Study the effect of machining process and Nano Sio2 on GFRP mechanical performances

  • Afzali, Mohammad (Department of Mechanical Engineering, Sari Branch, Islamic Azad University) ;
  • Rostamiyan, Yasser (Department of Mechanical Engineering, Sari Branch, Islamic Azad University)
  • Received : 2019.05.17
  • Accepted : 2020.10.30
  • Published : 2020.10.25

Abstract

In this study, the effect of Nano silica (SiO2) on the buckling strength of the glass fiber reinforced laminates containing the machining process causes holes were investigated. The tests have been applied on two status milled and non-milled. To promote the mechanical behavior of the fiber-reinforced glass epoxy-based composites, Nano sio2 was added to the matrix to improve and gradation. Nano sio2 is chosen because of flexibility and high mechanical features; the effect of Nanoparticles on surface serenity has been studied. Thus the effect of Nanoparticles on crack growth and machining process and delamination caused by machining has been studied. We can also imply that many machining factors are essential: feed rate, thrust force, and spindle speed. Also, feed rate and spindle speed were studied in constant values, that the thrust forces were studied as the main factor caused residual stress. Moreover, entrance forces were measured by local calibrated load cells on machining devices. The results showed that the buckling load of milled laminates had been increased by about 50% with adding 2 wt% of silica in comparison with the neat damaged laminates while adding more contents caused adverse effects. Also, with a comparison of two milling tools, the cylindrical radius-end tool had less destructive effects on specimens.

