Geopolymer is an alumina silicate-based ceramic material that has good heat-resistance and fire-resistance; it can be cured at room temperature, and thus its manufacturing process is simple. Geopolymer can be used as a reinforcement or floor finish for high-speed curing applications. In this manuscript, we investigate a high-speed curing geopolymer achieved by adding calcium to augment the curing rate. Metakaolin is used as the main raw material, and aqueous solutions of KOH and $K_2SiO_3$ are used as the activators. As a result of optimizing the high bending strength as a target factor for geopolymers with $SiO_2/Al_2O_3$ ratio of 4.1 ~ 4.8, the optimum ranges of the active agent are found to be $0.1{\leq}K_2O/SiO_2{\leq}0.4$ and $10{\leq}H_2O/K_2O{\leq}32.5$, and the optimum range of the curing accelerator is found to be $$0.82{\leq_-}Ca(OH)_2/Al_2O_3{\leq_-}2.87$$. The maximum flexural strength is found to be 1.35 MPa at $Ca(OH)_2/Al_2O_3=2.82$, $K_2O/SiO_2=0.3$, and $H_2O/K_2O=11.3$. The physical and thermal properties are analyzed to validate the applicability of these materials as industrial insulating parts or repairing finishing materials in construction.