24개월 대기 노출된 Al1050 및 Al7075 알루미늄 합금 산화막에 대한 투과전자현미경 분석

TEM Analysis on Oxide Films of Al1050 and Al7075 Exposed to 24-month Atmospheric Conditions

  • Kim, Dae-Geon (School of Mechanical Engineering, Pusan National University) ;
  • Kim, Ga-Rim (School of Mechanical Engineering, Pusan National University) ;
  • Choi, Wonjun (School of Mechanical Engineering, Pusan National University) ;
  • Bahn, Chi Bum (School of Mechanical Engineering, Pusan National University)
  • 투고 : 2019.01.17
  • 심사 : 2019.03.16
  • 발행 : 2019.04.30

초록

Al1050 and Al7075 alloy specimens were exposed to atmospheric conditions for 24 months and analyzed by Transmission Electron Microscopy to characterize their corrosion behavior and oxide film characteristics, especially focusing on intergranular corrosion or oxidation. In general, the intergranular oxygen penetration depth of Al1050 was deeper than Al7075. Since O and Si signals were overlapped at the oxidized grain boundaries of Al1050 and Mg is not included in Al1050, it is concluded that Si segregated along the grain boundaries directly impacts on the intergranular corrosion of Al1050. Cr-Si or Mg-Si intermetallic particles were not observed along the grain boundaries of Al7050, but Mg-Si particle was barely observed in the matrix. 10-nm size Mg-Zn particles were also found all over the matrix. Mg was mainly observed along the oxidized grain boundary of Al7075, but Si was not detected due to the Mg-Si particle formation in the matrix and relatively low concentration of Si in Al7075. Therefore, it is thought that Mg plays an important role in the intergranular corrosion of Al7075 under atmospheric corrosion conditions.

키워드

PMGHBJ_2019_v52n2_62_f0001.png 이미지

Fig. 1. SEM surface images of (a) Al1050 and (b) Al7075 after 24-month exposure to atmospheric conditions

PMGHBJ_2019_v52n2_62_f0002.png 이미지

Fig. 2. SEM cross-section images of Al1050 surface exposed to atmospheric conditions for 24 months

PMGHBJ_2019_v52n2_62_f0003.png 이미지

Fig. 3. TEM cross-section image and EDS elemental mapping of pitting area in Al1050 exposed to 24-month atmospheric conditions; (a) dark field image (b) Al (c) O

PMGHBJ_2019_v52n2_62_f0004.png 이미지

Fig. 4. TEM cross-section panorama images and EDS elemental mapping of surface oxide layer formed on Al1050(non-pitting); (a) dark field image (b) O

PMGHBJ_2019_v52n2_62_f0005.png 이미지

Fig. 5 TEM cross-section image and EDS elemental mapping for oxygen penetration region of Al1050; (a) dark field image (b) O (c) Al

PMGHBJ_2019_v52n2_62_f0006.png 이미지

Fig. 6. EDS elemental mapping of oxygen penetration area in Al1050 (higher magnification of area shown in Fig. 5); (a) O (b) Al (c) Si

PMGHBJ_2019_v52n2_62_f0007.png 이미지

Fig. 7. Line EDS analysis results for oxygen penetration regions of Al1050 (Note each area number is designated in Fig. 5.)

PMGHBJ_2019_v52n2_62_f0008.png 이미지

Fig. 9. TEM cross-section image and EDS elemental mapping of oxygen penetration area in Al7075 exposed to 24-month atmospheric conditions (Right side of each picture is external surface.); (a) Dark field image (b) O (c) Al

PMGHBJ_2019_v52n2_62_f0009.png 이미지

Fig. 10. TEM cross-section panorama image and EDS elemental mapping of oxygen penetration area in Al7075 (Right side of each picture is external surface); (a) O (b) Mg (c) Si (d) Fe (e) Cr

PMGHBJ_2019_v52n2_62_f0010.png 이미지

Fig. 11 SEM image and EDS elemental mapping near the Mg-Si particle in Al7075

PMGHBJ_2019_v52n2_62_f0011.png 이미지

Fig. 12 TEM image and EDS elemental mapping near the oxygen penetration tip in Al7075; (a) dark field image, (b) Mg, (c) O, Cr, Mg, (d) Al, (e) Cr, (f) Zn

PMGHBJ_2019_v52n2_62_f0012.png 이미지

Fig. 8. (a) SEM cross-section image of surface oxidation region and (b) TEM specimen image after FIB sectioning for Al7075

Table 1. Chemical composition(wt%) of aluminum alloy Al7075 and Al1050 specimens.

