Abstract
Fumigation treatment is mainly used on dead trees affected by the oak wilt disease to prevent the spread of damage. To verify the possibility of intensive use of the damaged Mongolian Oak wood treated by the fumigation treatment, we performed the compression and bending performance evaluation of the fumigation treated wood. The fumigation was done with Nemasect (Metam-sodium) for about 9 months. The dry longitudinal compressive strength of the fumigation treated oak wilt-diseased wood at the ambient temperature and humidity, and the compressive modulus of elasticity were measured to be 58.87MPa, and 5.66GPa, which were similar to the non-treated wood. The strength performance of mature wood of fumigation treated wood was 16% higher than that of juvenile wood. The compression fracture of the non-treated oak wood showed various shapes, however, most of the fumigation treated wood showed shear-type fracture shape. The bending strength of the fumigate treated wood was measured to be 157.43MPa, which was 8% higher than that of the non-treated wood, and the bending modulus of elasticity was measured to be 16.38GPa, which was 16% lower than that of the non-treated wood. However, it was confirmed that the coefficient of variation for the bending strength performance value of the fumigation treated wood was lower than that of the non-treated wood.
참나무시들음병 고사목으로부터 피해확산을 막기위해 주로 훈증처리 방법을 이용한다. 훈증처리에 따른 신갈나무 피해목의 강도적 활용 가능성을 검증하기 위해 훈증처리목재의 압축성능과 휨성능평가를 수행하였다. 훈증처리목재는 약 9개월 간 네마섹트(Metam-sodium)로 훈증처리하였다. 참나무시들음병 훈증처리목재의 기건 종압축강도는 58.87 MPa, 압축탄성계수는 5.66 GPa로 측정되었으며 건전목과 비슷한 경향을 보였다. 혼증목의 성숙재부 강도성능은 미성숙재부보다 16% 더 높은 강도값을 보였다. 참나무 건전목의 압축파괴형상은 다양한 형상으로 나타나지만 훈증처리목재의 경우 대부분 전단형 파괴형상을 보였다. 훈증처리목재의 휨강도는 157.43 MPa로 건전재보다 8% 높게 측정되었고 휨 탄성계수는 16.38 GPa로 건전재보다 16% 낮게 측정되었다. 그러나 훈증처리목재의 휨강도성능치에 대한 변동계수는 건전목보다 낮은 것을 확인하였다.