Physicochemical characterization of two bulk fill composites at different depths

  • Received : 2020.10.02
  • Accepted : 2021.01.21
  • Published : 2021.08.31

Abstract

Objectives: This study analyzed the physical-chemical behavior of 2 bulk fill resin composites (BFCs; Filtek Bulk Fill [FBF], and Tetric-N-Ceram Bulk Fill [TBF]) used in 2- and 4-mm increments and compared them with a conventional resin composite (Filtek Z250). Materials and Methods: Flexural strength and elastic modulus were evaluated by using a 3-point bending test. Knoop hardness was measured at depth areas 0-1, 1-2, 2-3, and 3-4 mm. The translucency parameter was measured using an optical spectrophotometer. Real-time polymerization kinetics was analyzed using Fourier transform infrared spectroscopy. Results: Flexural strength was similar among the materials, while TBF showed lower elastic modulus (Z250: 6.6 ± 1.3, FBF: 6.4 ± 0.9, TBF: 4.3 ± 1.3). The hardness of Z250 was similar only between 0-1 mm and 1-2 mm. Both BFCs had similar hardness until 2-3 mm, and showed significant decreases at 3-4 mm (FBF: 33.45 ± 1.95 at 0-1 mm to 23.19 ± 4.32 at 3-4 mm, TBF: 23.17 ± 2.51 at 0-1 mm to 15.11 ± 1.94 at 3-4 mm). The BFCs showed higher translucency than Z250. The polymerization kinetics of all the materials were similar at 2-mm increments. At 4-mm, only TBF had a similar degree of conversion compared with 2 mm. Conclusions: The BFCs tested had similar performance compared to the conventional composite when used in up to 2-mm increments. When the increment was thicker, the BFCs were properly polymerized only up to 3 mm.

Keywords

Acknowledgement

The authors want to thank 3M ESPE (Uruguay) and Ivoclar-Vivadent (Uruguay) for materials donation. This study was financed in part by the Coordenacao de Aperfeicoamento de Pessoal de Nivel Superior (CAPES), Brazil (Finance Code 001).

