Variable amplitude fatigue test of M30 high-strength bolt in bolt-sphere joint grid structures

  • Qiu, Bin (College of Civil Engineering, Taiyuan University of Technology) ;
  • Lei, Honggang (College of Civil Engineering, Taiyuan University of Technology) ;
  • Yang, Xu (College of Civil Engineering, Taiyuan University of Technology) ;
  • Zhou, Zichun (College of Civil Engineering, Taiyuan University of Technology) ;
  • Wang, Guoqing (College of Civil Engineering, Taiyuan University of Technology)
  • 투고 : 2019.04.25
  • 심사 : 2019.10.26
  • 발행 : 2019.11.10

초록

Fatigue failure of a grid structure using bolt-sphere joints is liable to occur in a high-strength bolt due to the alternating and reciprocal actions of a suspension crane. In this study, variable amplitude fatigue tests were carried out on 20 40 Cr steel alloy M30 high-strength bolts using an MTS fatigue testing machine, and four cyclic stress amplitude loading patterns, Low-High, High-Low, Low-High-Low, and High-Low-High, were tested. The scanning electron microscope images of bolt fatigue failure due to variable amplitude stress were obtained, and the fractographic analysis of fatigue fractures was performed to investigate the fatigue failure mechanisms. Based on the available data from the constant amplitude fatigue tests, the variable amplitude fatigue life of an M30 high-strength bolt in a bolt-sphere joint was estimated using both Miner's rule and the Corten-Dolan model. Since both cumulative damage models gave similar predictions, Miner's rule is suggested for estimating the variable-amplitude fatigue life of M30 high-strength bolts in a grid structure with bolt-sphere joints; the S-N fatigue curve of the M30 high-strength bolts under variable amplitude loading was derived using equivalent stress amplitude as a design parameter.

키워드

과제정보

연구 과제 주관 기관 : National Natural Science Foundation of China (NSFC)

