Production of Vaterite Type Calcium Carbonate by using Oyster Shell Waste with Lysine

라이신 첨가에 의한 폐 굴껍질 이용 vaterite형 탄산칼슘 제조

  • Bak, Young-Cheol (Department of Chemical Engineering Gyeongsang National University, Engineering Research Institute)
  • 박영철 (경상대학교 화학공학과)
  • Received : 2020.08.07
  • Accepted : 2020.09.09
  • Published : 2021.01.25
Download PDF
⟨ Previous Next ⟩

Abstract

The experiments to produce the vaterite type calcium carbonate were conducted for using the waste oyster shell as the recycling resources. Firstly, the oyster shell were calcinated at 800 ℃ for 24 h. Calcinated oyster shell were reacted with the nitric acid solution, and were diluted to 0.1 M Ca(NO3)2 solution. This solution was mixed with 0.1 M Na2CO3 contained 0.1 mol lysine/1 mol CaO at 20 ℃ and 600 rpm mixing condition for 1 h. The reaction products were identified to vaterite type calcium carbonate (84.5% vaterite, 15.5% calcite) by XRD and SEM analysis. Mean particle diameter was 6.87 ㎛, and the lysine content in calcium carbonate was analyzed to 0.1%.

폐기물로 대량 발생되는 굴껍질을 활용한 vaterite 형 탄산칼슘 제조 실험을 하였다. 굴껍질을 800 ℃의 온도에서 항량이 되도록 가열하여 산화칼슘이 주성분인 소성 굴껍질을 제조하였다. 이 굴껍질을 질산 용액에 녹여 0.1 M 질산칼슘 수용액을 만들고, 0.1 몰 라이신/1 몰 생석회가 첨가된 0.1 M 탄산나트륨 수용액과 20 ℃, 600 rpm 교반 조건에서 1시간동안 반응시켜 탄산칼슘을 제조하였다. XRD, SEM, Size 분석을 하고 vaterite 84.5%, calcite 15.5% 함유한 구형 탄산칼슘을 확인하였다. 평균 입경 범위는 6.87 ㎛ 이었고, 아미노산 분석에서 탄산칼슘 내의 라이신 함유량은 0.1%이었다.

