Effect of pozzolans on mechanical behavior of recycled refractory brick concrete in fire

  • 투고 : 2019.03.26
  • 심사 : 2019.06.07
  • 발행 : 2019.11.10

초록

Reusing building materials and concrete of old buildings can be a promising strategy for sustained development. In buildings, the performance of materials under elevated temperatures is of particular interest for determining fire resistance. In this study, the effect of pozzolan and aggregate type on properties of concrete exposed to fire was investigated. In doing so, nanosilica with cement-replacement levels of 0, 2, and 4% as well as silica fume and ultrafine fly ash with cement-replacement levels of 0, 7.5, and 15% were used to study effect of pozzolan type, and recycled refractory brick (RRB) fine aggregate replacing natural fine aggregate by 0 and 100% was utilized to explore effect of aggregate type. A total of 126 cubic concrete specimens were manufactured and then investigated in terms of compressive strength, ultrasonic pulse velocity, and weight loss at $23^{\circ}C$ and immediately after exposure to 400 and $800^{\circ}C$. Results show that replacing 100% of natural fine aggregate with recycled refectory brick fine aggregate in the concretes exposed to heat was desirable, in that it led to a mean compressive strength increase of above 25% at $800^{\circ}C$. In general, among the pozzolans used here, silica fume demonstrated the best performance in terms of retaining the compressive strength of heated concretes. The higher replacement level of silica fume and ultrafine fly ash pozzolans in the mixes containing RRB fine aggregate led to a greater weight loss rate, while the higher replacement level of nanosilica reduced the weight loss rate.

