Characteristics of Blood Mixed Cement in Percutaneous Vertebroplasty

경피적 척추 성형술에서 혈액 혼합 시멘트의 특성

Purpose: This study evaluated the efficacy of blood mixed cement for osteoporotic vertebral compression fractures in reducing the complications of percutaneous vertebroplasty using conventional cement. Materials and Methods: This study was performed retrospectively in 80 patients, from January 2016 to January 2017. Porous cement was formed by mixing 2, 4, and 6 ml of blood with 20 g of cement used previously. A tube with a diameter and length of 2.8 mm and 215 mm, respectively, was used and the polymerization temperature, setting time, and optimal passing-time were measured and compared with those using only conventional cement. Radiologically, the results were evaluated and compared. Results: The polymerization temperature was 70.3℃, 55.3℃, 52.7℃, and 45.5℃ in the conventional cement (R), 2 ml (B2), 4 ml (B4), and 6 ml (B6), respectively, and the corresponding setting time decreased from 960 seconds (R) to 558 seconds (B2), 533 seconds (B4), and 500 seconds (B6). The optimal passing-time was 45 seconds (B2), 60 seconds (B4), and 78 seconds (B6) at 73 seconds (R), respectively and as the amount of blood increased, it was similar to the cement passing-time. The radiological results showed that the height restoration rates and the vertebral subsidence rates similar among the groups. Two cases of adjacent vertebral compression fractures in the R group and one in the B2 and B4 groups were encountered, and the leakage rate of the cement was approximately two times higher than that in the conventional cement group. Conclusion: In conventional percutaneous vertebroplasty, the procedure of using autologous blood with cement decreased the polymerization temperature, reduced the setting time, and the incidence of cement leakage was low. These properties may contribute to more favorable mechanical properties that can reduce the complications compared to conventional cements alone.

목적: 골다공증성 척추 압박골절을 가진 환자에서 혈액을 혼합한 시멘트를 사용함으로써 기존 시멘트를 이용하여 경피적 척추 성형술을 시행했을 경우 나타나는 합병증을 줄이는 데 적합한지 알아보고자 한다. 대상 및 방법: 2016년 1월부터 2017년 1월까지 80명을 대상으로 후향적으로 진행되었다. 각 군에서 기존에 사용하던 시멘트 20 g에 혈액을 각각 2, 4, 6 ml를 섞어서 다공성 시멘트를 생성하였다. 지름 2.8 mm, 길이 215 mm의 튜브를 이용하였고 중합온도, 응결 시간, 적절한 통과시간을 측정하여 기존의 시멘트만 사용하던 것과 비교하였다. 방사선적으로 컴퓨터 단층촬영 및 X-ray를 통하여 결과를 평가하여 비교하였다. 결과: 중합온도는 기존의 시멘트(R), 2 ml (B2), 4 ml (B4), 6 ml (B6) 군에서 각각 70.3℃, 55.3℃, 52.7℃, 45.5℃였으며, 응결시간은 960초(R)에서 558초(B2), 533초(B4), 500초(B6)로 감소하는 양상을 보였다. 통과시간은 각각 73초(R)에서 45초(B2), 60초(B4), 78초(B6)를 보였으며, 혈액의 양이 증가할수록 기존의 시멘트 통과시간과 유사하였다. 방사선적 결과 분석에서 추체 재건율과 추체 재함몰률은 4군 간에 유의한 차이가 없었다. 인접 추체 골절은 R군에서 2건, B2, B4 군에서 1건씩 나타났으며, 시멘트 누출률은 기존 시멘트 군에서 약 2배 높게 측정되었다. 결론: 기존의 경피적 척추 성형술 시 본인 자가 혈액을 시멘트와 혼합하여 사용하는 술식은 중합온도의 감소, 응결시간의 단축을 보이며 시멘트 누출 발생률이 적었다. 이러한 물성은 기존의 시멘트만 사용하는 경우보다 합병증을 줄일 수 있는 더 적합한 기계적 특성에 도움일 될 것으로 판단된다.