References

  1. Garcia D, Yaman P, Dennison J, Neiva G. Polymerization shrinkage and depth of cure of bulk fill flowable composite resins. Oper Dent 2014;39:441-448. https://doi.org/10.2341/12-484-L
  2. Orlowski M, Tarczydlo B, Chalas R. Evaluation of marginal integrity of four bulk-fill dental composite materials: in vitro study. Sci World J 2015;2015:701262.
  3. Ferracane JL. Resin composite--state of the art. Dent Mater 2011;27:29-38. https://doi.org/10.1016/j.dental.2010.10.020
  4. Benetti AR, Havndrup-Pedersen C, Honore D, Pedersen MK, Pallesen U. Bulk-fill resin composites: polymerization contraction, depth of cure, and gap formation. Oper Dent 2015;40:190-200. https://doi.org/10.2341/13-324-L
  5. Kramer N, Lohbauer U, Garcia-Godoy F, Frankenberger R. Light curing of resin-based composites in the LED era. Am J Dent 2008;21:135-142.
  6. Corral Nunez C, Vildosola-Grez P, Bersezio-Miranda C, Alves-Dos Campos E, Fernandez Godoy E. Revision del estado actual de resinas compuestas bulk-fill. Rev Fac Odontol Univ Antioq 2015;27:177-196.
  7. Ferracane JL, Hilton TJ, Stansbury JW, Watts DC, Silikas N, Ilie N, Heintze S, Cadenaro M, Hickel R. Academy of dental materials guidance-resin composites: part II-technique sensitivity (handling, polymerization, dimensional changes). Dent Mater 2017;33:1171-1191. https://doi.org/10.1016/j.dental.2017.08.188
  8. Nascimento AS, de Lima EA, Durao MA, Sousa YC, Correia TC, Braz R. Marginal microleakage in Bulk Fill resins. Rev Odontol UNESP 2016;45:327-331. https://doi.org/10.1590/1807-2577.08316
  9. Al-Harbi F, Kaisarly D, Bader D, El Gezawi M. Marginal integrity of bulk versus incremental fill class II composite restorations. Oper Dent 2016;41:146-156. https://doi.org/10.2341/14-306-L
  10. El-Damanhoury H, Platt J. Polymerization shrinkage stress kinetics and related properties of bulk-fill resin composites. Oper Dent 2014;39:374-382. https://doi.org/10.2341/13-017-L
  11. Rengo C, Spagnuolo G, Ametrano G, Goracci C, Nappo A, Rengo S, Ferrari M. Marginal leakage of bulk fill composites in class II restorations: a microCT and digital microscope analysis. Int J Adhes Adhes 2015;60:123-129. https://doi.org/10.1016/j.ijadhadh.2015.04.007
  12. Ilie N, Bucuta S, Draenert M. Bulk-fill resin-based composites: an in vitro assessment of their mechanical performance. Oper Dent 2013;38:618-625. https://doi.org/10.2341/12-395-L
  13. Swift EJ Jr. Critical appraisal: bulk-fill composites, part I. J Esthet Restor Dent 2015;27:176-179. https://doi.org/10.1111/jerd.12162
  14. Khamverdi Z, Fazelian N, Aghaei M. Comparative evaluation of microleakage in class V composite resin restorations using two bulk filled resin composites and one conventional composite (grandio). Ann Dent Spec 2018;6:17-22. 
  15. Ilie N, Stark K. Curing behaviour of high-viscosity bulk-fill composites. J Dent 2014;42:977-985. https://doi.org/10.1016/j.jdent.2014.05.012
  16. Czasch P, Ilie N. In vitro comparison of mechanical properties and degree of cure of bulk fill composites. Clin Oral Investig 2013;17:227-235. https://doi.org/10.1007/s00784-012-0702-8
  17. Li X, Pongprueksa P, Van Meerbeek B, De Munck J. Curing profile of bulk-fill resin-based composites. J Dent 2015;43:664-672. https://doi.org/10.1016/j.jdent.2015.01.002
  18. International Organization for Standardization. ISO 4049:2009 Dentistry - Polymer based restorative materials. Geneva: International Organization for Standardization; 2009. 
  19. de Araujo CS, Schein MT, Zanchi CH, Rodrigues SA Jr, Demarco FF. Composite resin microhardness: the influence of light curing method, composite shade, and depth of cure. J Contemp Dent Pract 2008;9:43-50. https://doi.org/10.5005/jcdp-9-4-43
  20. Sharma G, Wu W, Dalal EN. The CIEDE2000 color-difference formula: implementation notes, supplementary test data, and mathematical observations. Color Res Appl 2005;30:21-30. https://doi.org/10.1002/col.20070
  21. Herrera-Gonzalez AM, Caldera-Villalobos M, Perez-Mondragon AA, Cuevas-Suarez CE, Gonzalez-Lopez JA. Analysis of double bond conversion of photopolymerizable monomers by FTIR-ATR spectroscopy. J Chem Educ 2019;96:1786-1789. https://doi.org/10.1021/acs.jchemed.8b00659
  22. Moraes RR, Faria-e-Silva AL, Ogliari FA, Correr-Sobrinho L, Demarco FF, Piva E. Impact of immediate and delayed light activation on self-polymerization of dual-cured dental resin luting agents. Acta Biomater 2009;5:2095-2100. https://doi.org/10.1016/j.actbio.2009.01.030
  23. Flury S, Hayoz S, Peutzfeldt A, Husler J, Lussi A. Depth of cure of resin composites: Is the ISO 4049 method suitable for bulk fill materials? Dent Mater 2012;28:521-528. https://doi.org/10.1016/j.dental.2012.02.002
  24. Masouras K, Silikas N, Watts DC. Correlation of filler content and elastic properties of resin-composites. Dent Mater 2008;24:932-939. https://doi.org/10.1016/j.dental.2007.11.007
  25. Son SA, Park JK, Seo DG, Ko CC, Kwon YH. How light attenuation and filler content affect the microhardness and polymerization shrinkage and translucency of bulk-fill composites? Clin Oral Investig 2017;21:559-565. https://doi.org/10.1007/s00784-016-1920-2