키워드

참고문헌

  1. ACI 228.2R-98 (2004), Nondestructive test methods for evaluation of concrete in structures. American Concrete Institute; Farmington Hills, MI. USA.
  2. ACI Committee 216 (1989), Guide for determining the fire endurance of concrete elements (ACI 216R-89), American Concrete Institute; Farmington Hills, MI. USA.
  3. Albano, C., Camacho, N., Hernandez, M., Matheus, A. and Gutierrez, A. (2009), "Influence of content and particle size of waste pet bottles on concrete behavior at different w/c ratios", Waste Management, 29(10), 2707-2716. https://doi.org/10.1016/j.wasman.2009.05.007.
  4. Arioz, O. (2007), "Effects of elevated temperatures on properties of concrete", Fire Safety J., 42(8), 516-522. https://doi.org/10.1016/j.firesaf.2007.01.003.
  5. ASTM C192/C192M (2002), Standard practice for making and curing concrete test specimens in the laboratory, American Society for Testing and Materials; Philadelphia, PA, USA.
  6. ASTM C33 (2003), Standard specification for concrete aggregates, American Society for Testing and Materials; Philadelphia, PA, USA.
  7. ASTM C494 (2016), Standard specification for chemical admixtures for concrete, American Society for Testing and Materials; Philadelphia, PA, USA.
  8. ASTM C597 (2016), Standard test method for pulse velocity through concrete, American Society for Testing and Materials; Philadelphia, PA, USA.
  9. Bakharev, T. (2006), "Thermal behaviour of geopolymers prepared using class F fly ash and elevated temperature curing", Cement Concrete Res., 36(6), 1134-1147. https://doi.org/10.1016/j.cemconres.2006.03.022.
  10. Baradaran-Nasiri, A. and Nematzadeh, M. (2017), "The effect of elevated temperatures on the mechanical properties of concrete with fine recycled refractory brick aggregate and aluminate cement", Construct. Build. Mater., 147, 865-875. https://doi.org/10.1016/j.conbuildmat.2017.04.138.
  11. Bastami, M., Baghbadrani, M. and Aslani, F. (2014). "Performance of nano-Silica modified high strength concrete at elevated temperatures", Construct. Build. Mater., 68, 402-408. https://doi.org/10.1016/j.conbuildmat.2014.06.026.
  12. BS 1881-116 (1983), Testing concretes. Method for determination of compressive strength of concrete cubes, British Standards Institution; London, UK.
  13. Cheng, F.P., Kodur, V.K.R. and Wang, T.C. (2004), "Stress-strain curves for high strength concrete at elevated temperatures", J. Mater. Civil Eng., 16(1), 84-90. https://doi.org/10.1061/(ASCE)0899-1561(2004)16:1(84).
  14. Chindaprasirt, P., Chareerat, T., Hatanaka, S. and Cao, T. (2010), "High-strength geopolymer using fine high-calcium fly ash", J. Mater. Civil Eng., 23(3), 264-270. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000161.
  15. Cree, D., Green, M. and Noumowe, A. (2013), "Residual strength of concrete containing recycled materials after exposure to fire: A review", Construct. Build. Mater., 45, 208-223. https://doi.org/10.1016/j.conbuildmat.2013.04.005.
  16. EN 1994-1-2: Eurocode 4 (2004). Design of composite steel and concrete structures-Part 1-2: General rules for structural fire design, European Committee for Standardization; Brussels, Belgium.
  17. Fernandez-Jimenez, A., Palomo, A., Pastor, J.Y. and Martin, A. (2008), "New cementitious materials based on alkali-activated fly ash: performance at high temperatures", J. American Ceramic Soc., 91(10), 3308-3314. https://doi.org/10.1111/j.1551-2916.2008.02625.x.
  18. Fernandez-Jimenez, A., Pastor, J.Y., Martin, A. and Palomo, A. (2010), "High-Temperature Resistance in Alkali-Activated Cement", J. American Ceramic Soc., 93(10), 3411-3417. https://doi.org/10.1111/j.1551-2916.2010.03887.x.
  19. Gul, R., Demirboga, R. and Guvercin, T. (2006), "Compressive strength and ultrasound pulse velocity of mineral admixtured mortars", Indian J. Eng. Mater. Sci., 13(1), 18-24. http://nopr.niscair.res.in/handle/123456789/7210.
  20. Hansen, T. C. (2014), Recycling of Demolished Concrete and Masonry, CRC Press, Florida, USA.
  21. Hasan-Nattaj, F. and Nematzadeh, M. (2017), "The effect of forta-ferro and steel fibers on mechanical properties of high-strength concrete with and without silica fume and nano-silica", Construct. Build. Mater., 137, 557-572. https://doi.org/10.1016/j.conbuildmat.2017.01.078.
  22. IS 13311-1 (1992), Non-destructive testing of concrete - methods of tests, Bureau of Indian Standard; New Delhi, India.
  23. Jalal, M. (2014), "Corrosion resistant self-compacting concrete using micro and nano silica admixtures", Struct. Eng. Mech., 51(3), 403-412. https://doi.org/10.12989/sem.2014.51.3.403.
  24. Khalaf, F.M. and DeVenny, A.S. (2004), "Recycling of demolished masonry rubble as coarse aggregate in concrete", J. Mater. Civil Eng., 16(4), 331-340. https://doi.org/10.1061/(ASCE)0899-1561(2004)16:4(331).
