Effect of Surface Film on Void Behavior in Composite Integrated Structure

표면접착필름이 복합재 일체형 구조물에서의 기공 거동에 미치는 영향

  • Received : 2020.02.01
  • Accepted : 2020.05.30
  • Published : 2020.06.30

Abstract

In this study, void behavior of composite laminate by local internal pressure gradient due to structural geometry and surface film application condition was experimentally evaluated through fabrication of spar/skin integrated structure specimens. Viscosity comparison and thermal analysis for both carbon fiber prepreg and surface film were conducted and cure characteristic and rate difference were analyzed. 2 types of spar/skin integrated structural specimens were prepared based on different application condition of surface film. Subsequently, those specimens were evaluated through visual surface inspection, non-destructive and destructive inspection. In a specimen #1 with full application of surface film, low pressurized area of composite laminate created by pressure gradient of structural geometry had voids. It exhibited that voids could not be evacuated and were locked in cured laminate by the influence of pre-cured surface film with relatively faster cure rate. In a specimen #2 without surface film, it revealed that all internal voids disappeared in the cured laminate. Therefore, it is verified that surface film acts as barrier film preventing void movement and evacuation during autoclave cure.

본 연구에서는 스파/스킨 복합재 일체형 구조물 시편 제작을 통해 구조물 형상에 의한 국부적인 내부압력 구배 및 표면접착필름 적용 조건에 따른 복합재 내부 기공의 거동에 대하여 실험적으로 평가하였다. 표면접착 필름과 탄소섬유 프리프레그 소재의 점도특성 및 열분석 비교를 통해 경화특성 및 속도 차이를 확인하였다. 그리고 스파/스킨 일체형 구조물 시편을 표면접착필름 적용 조건에 따라 2가지 유형으로 성형 제작하여 표면상태검사, 비파괴 검사 및 파괴 검사를 통하여 검증하였다. 표면접착필름이 전체 표면에 적용된 시편#1의 경우 내부구조에 의한 압력 구배가 발생하고 이로 인해 낮은 압력이 적용되는 부위에서 형성된 기공들이 먼저 경화된 표면접착필름에 막혀 배출되지 못함을 확인할 수 있었으며, 표면접착필름이 적용되지 않아 탄소섬유 프리프레그가 전면 노출된 시편#2에서는 내부 기공이 완전히 배출됨을 볼 수 있었으며 미리 경화된 표면접착필름이 내부 기공 이동 및 배출에 있어서 차단막(Barrier film)으로 작용할 수 있음을 확인하였다.

Keywords

References

  1. Pora, J., "Composite Materials in the Airbus A380 - from History to Future", Proceeding of the 13 International Committee on Composite Materials, Beijing, China, 2001.
  2. Marsh, G., "Airbus Takes on Boeing with Reinforced Plastic A350", Reinforced Plastics, Vol. 51, Issue 11, 2007, pp. 26-29. https://doi.org/10.1016/S0034-3617(07)70383-1
  3. Fernlund, G., Wells, J., Fahrang, L., Kay, J., and Poursartip, A., "Causes and Remedies for Porosity in Composite Manufacturing", Materials Science and Engineering, No. 139, 2016.
  4. Liu, L., Zhang, B., Wu, Z., and Wang, D., "Effects of Cure Pressure Induced Voids on the Mechanical Strength of Carbon/Epoxy Laminates", Science Technology, Vol. 21, No. 1, 2005, pp. 87-91.
  5. Di Landroa, L., Montaltob, A., Bettinia, P., Guerrac, S., Montagnolid, F., and Rigamontic, M., "Detection of Voids in Carbon/Epoxy Laminates and Their Influence on Mechanical Properties", Polymers & Polymer Composites, Vol. 25, No. 5, 2017, pp. 371-380. https://doi.org/10.1177/096739111702500506
  6. Liu, X., and Chen, F., "A Review of Void Formation and its Effects on the Mechanical Performance of Carbon Fiber Reinforced Plastic", Engineering Transactions, Vol. 64, No. 1, 2016, pp. 33-51.
  7. Gardiner, G., Out-of-Autoclave Prepregs: Hype or Revolution? Retrieved from Composites World website: http://www.compositesworld.com/articles/out-of-autoclave-prepregs-hype-orrevolution, 2011.
  8. Wells, J., Behaviour of Resin Voids in Out-of-Autoclave Prepreg Processing, Master Thesis, University of British Columbia, Canada, 2014.
  9. Roy, M., Porosity in Configured Structures Effect of Ply Drops and Caul Sheets in the Processing of Composite Parts, Master Thesis, University of British Columbia, Canada, 2015.
  10. Campbell, F.C., Manufacturing Processes for Advanced Composites, Elsevier, 2004.
  11. Campbell, F.C., Structural Composite Material, ASM International, 2010.
  12. Park, D.C., and Kim, Y.H., "Evaluation of Laminate Property using Caulplate Application", Journal of the Korean Society for Composite Materials, Vol. 29, No. 5, 2016, pp. 231-235.
  13. Park, D.C., and Kim, Y.H., "A Void Behavior in a Complexshaped Composite Structure", Modern Physics Letter B, Vol. 33, No. 14&15, 2019, pp.1940028. https://doi.org/10.1142/S0217984919400281
  14. ASTM D3418 Standard Test Method for Transition Temperatures and Enthalpies of Fusion and Crystallization of Polymers by Differential Scanning Calorimetry.
  15. ASTM E317 Standard Practice for Evaluation Performance Characteristics of Ultrasonic Pulse Echo Testing Instruments and Systems without the use of Electronic Measurement Instruments.
  16. Solvay-Cytec Technical Data Sheet, Surface Master 905 Surfacing Film, 2010.
  17. Solvay-Cytec Technical Data Sheet, Cycom 970 Epoxy Resin, 2013.