참고문헌

  1. ANSI/AISC 360-16 (2010), Specification for Structural Steel Buildings, American Institute of Steel Construction; Chicago, IL, USA.
  2. ASTM E606/E606M-12 (2012), Test method for strain-controlled fatigue testing, West Conshohocken, PA, USA.
  3. Chen, S. (2016), Principles of Steel Structure Design, Science Press, Beijing, China.
  4. Corten, H.T. and Dolan, T.J. (1956), "Cumulative fatigue damage", Proceedings of the International Conference on Fatigue of Metals, London, UK & New York, USA, September.
  5. Eurocode 3 (2003), Design of Steel Structures-Part 1.9: Fatigue, CEN: European Committee for Standardization; Brussels, Belgium.
  6. Fatemi, A. and Yang, L. (1998), "Cumulative fatigue damage and life prediction theories: a survey of the state of the art for homogeneous materials", Int. J. Fatigue, 20(1), 9-34. https://doi.org/10.1016/S0142-1123(97)00081-9
  7. Feng, S. (2017), "Simulation of fatigue load spectrum and fatigue life estimation of space grid with bolt sphere joint", MSc. Dissertation; Taiyuan University of Technology, China.
  8. Feng, X., Lin, X., Pan, W., Qin, Y. and Huang, B. (1995), "Fatigue performance under suspension crane action of bolt ball grid nodes", J. Build. Struct., 16(4), 3-12. [In Chinese]
  9. Ferjaoui, A., Yue, T., Wahab, M.A. and Hojjati-Talemi, R. (2015), "Prediction of fretting fatigue crack initiation in double lap bolted joint using Continuum Damage Mechanics", Int. J. Fatigue, 73, 66-76. https://doi.org/10.1016/j.ijfatigue.2014.11.012
  10. GB50017-2017 (2017), Standard for Design of Steel Structures, China Architecture and Building Press; Beijing, China.
  11. GB700-2006 (2006), Carbon structural steels, Standard Press of China; Beijing, China.
  12. GB/T13682-1992 (1992), Axial load fatigue testing for threaded fasteners, Standard Press of China; Beijing, China.
  13. He, L., Akebono, H. and Sugeta, A. (2018), "Effect of high-amplitude loading on accumulated fatigue damage under variable-amplitude loading in 316 stainless steel", Int. J. Fatigue, 116, 388-395. https://doi.org/10.1016/j.ijfatigue.2018.06.045
  14. Ibrahim, R.A. and Pettit, C.L. (2005), "Uncertainties and dynamic problems of bolted joints and other fasteners", J. Sound Vib., 279(3-5), 857-936. https://doi.org/10.1016/j.jsv.2003.11.064
  15. JG/T 10-2009 (2009), Bolted spherical node of space grid structures, Standard Press of China; Beijing, China.
  16. JGJ7-2010 (2010), Technical Specification for Space Frame Structures, China Architecture and Building Press; Beijing, China.
  17. Kapidzic, Z., Ansell, H., Schon, J. and Simonsson, K. (2016), "Fatigue bearing failure of CFRP composite in bolted joints exposed to biaxial variable amplitude loading at elevated temperature", Compos. Struct., 142, 71-77. https://doi.org/10.1016/j.compstruct.2016.01.064
  18. Lei, H. and Yin, D. (2008), "Research progress on fatigue of grid structure with suspension cranes", Space Struct., 14(4), 32-36. [In Chinese]
  19. Mahtabi, M.J., Stone, T.W. and Shamsaei, N. (2018), "Load sequence effects and variable amplitude fatigue of superelastic NiTi", Int. J. Mech. Sci., 148, 307-315. https://doi.org/10.1016/j.ijmecsci.2018.08.037
  20. Miner, M.A. (1945), "Cumulative damage in fatigue", J. Appl. Mech., 12(3), 159-164. https://doi.org/10.1115/1.4009458
  21. Qiu, B., Lin, J., Yang, X. and Lei, H. (2017), "Experimental research on fatigue properties of the M30 high-strength bolt under false twisting", Sci. Tech. Eng., 17(7), 20-25. [In Chinese]
  22. Sarkar, S., Kumar, C.S. and Nath, A.K. (2019), "Investigation on the mode of failures and fatigue life of laser-based powder bed fusion produced stainless steel parts under variable amplitude loading conditions", Addit. Manuf., 25, 71-83. https://doi.org/10.1016/j.addma.2018.10.044
  23. Sunder, R. (1979), "A mathematical model of fatigue crack propagation under variable amplitude loading", Eng. Fract. Mech., 12(2), 155-165. https://doi.org/10.1016/0013-7944(79)90108-5
  24. Suresh, S. (2006), Fatigue of Materials, (2nd Edition), Cambridge University Press, Cambridge, UK.
  25. Xu, G. and Cui, J. (1994), "Grid structure fatigue and fatigue life calculation", J. Build. Struct., 15(2), 25-34. [In Chinese]
  26. Yang, X. (2017), "The theoretical and experimental research on fatigue performance of M30 and M39 high-strength bolts in grid structures with bolt sphere joints", Ph.D. Dissertation; Taiyuan University of Technology, China.
  27. Yang, X. and Lei, H. (2017), "Constant amplitude fatigue test of high-strength bolts in grid structures with bolt-sphere joints", Steel Compos. Struct., Int. J., 25(5), 571-579. https://doi.org/10.12989/scs.2017.25.5.571
  28. Zhou, S., Sun, Y., Ge, J. and Chen, X. (2015), "Multiaxial fatigue life prediction of composite bolted joint under constant amplitude cycle loading", Compos. B Eng., 74, 131-137. https://doi.org/10.1016/j.compositesb.2015.01.013
  29. Zhu, H. (2011), "Calculation methods for equivalent fatigue stress amplitude based on Corten-Dolan accumulative damage rule", Adv. Mater. Res.,156-157, 1271-1274. https://doi.org/10.4028/www.scientific.net/AMR.156-157.1271
  30. Zuo, F., Huang, H., Zhu, S., Lv, Z. and Gao, H. (2015), "Fatigue life prediction under variable amplitude loading using a nonlinear damage accumulation model", Int. J. Damage Mech., 24(5), 767-784. https://doi.org/10.1177/1056789514553042