Role of residual ferrites on crevice SCC of austenitic stainless steels in PWR water with high-dissolved oxygen

  • 투고 : 2020.02.04
  • 심사 : 2020.04.23
  • 발행 : 2020.11.25
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

The crevice stress corrosion cracking (SCC) susceptibility of austenitic stainless steels was evaluated in simulated pressurized water reactor (PWR) environments. To simulate the abnormal condition in temporary clamping devices on leaking small bore pipes, crevice bent beam (CBB) tests were performed in the oxygenated as well as hydrogenated conditions. No SCC cracks were found for SS316 in both conditions. SS304 also showed good resistance in the hydrogenated condition. However, all SS304 specimens showed SCC cracks in the oxygenated condition, indicating poor crevice SCC resistance. It was found that residual ferrites were selectively dissolved because of the galvanic corrosion coupled with the neigh-bouring austenite phase, resulting in SCC initiation in SS304. Crack morphologies were mostly transgranular assisted by the damaged δ-ferrite and deformation-induced slip bands.

키워드

참고문헌

  1. J. Xiu, H. Jing, Y. Han, L. Zhao, L. Xu, Effect of groove on socket welds under the condition of vibration fatigue, J. Nucl. Mater. 433 (2013) 10-16. https://doi.org/10.1016/j.jnucmat.2012.08.051
  2. Vibration Fatigue Testing of Socket Welds (PWRMRP-07), EPRI, Palo Alto, CA, 1999.
  3. Y.H. Choi, S.Y. Choi, Socket weld integrity in nuclear piping under fatigue loading condition, Nucl. Eng. Des. 237 (2007) 213-218. https://doi.org/10.1016/j.nucengdes.2006.06.005
  4. D.N. Hopkins, D.J. Benac, Investigation of fatigue-induced socket-welded joint failures for small-bore piping used in power plants, Practical Fail. Anal. 1 (2001) 71-82. https://doi.org/10.1007/BF02715165
  5. P. Hirschberg, P.C. Riccardella, M. Sullivan, R. Carter, Vibration Fatgiue Testing of Socket Welds, Phase II, Pennsylvania State University CiteSeerx, 1998, pp. 1-13 (Available Online).
  6. W. Kuang, X. Wu, E.H. Han, Influence of dissolved oxygen concentration on the oxide film formed on Alloy 690 in high temperature water, Corrosion Sci. 69 (2013) 197-204. https://doi.org/10.1016/j.corsci.2012.12.003
  7. L. Zhang, J. Wang, Effect of dissolved oxygen content on stress corrosion cracking of a cold worked 316L stainless steel in simulated pressurized water reactor primary water environment, J. Nucl. Mater. 446 (2014) 15-26. https://doi.org/10.1016/j.jnucmat.2013.11.027
  8. M. Fontana, Corrosion Engineering, Corrosion Engineering, third ed., Mcgraw-Hill International, 1986, pp. 40-60.
  9. P.L. Andresen, Emerging issues and fundamental processes in environmental cracking in hot water, Corrosion 64 (2008) 439-464. https://doi.org/10.5006/1.3278483
  10. W. Kuang, X. Wu, E.H. Han, The oxidation behaviour of 304 stainless steel in oxygenated high temperature water, Corrosion Sci. 52 (2010) 4081-4087. https://doi.org/10.1016/j.corsci.2010.09.001
  11. J. Kuniya, I. Masaoka, R. Sasaki, Effect of cold work on the stress corrosion cracking of nonsensitized aisi 304 stainless steel in high-temperature oxygenated water, Corrosion 44 (1988) 21-28. https://doi.org/10.5006/1.3582020
  12. M. Hansson, S. Yamamoto, Stress corrosion cracking testing of non-sensitised stainless steel, Ski Rep (2004) 1-36, 200429.
  13. J. Isselin, R. Kasada, A. Kimura, Work hardening, sensitization, and potential effects on the susceptibility to crack initiation of 316L stainless steel in BWR environment, J. Nucl. Sci. Technol. 48 (2011) 1462-1470. https://doi.org/10.1080/18811248.2011.9711839
