Abstract
The objectives of this study were to identify the optimal mix of foam concrete with the low-strength and high-flow for the repairing ground subsidence situation emergently by utilizing a large amount of industrial by-products and evaluate the possibility by applying it to the site. The factors of the experiment were the mixing ratio of mixing water and a foaming agent and the mixing ratio of foam over paste volume. The optimal mix identified by the experiment was applied to the field and basic properties were evaluated. The results of the experiment showed that the optimal mixing ratio of mixing water and the foaming agent was 10%. Moreover, when the mixing ratio of pre-foam over paste volume was 170%, it satisfied the target. However, to ensure stable quality when applying to the field, the foam mixing ratio was set 140% for the field application. The field application test of foam concrete with the low-strength and high-flow using an eco-friendly binder satisfied all target performances. Therefore, the possibility of using it as a mixture and construction method for a ground repair system is confirmed. However, there was a quality deviation between the upper part and the lower part due to the separation between foam and paste. Consequently, further studies are needed to improve it.
본 연구는 산업부산물을 다량 활용하여 지반 함몰 발생시 긴급 복구를 위한 저강도·고유동 경량기포 콘크리트의 최적배합을 설정하고, 이를 현장에 적용하여 가능성을 평가하기 위한 연구이다. 실험의 변수로는 배합수 대비 기포제의 혼입률과 페이스트 용적대비 기포의 혼입률이며, 실험을 통하여 선정된 최적배합으로 현장적용을 통한 기초특성을 평가하였다. 실험결과 배합수 대비 최적의 기포제 혼입률은 10%가 가장 효율적이라 판단되었으며, 페이스트 대비 선발포된 기포의 혼입률은 170%에서 목표를 만족하였다. 그러나, 현장적용 시안정적인 품질확보를 위하여 기포 혼입률은 140%로 현장의 배합에 적용하였다. 친환경 결합재를 이용한 저강도·고유동 경량기포 콘크리트의 현장적용 결과 목표성능을 모두 만족하여 지반복구용 배합 및 공법으로서의 가능성을 확인하였다. 그러나 기포 및 페이스트간의 분리로 인한 상하부의 품질편차가 발생함에 따라 이의 개선을 위한 후속연구가 요구된다.