Punching Test for Development of High-strength Rockfall Net

고강도 포획망 개발을 위한 펀칭시험

The high-strength rockfall net developed in this study is to replace the fallout prevention net method using PVC coating net made of core wire thickness 3.2 mm and tensile strength 290-540 MPa class steel wire. General PVC coating net have low performance, and in the event of falling rocks or surface loss, they cannot withstand the load and are torn, which rather adds to the damage. Developed rockfall net was manufactured using steel wires with a core wire thickness of 2.8 to 3.2 mm and a tensile strength of 1,000 to 2,000 MPa. Test method was referred to the international standard Steel wire rope net panels and rolls-Definitions and specifications (ISO 17746:2016), and was conducted in accordance with the provisions of the punching test. Through indoor punching tests, the load-displacement curves of the general PVC coating network and the developed high-strength capture net (1,000 and 2,000 MPa) were compared, and the maximum Pull-out load was analyzed to be improved by 324.47% (2,000 MPa high-strength net).

본 연구에서 개발하고자 하는 고강도 포획망은 심선 직경 3.2mm, 인장강도 290~540MPa급 강선으로 제작되는 일반 PVC 코팅망을 활용한 낙석방지망 공법을 대체하기 위함이다. 일반 PVC 코팅망은 그 성능이 낮아 낙석이나 표층유실이 발생할 경우 그 하중을 버티지 못하고 찢어지며 오히려 피해가 가중된다. 따라서 심선 직경 2.8~3.2mm, 인장강도 1,000~2,000MPa급 강선을 활용하여 고강도 포획망을 제작하였다. 시험 방법은 국제 기준인 Steel wire rope net panels and rolls-Definitions and specifications(ISO 17746:2016)을 참조하였으며, 펀칭시험에 대한 사항의 규정을 따라 실시하였다. 실내펀칭시험을 통해 일반 PVC 코팅망과 개발한 고강도 포획망(1,000MPa, 2,000MPa)의 하중-변위 곡선을 비교하였으며, 최대 인발력이 324.47%(고강도 포획망 2,000MPa)가 향상되는 것으로 분석되었다.