  26. Marovic D, Taubock TT, Attin T, Panduric V, Tarle Z. Monomer conversion and shrinkage force kinetics of low-viscosity bulk-fill resin composites. Acta Odontol Scand 2015;73:474-480. https://doi.org/10.3109/00016357.2014.992810
  27. Leprince JG, Palin WM, Vanacker J, Sabbagh J, Devaux J, Leloup G. Physico-mechanical characteristics of commercially available bulk-fill composites. J Dent 2014;42:993-1000. https://doi.org/10.1016/j.jdent.2014.05.009
  28. Cuevas-Suarez CE, Pimentel-Garcia B, Rivera-Gonzaga A, Alvarez-Gayosso C, Ancona-Meza AL, Grazioli G, Zamarripa-Calderon E. Examining the effect of radiant exposure on commercial photopolimerizable dental resin composites. Dent J (Basel) 2018;6:55.
  29. Abed YA, Sabry HA, Alrobeigy NA. Degree of conversion and surface hardness of bulk-fill composite versus incremental-fill composite. Tanta Dent J 2015;12:71-80. https://doi.org/10.1016/j.tdj.2015.01.003
  30. Camassari JR, Correr-Sobrinho L, Correr AB, Puppin-Rontani J, Stipp RN, Puppin-Rontani RM, Paula AB. Physical-mechanical properties of bulk fill composites submitted to biodegradation by Streptococcus mutans. Braz Dent J 2020;31:431-439. https://doi.org/10.1590/0103-6440202003196
  31. Vojdani M, Bagheri R, Khaledi AA. Effects of aluminum oxide addition on the flexural strength, surface hardness, and roughness of heat-polymerized acrylic resin. J Dent Sci 2012;7:238-244. https://doi.org/10.1016/j.jds.2012.05.008
  32. Tchorz JP, Doll R, Wolkewitz M, Hellwig E, Hannig C. Microhardness of composite materials with different organic phases in deep class II cavities: an in vitro study. Oper Dent 2011;36:502-511. https://doi.org/10.2341/10-325-L
  33. Van Ende A, De Munck J, Lise DP, Van Meerbeek B. Bulk-fill composites: a review of the current literature. J Adhes Dent 2017;19:95-109.
  34. Cidreira Boaro LC, Pereira Lopes D, de Souza AS, Lie Nakano E, Ayala Perez MD, Pfeifer CS, Goncalves F. Clinical performance and chemical-physical properties of bulk fill composites resin -a systematic review and meta-analysis. Dent Mater 2019;35:e249-e264. https://doi.org/10.1016/j.dental.2019.07.007
  35. Tomaszewska IM, Kearns JO, Ilie N, Fleming GJ. Bulk fill restoratives: to cap or not to cap--That is the question? J Dent 2015;43:309-316. https://doi.org/10.1016/j.jdent.2015.01.010
  36. Bucuta S, Ilie N. Light transmittance and micro-mechanical properties of bulk fill vs. conventional resin based composites. Clin Oral Investig 2014;18:1991-2000. https://doi.org/10.1007/s00784-013-1177-y
  37. Lee YK. Influence of filler on the difference between the transmitted and reflected colors of experimental resin composites. Dent Mater 2008;24:1243-1247. https://doi.org/10.1016/j.dental.2008.01.014
  38. Shortall AC, Palin WM, Burtscher P. Refractive index mismatch and monomer reactivity influence composite curing depth. J Dent Res 2008;87:84-88. https://doi.org/10.1177/154405910808700115
  39. Fujita K, Nishiyama N, Nemoto K, Okada T, Ikemi T. Effect of base monomer's refractive index on curing depth and polymerization conversion of photo-cured resin composites. Dent Mater J 2005;24:403-408. https://doi.org/10.4012/dmj.24.403
  40. Garoushi S, Vallittu P, Shinya A, Lassila L. Influence of increment thickness on light transmission, degree of conversion and micro hardness of bulk fill composites. Odontology 2016;104:291-297. https://doi.org/10.1007/s10266-015-0227-0
  41. Leprince JG, Palin WM, Hadis MA, Devaux J, Leloup G. Progress in dimethacrylate-based dental composite technology and curing efficiency. Dent Mater 2013;29:139-156.  https://doi.org/10.1016/j.dental.2012.11.005
  42. Fronza BM, Rueggeberg FA, Braga RR, Mogilevych B, Soares LE, Martin AA, Ambrosano G, Giannini M. Monomer conversion, microhardness, internal marginal adaptation, and shrinkage stress of bulk-fill resin composites. Dent Mater 2015;31:1542-1551. https://doi.org/10.1016/j.dental.2015.10.001
  43. Radebner J, Eibel A, Leypold M, Gorsche C, Schuh L, Fischer R, Torvisco A, Neshchadin D, Geier R, Moszner N, Liska R, Gescheidt G, Haas M, Stueger H. Tetraacylgermanes: highly efficient photoinitiators for visible-light-induced free-radical polymerization. Angew Chem Int Ed Engl 2017;56:3103-3107. https://doi.org/10.1002/anie.201611686
  44. Al-Ahdal K, Ilie N, Silikas N, Watts DC. Polymerization kinetics and impact of post polymerization on the degree of conversion of bulk-fill resin-composite at clinically relevant depth. Dent Mater 2015;31:1207-1213. https://doi.org/10.1016/j.dental.2015.07.004
  45. Al-Mansour K, Al-Sada A, Al-Sinan H. Curing depth of bulk-fill composites-an in-vitro study. Pak Oral Dent J 2015;35:270-274. 
  46. Yap AU, Pandya M, Toh WS. Depth of cure of contemporary bulk-fill resin-based composites. Dent Mater J 2016;35:503-510. https://doi.org/10.4012/dmj.2015-402
  47. Price RB, Murphy DG, Derand T. Light energy transmission through cured resin composite and human dentin. Quintessence Int 2000;31:659-667.
  48. Price RB, Derand T, Loney RW, Andreou P. Effect of light source and specimen thickness on the surface hardness of resin composite. Am J Dent 2002;15:47-53.
  49. Moszner N, Fischer UK, Ganster B, Liska R, Rheinberger V. Benzoyl germanium derivatives as novel visible light photoinitiators for dental materials. Dent Mater 2008;24:901-907. https://doi.org/10.1016/j.dental.2007.11.004