  25. Khalaf, F. M. and DeVenny, A. S. (2005), "Properties of new and recycled clay brick aggregates for use in concrete", J. Mater. Civil Eng., 17(4), 456-464. https://doi.org/10.1061/(ASCE)0899-1561(2005)17:4(456).
  26. Khan, M.S. and Abbas, H. (2015), "Effect of elevated temperature on the behavior of high volume fly ash concrete", KSCE J. Civil Eng., 19(6), 1825-1831. https://doi.org/10.1007/s12205-014-1092-z.
  27. Kurda, R., de Brito, J. and Silvestre, J.D. (2017), "Combined influence of recycled concrete aggregates and high contents of fly ash on concrete properties", Construct. Build. Mater., 157, 554-572. https://doi.org/10.1016/j.conbuildmat.2017.09.128.
  28. Li, H., Xiao, H. G., Yuan, J. and Ou, J. (2004), "Microstructure of cement mortar with nano-particles", Composites Part B Eng., 35(2), 185-189. https://doi.org/10.1016/S1359-8368(03)00052-0.
  29. Liu, Y., Wang, W., Chen, Y.F. and Ji, H. (2016), "Residual stress-strain relationship for thermal insulation concrete with recycled aggregate after high temperature exposure", Construct. Build. Mater., 129, 37-47. https://doi.org/10.1016/j.conbuildmat.2016.11.006.
  30. Mahdavi, M., Abolmaali, A. and Ghahremannejad, M. (2018), "The effects of pH and temperature on compressive strength of synthetic fiber-reinforced concrete cylinders exposed to sulfuric acid", Adv. Civil Eng. Mater., 7(1), 403-413. https://doi.org/10.1520/ACEM20180018.
  31. Martin, A., Pastor, J.Y., Palomo, A. and Jimenez, A.F. (2015), "Mechanical behaviour at high temperature of alkali-activated aluminosilicates (geopolymers)", Construct. Build. Mater., 93, 1188-1196. https://doi.org/10.1016/j.conbuildmat.2015.04.044.
  32. Mousa, M.I. (2017), "Effect of elevated temperature on the properties of silica fume and recycled rubber-filled high strength concretes (RHSC)" HBRC J., 13(1), 1-7. https://doi.org/10.1016/j.hbrcj.2015.03.002.
  33. Nematzadeh, M. and Baradaran-Nasiri, A. (2017), "Residual properties of concrete containing recycled refractory brick aggregate at elevated temperatures", J. Mater. Civil Eng., 30(1), https://doi.org/10.1061/(ASCE)MT.1943-5533.0002125.
  34. Nematzadeh, M. and Fallah-Valukolaee, S. (2017), "Effectiveness of fibers and binders in high-strength concrete under chemical corrosion", Struct. Eng. Mech., 64(2), 243-257. https://doi.org/10.12989/sem.2017.64.2.243.
  35. Nematzadeh, M. and Mousavimehr, M. (2019), "Residual Compressive Stress-Strain Relationship for Hybrid Recycled PET-Crumb Rubber Aggregate Concrete after Exposure to Elevated Temperatures", J. Mater. Civil Eng., 31(8). https://doi.org/10.1061/(ASCE)MT.1943-5533.0002749.
  36. Nik, A.S. and Omran, O.L. (2013), "Estimation of compressive strength of self-compacted concrete with fibers consisting nano-SiO2 using ultrasonic pulse velocity", Construct. Build. Mater., 44, 654-662. https://doi.org/10.1016/j.conbuildmat.2013.03.082.
  37. Peng, G.F., Yang, W.W., Zhao, J., Liu, Y.F., Bian, S.H. and Zhao, L.H. (2006), "Explosive spalling and residual mechanical properties of fiber-toughened high-performance concrete subjected to high temperatures", Cement Concrete Res., 36(4), 723-727. https://doi.org/10.1016/j.cemconres.2005.12.014.
  38. Rashiddadash, P., Ramezanianpour, A.A. and Mahdikhani, M. (2014), "Experimental investigation on flexural toughness of hybrid fiber reinforced concrete (HFRC) containing metakaolin and pumice", Construct. Build. Mater., 51, 313-320. https://doi.org/10.1016/j.conbuildmat.2013.10.087.
  39. Saavedra, W.G.V. and de Gutierrez, R.M. (2017), "Performance of geopolymer concrete composed of fly ash after exposure to elevated temperatures", Construct. Build. Mater., 154, 229-235. https://doi.org/10.1016/j.conbuildmat.2017.07.208.
  40. Sagoe-Crentsil, K.K., Brown, T. and Taylor, A.H. (2001), "Performance of concrete made with commercially produced coarse recycled concrete aggregate", Cement Concrete Res., 31(5), 707-712. https://doi.org/10.1016/S0008-8846(00)00476-2.
  41. Sarhat, S.R. and Sherwood, E.G. (2012), "Residual mechanical response of recycled aggregate concrete after exposure to elevated temperatures", J. Mater. Civil Eng., 25(11), 1721-1730. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000719.
  42. Wang, W., Lu, C., Li, Y. and Li, Q. (2017), "An investigation on thermal conductivity of fly ash concrete after elevated temperature exposure", Construct. Build. Mater., 148, 148-154. https://doi.org/10.1016/j.conbuildmat.2017.05.068.
  43. Xiao, J., Li, J. and Zhang, C. (2005), "Mechanical properties of recycled aggregate concrete under uniaxial loading", Cement Concrete Res., 35(6), 1187-1194. https://doi.org/10.1016/j.cemconres.2004.09.020.
  44. Zhang, P., Gao, J.X., Dai, X.B., Zhang, T.H. and Wang, J. (2016), "Fracture behavior of fly ash concrete containing silica fume", Struct. Eng. Mech., 59(2), 261-275. https://doi.org/10.12989/sem.2016.59.2.261.