PMGHBJ_2019_v52n2_62_t0001.png 이미지

참고문헌

  1. ASM International, ASM Handbook Vol 13A Corrosion: Fundamentals, Testing, and Protection, 2003, pp. 196-209.
  2. T. F. Otero, A. Porro, A. S. Elola, Prediction of Pitting Probability on 1050 Aluminum in Environmental Conditions, Corrosion 48 (1992) 785-791. https://doi.org/10.5006/1.3316000
  3. S. Sun, Q. Zheng, D. Li, J. Wen, Long-term atmospheric corrosion behaviour of aluminium alloys 2024 and 7075 in urban, coastal and industrial environments, Corros. Sci. 51 (2009) 719-727. https://doi.org/10.1016/j.corsci.2009.01.016
  4. T. Zhang, Y. He, R. Cui, T. An, Long-Term Atmospheric Corrosion of Aluminum Alloy 2024-T4 in a Coastal Environment, J. Mater. Eng. Perform. 24 (2015) 2764-2773. https://doi.org/10.1007/s11665-015-1541-y
  5. X. K. Yang, L. W. Zhang, S. Y. Zhang, M. Liu, K. Zhou, X. L. Mu, Properties degradation and atmospheric corrosion mechanism of 6061 aluminum alloy in industrial and marine atmosphere environments, Mater. Corros. 68 (2017) 529-535. https://doi.org/10.1002/maco.201609201
  6. M. Poltavtseva, A. Heyn, E. Boese, Long term corrosion behavior of clad aluminum materials under different atmospheric conditions, Mater. Corros. 64 (2013) 723-730. https://doi.org/10.1002/maco.201206962
  7. J. Ryl, J. Wysocka, M. Jarzynka, A. Zielinski, J. Orlikowski, K. Darowicki, Effect of native airformed oxidation on the corrosion behavior of AA 7075 aluminum alloys, Corros. Sci. 87 (2014) 150-155. https://doi.org/10.1016/j.corsci.2014.06.022
  8. Y. S. Kim, H. K. Lim, J. J. Kim, W. S. Hwang, and Y. S. Park, Corrosion cost and corrosion map of Korea-Based on the data from 2005 to 2010, Corros. Sci. Tech. 10 (2011) 52-59. https://doi.org/10.14773/CST.2011.10.2.052
  9. 김선규, 이찬형, 반치범. 대기 부식에 의해 생성된 Al1050 및 Al7075 알루미늄 합금 산화막에 대한 투과전자현미경 분석. 한국표면공학회지, 50(6), (2017) 447-454. https://doi.org/10.5695/JKISE.2017.50.6.447
  10. S.P. Knight, M. Salagaras, A.R. Trueman, The study of intergranular corrosion in aircraft aluminium alloys using X-ray tomography, Corros. Sci. 53 (2011) 727-734. https://doi.org/10.1016/j.corsci.2010.11.005
  11. Yoshiyuki Oya, Yoichi Kojima, Nobuyoshi Hara, Influence of Silicon on Intergranular Corrosion for Aluminum Alloys, MATERIALS TRANSACTIONS, Volume 54, Issue 7, (2013), 1200-1208. https://doi.org/10.2320/matertrans.M2013048
  12. Binger, W. W., Hollingsworth, E. H. and Sprawls, D., In Aluminium Vol. I, ed. Van Horn, ASM, (1967), p. 209.
  13. M. Kaifu, H. Fujimoto and M. Takemoto, Influence of Mn contents and heat treatments on intergranular corrosion of Al-Mn alloys, J. Japan Inst. Met. 32 (1982), 135-142.
  14. M. Zamin, The Role of Mn in the Corrosion Behavior of Al-Mn Alloys, Corrosion 37 (1981) 627-632. https://doi.org/10.5006/1.3577549
  15. A.K. Bhattamishra, Kishori Lal, Microstructural studies on the effect of Si and Cr on the intergranular corrosion in Al-Mg-Si alloys, Materials & Design, Volume 18, Issue 1, (1997) 25-28. https://doi.org/10.1016/S0261-3069(97)00027-7
  16. Y. Zheng, B. Luo, Z. Bai, J. Wang, and Y. Yin, Study of the Precipitation Hardening Behavior and Intergranular Corrosion of Al-Mg-Si Alloys with Differing Si Contents, Metals (2017) 7, 387. https://doi.org/10.3390/met7100387
  17. J. R. Galvele and S. M. de De Micheli, Mechanism of intergranular corrosion of Al-Cu alloys, Corros. Sci. 10 (1970), 795-807. https://doi.org/10.1016/S0010-938X(70)80003-8
  18. Y. Zou, Q. Liu, Z. Jia, Y. Xing, L. Ding, and X. Wang, The intergranular corrosion behavior of 6000-series alloys with different Mg/Si and Cu content, Appl. Surf. Sci. 405 (2017) 489-496. https://doi.org/10.1016/j.apsusc.2017.02.045
  19. American Society for Testing and Materials (ASTM) International, ASTM G50-10 Standard Practice for Conducting Atmospheric Corrosion Tests on Metals (2010).
  20. M. Navaser, M. Atapour, Effect of Friction Stir Processing on Pitting Corrosion and Intergranular Attack of 7075 Aluminum Alloy, J. Mater. Sci. Tech. 33 (2017) 155-165. https://doi.org/10.1016/j.jmst.2016.07.008