Keywords

References

  1. Arani, A.G., Maghamikia, S., Mohammadimehr, M. and Arefmanesh, A. (2011), "Buckling analysis of laminated composite rectangular plates reinforced by SWCNTs using analytical and finite element methods", J. Mech. Sci. Technol., 25(3), 809-820. https://doi.org/10.1007/s12206-011-0127-3.
  2. Azadi, R. and Rostamiyan, Y. (2015), "Experimental and analytical study of buckling strength of new quaternary hybrid nanocomposite using Taguchi method for optimization", Construct. Build. Mater., 88, 212-224. https://doi.org/10.1016/j.conbuildmat.2015.04.018.
  3. Bhatnagar, N., Ramakrishnan, N., Naik, N.K. and Komanduri, R. (1995), "On the machining of fiber reinforced plastic (FRP) composite laminates", J. Machine Tools Manufacture, 35(5), 701-716. https://doi.org/10.1016/0890-6955(95)93039-9.
  4. Butler, R. (2015), 4 - Buckling and Compressive Strength of Laminates with Optimized Fibre-Steering and Layer-Stacking for Aerospace Applications, Woodhead Publishing, Sawston, United Kingdom.
  5. Campos Rubio, J., Abrao, A.M., Faria, P.E., Correia, A.E. and Davim, J.P. (2008), "Effects of high speed in the drilling of glass fibre reinforced plastic: Evaluation of the delamination factor", J. Machine Tools Manufacture, 48(6), 715-720. https://doi.org/10.1016/j.ijmachtools.2007.10.015.
  6. Caprino, G. and Tagliaferri, V. (1995), "Damage development in drilling glass fibre reinforced plastics", J. Machine Tools Manufacture, 35(6), 817-829. https://doi.org/10.1016/0890-6955(94)00055-O.
  7. Chen, S. and Feng, J. (2014), "Epoxy laminated composites reinforced with polyethyleneimine functionalized carbon fiber fabric: Mechanical and thermal properties", Compo. Sci. Technol., 101, 145-151. https://doi.org/10.1016/j.compscitech.2014.07.003.
  8. Chen, X., Yuan, L., Zhang, Z., Wang, H., Liang, G. and Gu, A. (2015), "New glass fiber/bismaleimide composites with significantly improved flame retardancy, higher mechanical strength and lower dielectric loss", Compos. Part B Eng., 71(0), 96-102. https://doi.org/10.1016/j.compositesb.2014.11.001.
  9. Choi, S.W., Li, M., Lee, W.I. and Kim, H.S. (2014), "Analysis of buckling load of glass fiber/epoxy-reinforced plywood and its temperature dependence", J. Compos. Mater., 48(18), 2191-2206. https://doi.org/10.1177/0021998313495071.
  10. Davim, J.P. and Reis, P. (2005), "Damage and dimensional precision on milling carbon fiber-reinforced plastics using design experiments", J. Mater. Process Technol., 160(2), 160-167. https://doi.org/10.1016/j.jmatprotec.2004.06.003.
  11. Elamary, A.S. and Abd-ELWahab, R.K (2016), "Numerical simulation of concrete beams reinforced with composite GFRP-Steel bars under three points bending", Struct. Eng. Mech., 57(5), 937-949. https://doi.org/10.12989/sem.2016.57.5.937.
  12. Eronat, N., Candan, U. and Turkun, M. (2009), "Effects of glass fiber layering on the flexural strength of microfill and hybrid composites", J. Esthetic and Restorative Dentistry, 21(3), 171-178. discussion 179-181. https://doi.org/10.1111/j.1708-8240.2009.00259.x.
  13. Ghosh, P.K., Kumar, K. and Chaudhary, N. (2015), "Influence of ultrasonic dual mixing on thermal and tensile properties of MWCNTs-epoxy composite", Compos. Part B Eng., 77, 139-144. https://doi.org/10.1016/j.compositesb.2015.03.028.
  14. Icardi, U. (1998), "Cylindrical bending of laminated cylindrical shells using a modified zig-zag theory", 6(5), 497-516. https://doi.org/10.12989/sem.1998.6.5.497.
  15. Kelly, G. and Hallstrom, S. (2004), "Bearing strength of carbon fibre/epoxy laminates: effects of bolt-hole clearance", Compos. Part B Eng., 35(4), 331-343. https://doi.org/10.1016/j.compositesb.2003.11.001.
  16. Kheirikhah, M.M., Khalili, S.M.R. and Malekzadeh Fard, K. (2012), "Analytical solution for bending analysis of soft-core composite sandwich plates using improved high-order theory", Struct. Eng. Mech.,44(1), 15-34. https://doi.org/10.12989/sem.2012.44.1.015.
  17. Klasztorny, M., Nycz, D. and Labuda, R. (2018), "Modelling, simulation and experimental validation of bend tests on GFRP laminate beam and plate specimens", Compos. Struct., 184, 604-612. https://doi.org/10.1016/j.compstruct.2017.10.046.
  18. Konig, W. and Grass, P. (1989), "Quality Definition and Assessment in Drilling of Fibre Reinforced Thermosets", CIRP Annals. Manufact. Technol., 38(1), 119-124. https://doi.org/10.1016/S0007-8506(07)62665-1.
  19. Liu, F.R., Zhao, J.J., Zhang, Q., He, C. and Chen, J.M. (2012), "Processing and characterizations of 2%PF/silica sand core-shell composite powders by selective laser sintering with a higher transmittance fiber laser", J. Machine Tools Manufact., 60, 52-58. https://doi.org/10.1016/j.ijmachtools.2012.05.003.
  20. Mohan, N.S., Kulkarni, S.M. and Ramachandra, A. (2007), "Delamination analysis in drilling process of glass fiber reinforced plastic (GFRP) composite materials", J. Mater. Process Technol., 186(1-3), 265-271. https://doi.org/10.1016/j.jmatprotec.2006.12.043.
  21. N. Rajesh Mathivanan, B.S.M., H. Anup Shetty (2016), "An experimental investigation on the process parameters influencing machining forces during milling of carbon and glass fiber laminates", Measurement, 91, 39-45. https://doi.org/10.1016/j.measurement.2016.04.077.
  22. Osmannezhad, S., Faezipour, M. and Ebrahimi, G. (2014), "Effects of GFRP on bending strength of glulam made of poplar (Populus deltoids) and beech (Fagus orientalis)", Construct. Build. Mater., 51, 34-39. https://doi.org/10.1016/j.conbuildmat.2013.10.035.
  23. Persson, E., Eriksson, I. and Zackrisson, L. (1997), "Effects of hole machining defects on strength and fatigue life of composite laminates", Compos. Part A Appl. Sci. Manufact., 28(2), 141-151. https://doi.org/10.1016/S1359-835X(96)00106-6.
  24. Persson, E., Madenci, E. and Eriksson, I. (1998), "Delamination initiation of laminates with pin-loaded holes", Theoretical Appl. Fracture Mech., 30(2), 87-101. https://doi.org/10.1016/S0167-8442(98)00046-9.
  25. Shahkhosravi, N.A., Yousefi, J., Najafabadi, M.A., Burvill, C. and Minak, G. (2019), "Fatigue life reduction of GFRP composites due to delamination associated with the introduction of functional discontinuities", Compos. Part B Eng., 163, 536-547. https://doi.org/10.1016/j.compositesb.2019.01.005.
  26. Tagliaferri, V., Caprino, G. and Diterlizzi, A. (1990), "Effect of drilling parameters on the finish and mechanical properties of GFRP composites", J. Machine Tools Manufacture, 30(1), 77-84. https://doi.org/10.1016/0890-6955(90)90043-I.
  27. Turki, Y., Habak, M., Velasco, R., Aboura, Z., Khellil, K. and Vantomme, P. (2014), "Experimental investigation of drilling damage and stitching effects on the mechanical behavior of carbon/epoxy composites", J. Machine Tools Manufacture, 87, 61-72. https://doi.org/10.1016/j.ijmachtools.2014.06.004.
  28. Withers, G.J., Yu, Y., Khabashesku, V.N., Cercone, L., Hadjiev, V.G., Souza, J.M. and Davis, D.C. (2015), "Improved mechanical properties of an epoxy glass-fiber composite reinforced with surface organomodified nanoclays", Compos. Part B Eng., 72(0), 175-182. https://doi.org/10.1016/j.compositesb.2014.12.008.
  29. Youssef, J. and Hadi, M.N.S. (2017), "Axial load-bending moment diagrams of GFRP reinforced columns and GFRP encased square columns", Construct. Build. Mater., 135, 550-564. https://doi.org/10.1016/j.conbuildmat.2016.12.125.
  30. Zitoune, R., Crouzeix, L., Collombet, F., Tamine, T. and Grunevald, Y.H. (2011), "Behaviour of composite plates with drilled and moulded hole under tensile load", Compos. Struct., 93(9), 2384-2391. https://doi.org/10.1016/j.compstruct.2011.03.027.