Optimal Mix Design of High-Performance, Low-Heat Self-Compacting Concrete

고성능 저발열 자기충전 콘크리트의 최적 배합설계

The foundation of high-rise concrete building in coastal areas generally must be installed in an integrated manner, not separately, in order to prevent defects caused by stress on the upper and lower parts of the mounting surface and to manage the process smoothly. However, when performing integrated punching, there is a concern that temperature stress cracks may occur due to hydration heat. Due to the large member size, it is difficult to make a sufficient commitment, so it is necessary to mix concrete with high self-charging properties to ensure workability. In this research, the amount of high-performance spray and admixture used was adjusted as experimental variables to satisfy this required performance. Through the analysis of the results for each blending variable, it was found that the unit quantity was 155kg/m³ and the cement ratio in the binder was 18%, and the target values of the pre-concrete properties and compressive strength were satisfied. A four-component binder(18% cement, 50% slag fine powder, 27% fly ash, 5% silica fume) was used.

해안지역 초고층 콘크리트 건축물 매트기초는 상하층 응력발생으로 인한 결함예방과 원활한 공정관리를 위해 일반적으로 일체타설이 요구되지만 일체타설의 경우 수화열에 의한 온도응력 균열 발생의 우려가 있으며 다짐에 대한 시공성을 확보하기 위해 높은 수준의 자기충전성의 콘크리트 배합이 필요하다. 본 연구에서는 이러한 요구성능을 만족할 수 있도록 고성능 분사제와 혼화재의 사용량을 실험변수로 배합 실험을 통해 최적량을 도출하고자 하였다. 배합 변수별 결과분석을 통해 단위수량은 155kg/m³, 결합재에서 시멘트 비율 18% 일 때 굳지 않은 콘크리트 물성 및 강도발현 목표값을 만족하는 것으로 나타났다. 4성분계(시멘트 18%, 슬래그미분말 50%, 플라이애시 27%, 실리카흄 5%)가 사용되었다.