  14. N. Ishiyama, M. Mayuzumi, Y. Mitzutani, J. Tani, Stress corrosion cracking of type 316 and 316L stainless steels in high temperature water, in: Proc. 12th Int. Conf. Environ. Degrad. Mater. Nucl. Power Syst. React, 2005, pp. 57-64.
  15. B. Beverskog, I. Puigdomenech, Pourbaix diagrams for the ternary system of iron-chromium-nickel, Corrosion 55 (1999) 1077-1087. https://doi.org/10.5006/1.3283945
  16. D. Cubicciotti, Potential-pH diagrams for alloy-water systems under LWR conditions, J. Nucl. Mater. 201 (1993) 176-183. https://doi.org/10.1016/0022-3115(93)90173-V
  17. W. Kuang, X. Wu, E.H. Han, Influence of dissolved oxygen concentration on the oxide film formed on 304 stainless steel in high temperature water, Corrosion Sci. 63 (2012) 259-266. https://doi.org/10.1016/j.corsci.2012.06.007
  18. B. Stellwag, The mechanism of oxide film formation on austenitic stainless steels in high temperature water, Corrosion Sci. 40 (1998) 337-370. https://doi.org/10.1016/S0010-938X(97)00140-6
  19. Y. Asakura, H. Karasawa, M. Sakagami, S. Uchida, Relationships between corrosion behavior of AISI 304 stainless steel in high-temperature pure water and lts oxide film structures, Corrosion 45 (1989) 119-124. https://doi.org/10.5006/1.3577828
  20. T. Magnin, A. Chambreuil, B. Bayle, The corrosion-enhanced plasticity model for stress corrosion cracking in ductile fcc alloys, Acta Mater. 44 (1996) 1457-1470. https://doi.org/10.1016/1359-6454(95)00301-0
  21. S. Lozano-perez, T. Yamada, T. Terachi, M. Schro, Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content, Acta Mater. 57 (2009) 5361-5381. https://doi.org/10.1016/j.actamat.2009.07.040
  22. P. Fejes, L. Ljungberg, L. Unneberg, Impurity effects in BWR water chemistry, Int. J. Pres. Ves. Pip. 34 (1988) 47-57. https://doi.org/10.1016/0308-0161(88)90041-5
  23. C. Ornek, D.L. Engelberg, Towards understanding the effect of deformation mode on stress corrosion cracking susceptibility of grade 2205 duplex stainless steel, Mater. Sci. Eng. 666 (2016) 269-279. https://doi.org/10.1016/j.msea.2016.04.062
  24. C.L. Lai, W.F. Lu, J.Y. Huang, Effect of ${\delta}$-ferrite content on the stress corrosion cracking behavior of cast austenitic stainless steel in high-temperature water environment, Corrosion 70 (2014) 591-597. https://doi.org/10.5006/1155
  25. Y.H. Lu, Q.J. Peng, T. Sato, T. Shoji, An ATEM study of oxidation behavior of SCC crack tips in 304L stainless steel in high temperature oxygenated water, J. Nucl. Mater. 347 (2005) 52-68. https://doi.org/10.1016/j.jnucmat.2005.07.006
  26. F.P. Ford, Quantitative prediction of environmentally assisted cracking, Corrosion 52 (1996) 375-395. https://doi.org/10.5006/1.3292125
  27. N. Saito, H. Sakamoto, K. Sugimoto, Crevice corrosion of austenitic alloys in high-temperature water, Corrosion 54 (1998) 700-712. https://doi.org/10.5006/1.3284889
  28. S. Ghosh, V. Kain, Microstructural changes in AISI 304L stainless steel due to surface machining : effect on its susceptibility to chloride stress corrosion cracking, J. Nucl. Mater. 403 (2010) 62-67. https://doi.org/10.1016/j.jnucmat.2010.05.028
  29. C. Garcia, F. Martin, P. De Tiedra, J.A. Heredero, M.L. Aparicio, Effects of prior cold work and sensitization heat treatment on chloride stress corrosion cracking in type 304 stainless steels, Corrosion Sci. 43 (2001) 1519-1539. https://doi.org/10.1016/S0010-938X(00)00165-7
  30. Y.Z. Huang, J.M. Titchmarsh, TEM investigation of intergranular stress corrosion cracking for 316 stainless steel in PWR environment, Acta Mater. 54 (2006) 635-641. https://doi.org/10.1016/j.actamat.2005.10.011
  31. Y.F. Shen, X.X. Li, X. Sun, Y.D. Wang, L. Zuo, Twinning and martensite in a 304 austenitic stainless steel, Mater. Sci. Eng. 552 (2012) 514-522. https://doi.org/10.1016/j.msea.2012.05.080