. As results of the X-ray diffraction and microstructure analysis, the grain size of BSCT thick films was decreased with increasing $Al_{2}O_{3}$ amount. The thickness of BSCT thick films by 4-coating/drying is about $110{\sim}120{\mu}m$. The tunability increased with decreasing Ca content, and the BSCT(50/40/10) specimen doped with 1.0wt% $Al_{2}O_{3}$ showed the highest value of 12.94% at 5kV /cm.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.3
• /
• pp.37-43
• /
• 1999

Co-firing incompatibility between the low temperature sinterable Glass/ceramic and Ag-thick film was studied. The dielectric material, which has been developed for microwave frequency applications, consists of $SiO_2-TiO_2-Bi_2O_3$-$Bi_2O_3$-RO system(RO:BaO -CaO-SrO) crystallizable glass and $Al_2O_3$as a ceramic filler. The large camber in the sintered specimen and cracks at the Ag-film under the influence of the camber occurred due to the difference of densification rate between the ceramic sheet and the Ag-film $B_2O_3$addition to the Glass/ceramic mixture reduced the severe camber. The cambers decreased with increasing the $B_2O_3$ content, and completely disappeared with 14 vol% $B_2O_3$addition. With additions of $B_2O_3$, $\varepsilon_{r}$ decreased abruptly, Q$\times$f value increased largely and the $\tau_f$ value of the material quickly shifted to positive one.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.2
• /
• pp.49-52
• /
• 2009

Barium strontium calcium titanate powders were prepared with the sol-gel method. Ferroelectric $(Ba_{0.54}Sr_{0.36}Ca_{0.1})TiO_3$(BSCT) thick films were fabricated by the screen-printing method on alumina substrate. Then we investigated the structural and dielectric properties of the BSCT thick films at different sintering temperatures. The thermal analysis showed that the BSCT polycrystalline perovskite phase formed at around $660^{\circ}C$. The X-ray diffraction analysis showed a cubic perovskite structure with no second phase present in all of the BSCT thick films. The average grain size and the thickness of the specimens sintered at $1450^{\circ}C$ were about $1.6{\mu}m$ and $45{\mu}m$, respectively. The relative dielectric constant increased and the dielectric loss decreased as the sintering temperature was increased; for BSCT thick films sintered at $1450^{\circ}C$ the values of the dielectric constant and the dielectric loss were 5641 and 0.4%, respectively, at 1 kHz.

• The Journal of the Petrological Society of Korea
• /
• v.12 no.3
• /
• pp.119-134
• /
• 2003

Yuksipryeong two-mica granite presents strongly peraluminous characteristics in both mineralogy and geochemistry. It has high aluminum saturation index with 1.15∼l.20 and high corundum with 2.20∼2.98 wt% CIPW norm. As the color index is <16% and FeO$\^$T/+ MgO + TiO$_2$is average 1.9 wt％, it corresponds to leucogranite. Yuksipryeong two-mica leucogranite shows negative linear trend for TiO$_2$, Al$_2$O$_3$, FeO, Fe$_2$O$_3$, MgO, CaO, K$_2$O, P$_2$O$\_$5/, Rb, Ba, and Sr as SiO$_2$increases, and the positive relation of Zr and Th, which result from feldspar, biotite, apatite and zircon fractionation. Pegmatitic dike has higher SiO$_2$and P$_2$O$\_$5/, but lower another major elements. Yuksipryeong two-mica leucogranite has lower Rb, but higher Ba and Sr than Manaslu, Hercynian two-mica leucogranites, and S-type granites in Lachlan Fold Belt. Pegmatitic dike has higher Rb and Nb but lower Ba, Sr, Zr, Th, and Pb contents than Yuksipryeong two-mica leucogranite, resulting in removing or mobilizing for some trace elements from the granitic melt. Yuksipryeong two-mica leucogranite has total REEs with 95.7∼l23.3 ppm, and chondrite-normalized REE pattern is very steep ((La/Yb)$\_$N/ = 6.9∼24.8), light REEs (LREEs)-enriched End heavy REEs (HREEs)- depleted pattern with low to moderate Eu anomalies (Eu/Eu＊= 0.7∼0.9). While pegmatitic dike has low total REEs with 7.0 ppm, and chondrite-normalized REE pattern is flat-pattern ((La/Yb)$\_$N/ = 2.1) with strong negative Eu anomalies (Eu/Eu＊= 0.2). The melt compositions having formed two-mica leucogranites depend on not only the source rock but also the amounts of the residual remaining after melting of source rocks. The CaO/Na$_2$O and Rb/Sr-Rb/Ba ratios depend mainly on the composition of source rocks in the strongly peraluminous granite, that is, plagioclase/clay ratio of the source rocks. Yuksipryeong two-mica leucogranite has higher CaO/Na$_2$O and lower Rb/Sr-Rb/Ba ratios than Manaslu and Hercynian two-mica leucogranites (Millevaches and Gueret) derived from clay-rich, plagioclase-poor (polite), which suggest that the probable source rocks for Yuksipryeong two-mica leucogranite is clay-poor, plagioclase-rich quartzofeldspathic rocks. As the concentrations of Al$_2$O$_3$remain nearly constant but those of TiO$_2$increases as increasing temperature in the strong peraluminous melt, the Al$_2$O$_3$/TiO$_2$ratio may reflect relative temperature at which the melts have formed. Comparing the polite-derived Manaslu and Hercynian two- mica leucogranites, Manaslu two-mica leucogranite has higher Al$_2$O$_3$/TiO$_2$ratio than latter, and its melt have formed at relatively lower temperature ($\leq$ 875$^{\circ}C$) than Hercynian two-mica leucogranites. Likewise, comparing the quartzofeldspathic rock-derived granites, Yuksipryeong two-mica granite has higher Al$_2$O$_3$/TiO$_2$, ratio than S-type granites in Lachlan Fold Belt (>875$^{\circ}C$). The melt formed Yuksipryeong two-mica leucogranite are considered to have been formed at temperature at below the maximum 875$^{\circ}C$C$.