Silver nanowire-based transparent electrodes are very attractive as a next-generation flexible and transparent electrode that can replace ITO-based flexible electrodes because they have excellent conductivity, transmittance and mechanical flexibility. However, weak understanding of the silver nanowire solution for the fabrication of silver nanowire-based transparent electrodes often cause abnormal operation of the electrical device or peeling problem of the electrode films when applied to electronic devices. Here, we studied a Hydroxypropyl Methylcellulose (HPMC) adhesion promoter, which is one of the additives for silver nanowire solution, to improve the understanding of silver nanowire solution. In detail, it is characterized how the HPMC changes the properties of silver nanowire solution and silver nanowire film, which is fabricated with silver nanowire solution including the HPMC adhesion promoter. As the characteristics of solution, polar surface tension and dispersive surface tension were measured. As the film characteristics, surface energy, surface morphology, silver nanowire density, and sheet resistance were analyzed.
은 나노와이어 기반 투명전극은 우수한 전도도와 투과도, 유연성을 가지고 있어 ITO 기반의 유연전극을 대체할 수 있는 차세대 유연투명전극으로 각광받고 있다. 그러나 은 나노와이어 기반 투명전극 제작에 사용되는 은 나노와이어 용액에 대한 이해가 부족하여 전자소자 응용 시 소자의 비정상적인 작동이나 전극 필름의 박리 문제가 종종 발생하곤 한다. 본 연구에서는 은 나노와이어 용액에 대한 이해를 높이고자 은 나노와이어 용액에 사용되는 첨가제 중 하나인 hydroxypropyl methylcellulose 접착력 증진제에 대한 연구를 진행하였으며, 접착력 증진제를 첨가함에 따라 은 나노와이어 용액의 특성이 어떻게 변화되고 이러한 용액을 사용하여 제작된 은 나노와이어 필름의 특성이 어떻게 변화되는지 연구하였다. 용액의 특성으로는 극성성분의 표면장력과 분산 성분의 표면장력이 측정되었으며, 필름 특성으로는 표면 에너지와 표면 형상, 은 나노와이어 밀도, 면저항 등이 분석되었다.