Keywords

References

  1. https://www.kmi.re.kr/web/contents View.do?rbsidx=224, Korea Maritime Institute, Marine ocean statics(2018).
  2. Park, S. C., Cho, H. S. and Chung, J. D., "Feasibility Study of Paper Filler Recycling using Oyster Shell," Journal of Korea Society of Waste Management, 33(5), 513-520(2016). https://doi.org/10.9786/kswm.2016.33.5.513
  3. Song, S. M., Seong, B. I., Koo, J. H. and Kim, I. H., "Effect of Aspartic Acid and Lysine on Polymorphism of Calcium Carbonate Crystal formed by Gas-liquid Reaction," Korean Chem. Eng. Res., 49(1), 109-113(2011). https://doi.org/10.9713/kcer.2011.49.1.109
  4. Thenepalli, T., Jun, A. Y., Han, C., Ramakrishna, C., Ahn, J. W., "A Strategy of Precipitated Calcium Carbonate (CaCO3) Fillers for Enhancing the Mechanical Properties of Polypropylene Polymers," Korean J. Chem. Eng., 32(6), 1009-1022(2015). https://doi.org/10.1007/s11814-015-0057-3
  5. Maruo Calcium, "Monodispersed Vaterite type Calcium Carbonate, and Shape Control Method," Korea Patent No 10-0176250(1998).
  6. KAIST, "Method for preparing Hydroxyapatite from Vaterite containing Catechol Amine," Korea Patent No 10-1318348(2013).
  7. Lyu, S. G,, Ryu, S. O., Park, Y, H. and Sur, G. S., "The preparation of Spherical Vaterite in the presence of NH4Cl by Carbonation Process," Korean Chem. Eng. Res., 36(2), 262-266(1998).
  8. Kang, Y. C. and Park, S. B., "Preparation of Cubic-type Calcium Carbonate particles from High Concentration Calcium Hydroxide Suspension by Controlling Hydration Temperature of Calcium Oxide," Korean Chem. Eng. Res., 35(6), 846-849(1997).
  9. Lee, S. G., Jung, W. M., Kim, W. S. and Choi, C. K., "Effect of Agitation on Gas-Liquid Reaction Crystallization of Calcium Carbonate in an MSMPR Reactor," Korean Chem. Eng. Res., 36(1), 49-55(1998).
  10. Saksono, N., Gozan, M., Bismo, S, Krisanti, E., Widaningrum, R. and Song, S. K., "Effects of Magnetic Field on Calcium Carbon ate Precipitation : Ionic and Particle Mechanism," Korean J. Chem. Eng., 25(5), 1145-1150(2008). https://doi.org/10.1007/s11814-008-0188-x
  11. Han, H. K., Kim, B. M. and Kim, J. A., "Influence of Temperatures and PAA Solution in the Formation of Calcium Carbonate Crystal," Korean Chem. Eng. Res., 46(6), 1052-1056(2008).
  12. Kim, J. H., Kim, J. M., Kim, W. S. and Kim, I. H., "Polymorphism of Calcium Carbonate Crystal by Silk Digested Amino Acid," Korean Chem. Eng. Res., 46(6), 1107-1112(2008).
  13. Kim, J. H., Kim, J. M., Kim, W. S. and Kim, I. H., "Polymorphism of Calcium Carbonate Crystal by addition of various Amino," Korean Chem. Eng. Res., 47(2), 213-219(2009).
  14. Kim, J. H., Song, S. M., Kim, J. M., Kim, W. S. and Kim, I. H., "CaCO3 Crystallization with feeding of Aspartic Acid," Korean J. Chem. Eng., 27(5), 1532-1537(2010). https://doi.org/10.1007/s11814-010-0245-0
  15. Son, C., Song, W., Hwang D. S., Hong, Y. K., Joo, J. and Choi, Y. S., "Recombinant Production and Biochemical Characterization of a Hypothetical Acidic Shell Matrix Protein in Escherichia Coli for the preparation of Protein-based CaCO3 Biominerals," Korean J. Chem. Eng., 33(8), 2406-2410(2016). https://doi.org/10.1007/s11814-016-0091-9
  16. Song, S. M., Seong, B. I., Koo, J. H. and Kim, I. H., "Effect of Aspartic Acid and Lysine on Polymorphism of Calcium Carbonate Crystal Formed by Gas-Liquid Reaction," Korean Chem. Eng. Res., 49(1), 109-113(2011). https://doi.org/10.9713/kcer.2011.49.1.109
  17. Kralj, D. and Brecevic, L., "Vaterite Growth and Dissolution in Aqueous Solution 1. Kinetics of Crystal growth," J. Crystal Growth, 104, 793-800(1990). https://doi.org/10.1016/0022-0248(90)90104-S
  18. Albeck, S., Weiner, S. and Addadi, L., "Polysaccharides of Intracrystalline Glycoproteins Modulate Calcite Crystal Growth In vitro," Chem. Eur. J., 2(3), 278-284(1996). https://doi.org/10.1002/chem.19960020308
  19. Zhang, S. and Gonsalves, K. E., "Influence of the Chitosan Surface Profile on the Nucleation and Growth of Calcium Carbonate Films," Langmuir, 14, 6761-6766(1998). https://doi.org/10.1021/la970962s
  20. Ogino, T., Suzuki, T. and Sawada, K., "The Rate and Mechanism of Polymorphic Transfomation of Calcium Carbonate in Water," Journal of Crystal Growth, 100, 159-167(1990). https://doi.org/10.1016/0022-0248(90)90618-U
  21. Rao, M. S., "Kinetics and Mechanism of the Transformation of Vaterite to Cacite," Bulletin of the Chemical Society of Japan, 46, 1414-1417(1973). https://doi.org/10.1246/bcsj.46.1414
  22. Kontoyannis, C. and Vagenas, N. V., "Calcium Carbonate Phase Analysis using XRD and FT-Raman Spectroscopy," Analyst, 125, 251-255(2000). https://doi.org/10.1039/a908609i
  23. Lyu, S. G., Sur, G. S. and Kang, S. H., "A Study of Crystal Shape of the precipitated Calcium Carbonate formed in the Emulsion State," Korean Chem. Eng. Res., 35(2), 186-191(1997).
  24. Han, H. K., Jeong, O. H., Lim, M. H. and Kim, J. A., "Effect of RPM and Temperature on the CSD in the CMSMPR Calcium Carborate Crystallization," Korean Chem. Eng. Res., 44(3), 289-293(2006).