Abstract
Purpose: This paper aims to develop an asphalt pavement system with reduced cracks, structural stability and waterproofing at sub-zero temperature conditions. Method: Under various temperature conditions, SIS polymer asphalt, normal asphalt, and guss asphalt were tested for adhesion strength of the binder and deformation strength of the mixture. Result: The adhesion strength of asphalt binder was higher in SIS polymer asphalt than that of normal asphalt and guss asphalt. The deformation strength of the asphalt mixture was almost the same as that of SIS polymer asphalt and normal asphalt. The energy absorption of the SIS polymer asphalt mixture was relatively higher than that of the normal asphalt mixture and the guss asphalt mixture. Conclusion: The maximum load of the SIS polymer asphalt mixture was lower than that of the guss asphalt mixture. However, in sub-zero temperature conditions, sufficient energy absorption was secured by stable load reduction. Therefore, it is expected to improve the durability of asphalt pavement by reducing the occurrence of microcracks with stable fracture behavior.
연구목적: 영하의 조건에서도 균열발생을 억제하고, 구조적으로 안정된 성능과 방수기능을 동시에 발휘하는 아스팔트 포장시스템을 개발하고자 한다. 연구방법: SIS 폴리머 아스팔트, 일반 아스팔트 및 구스아스팔트를 대상으로 다양한 온도조건에 따른 유제의 부착실험 및 혼합물의 변형강도 실험을 실시하여 그 특성을 비교, 분석하였다. 연구결과: 아스팔트 유제의 부착강도는 SIS 폴리머 아스팔트가 일반 아스팔트 및 구스아스팔트에 비해 높은 것으로 나타났다. 아스팔트 혼합물의 변형강도는 SIS 폴리머 아스팔트와 일반 아스팔트가 거의 동일하게 나타났다. SIS 폴리머 아스팔트 혼합물은 일반 아스팔트 혼합물 및 구스아스팔트 혼합물에 비해 에너지흡수량이 상대적으로 높게 나타났다. 결론: SIS 폴리머 아스팔트 혼합물의 최대하중은 구스아스팔트 혼합물에 비해 낮게 나타났지만, 열악한 온도조건에서도 최대하중 이후에 안정적인 하중감소로 충분한 에너지흡수량을 확보하고 있고, 안정적인 파괴거동으로 미세균열 발생 등을 감소시켜 아스팔트 포장의 내구성 향상에 기여할 수 있을 것으로 판단된다.