Effect of casein phosphopeptide-amorphous calcium phosphate on fluoride release and micro-shear bond strength of resin-modified glass ionomer cement in caries-affected dentin

  • 투고 : 2018.05.15
  • 심사 : 2018.08.23
  • 발행 : 2018.11.30
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

Objectives: This study was conducted to evaluate fluoride release and the micro-shear bond strength of resin-modified glass ionomer cement (RMGIC) in casein phosphopeptide-amorphous calcium phosphate (CPP-ACP)-remineralized caries-affected dentin (CAD). Materials and Methods: Exposed dentin surfaces of 30 human third molar teeth were divided into 2 equal groups for evaluating fluoride release and the micro-shear bond strength of RMGIC to CAD. Each group was subdivided into 3 equal subgroups: 1) control (sound dentin); 2) artificially demineralized dentin (CAD); 3) CPP-ACP remineralized dentin (remineralized CAD). To measure fluoride release, 15 disc-shaped specimens of RMGIC (4 mm in diameter and 2 mm in thickness) were bonded on one flat surface of the dentin discs of each group. Fluoride release was tested using ion chromatography at different intervals; 24 hours, 3, 5, 7 days. RMGIC micro-cylinders were built on the flat dentin surface of the 15 discs, which were prepared according to the assigned group. Micro-shear bond strength was measured after 24 hours water storage. Data were analyzed using 1- and 2-way analysis of variance and the post hoc least significant difference test (${\alpha}=0.05$). Results: Fluoride detected in solutions (at all intervals) and the micro-shear bond strength of RMGIC bonded to CPP-ACP-remineralized dentin were significantly higher than those bonded to artificial CAD (p < 0.05). Conclusions: Demineralized CAD consumes more fluoride released from RMGIC into the solution for remineralization than CPP-ACP mineralized dentin does. CPP-ACP increases the micro-shear bond strength of RMGIC to CAD.

키워드

참고문헌

  1. Llena C, Leyda A, Forner L, Garcet S. Association between the number of early carious lesions and diet in children with a high prevalence of caries. Eur J Paediatr Dent 2015;16:7-12.
  2. Pereira PN, Nunes MF, Miguez PA, Swift EJ Jr. Bond strengths of a 1-step self-etching system to cariesaffected and normal dentin. Oper Dent 2006;31:677-681. https://doi.org/10.2341/05-131
  3. Mount GJ, Ngo H. Minimal intervention: a new concept for operative dentistry. Quintessence Int 2000;31:527-533.
  4. Zhong B, Peng C, Wang G, Tian L, Cai Q, Cui F. Contemporary research findings on dentine remineralization. J Tissue Eng Regen Med 2015;9:1004-1016. https://doi.org/10.1002/term.1814
  5. Rahiotis C, Vougiouklakis G. Effect of a CPP-ACP agent on the demineralization and remineralization of dentine in vitro. J Dent 2007;35:695-698. https://doi.org/10.1016/j.jdent.2007.05.008
  6. Fusayama T. Two layers of carious dentin; diagnosis and treatment. Oper Dent 1979;4:63-70.
  7. Yamaguchi K, Miyazaki M, Takamizawa T, Inage H, Kurokawa H. Ultrasonic determination of the effect of casein phosphopeptide-amorphous calcium phosphate paste on the demineralization of bovine dentin. Caries Res 2007;41:204-207. https://doi.org/10.1159/000099319
  8. Alves FB, Lenzi TL, Reis A, Loguercio AD, Carvalho TS, Raggio DP. Bonding of simplified adhesive systems to caries-affected dentin of primary teeth. J Adhes Dent 2013;15:439-445.
  9. Marquezan M, Correa FN, Sanabe ME, Rodrigues Filho LE, Hebling J, Guedes-Pinto AC, Mendes FM. Artificial methods of dentine caries induction: a hardness and morphological comparative study. Arch Oral Biol 2009;54:1111-1117. https://doi.org/10.1016/j.archoralbio.2009.09.007
  10. Mitra SB. Adhesion to dentin and physical properties of a light-cured glass-ionomer liner/base. J Dent Res 1991;70:72-74. https://doi.org/10.1177/00220345910700011201
  11. Nagamine M, Itota T, Torii Y, Irie M, Staninec M, Inoue K. Effect of resin-modified glass ionomer cements on secondary caries. Am J Dent 1997;10:173-178.
  12. Hamama HH, Burrow MF, Yiu C. Effect of dentine conditioning on adhesion of resin-modified glass ionomer adhesives. Aust Dent J 2014;59:193-200. https://doi.org/10.1111/adj.12169
  13. Bahari M, Savadi Oskoee S, Kimyai S, Pouralibaba F, Farhadi F, Norouzi M. Effect of casein phosphopeptide-amorphous calcium phosphate treatment on microtensile bond strength to carious affected dentin using two adhesive strategies. J Dent Res Dent Clin Dent Prospects 2014;8:141-147.
  14. Itota T, Carrick TE, Rusby S, Al-Naimi OT, Yoshiyama M, McCabe JF. Determination of fluoride ions released from resin-based dental materials using ion-selective electrode and ion chromatograph. J Dent 2004;32:117-122. https://doi.org/10.1016/j.jdent.2003.09.002
  15. Cross KJ, Huq NL, Palamara JE, Perich JW, Reynolds EC. Physicochemical characterization of casein phosphopeptide-amorphous calcium phosphate nanocomplexes. J Biol Chem 2005;280:15362-15369. https://doi.org/10.1074/jbc.M413504200
  16. Zafar MS, Ahmed N. Therapeutic roles of fluoride released from restorative dental materials. Fluoride 2015;48:184-194.
  17. Sakaguchi RL, Powers JM. Craig's restorative dental materials. 13th ed. Philadelphia (PA): Elsevier Health Sciences; 2012. p155-158.
  18. Zalizniak I, Palamara JE, Wong RH, Cochrane NJ, Burrow MF, Reynolds EC. Ion release and physical properties of CPP-ACP modified GIC in acid solutions. J Dent 2013;41:449-454. https://doi.org/10.1016/j.jdent.2013.02.003
  19. Zhao IS, Mei ML, Burrow MF, Lo EC, Chu CH. Prevention of secondary caries using silver diamine fluoride treatment and casein phosphopeptide-amorphous calcium phosphate modified glass-ionomer cement. J Dent 2017;57:38-44. https://doi.org/10.1016/j.jdent.2016.12.001
  20. Kucukyilmaz E, Savas S. Evaluation of shear bond strength, penetration ability, microleakage and remineralisation capacity of glass ionomer-based fissure sealants. Eur J Paediatr Dent 2016;17:17-23.
  21. Smith PW, Preston KP, Higham SM. Development of an in situ root caries model. A. In vitro investigations. J Dent 2005;33:253-267. https://doi.org/10.1016/j.jdent.2004.10.020
  22. Hattab FN, Amin WM. Fluoride release from glass ionomer restorative materials and the effects of surface coating. Biomaterials 2001;22:1449-1458. https://doi.org/10.1016/S0142-9612(00)00253-2
  23. Shakya VK, Singh RK, Pathak AK, Singh BP, Chandra A, Bharti R, Yadav RK. Analysis of micro-shear bond strength of self-etch adhesive systems with dentine: an in vitro study. J Oral Biol Craniofac Res 2015;5:185-188. https://doi.org/10.1016/j.jobcr.2015.07.006
  24. Diefenderfer KE, Stahl J. Caries remineralization therapy: implications for dental readiness. Mil Med 2008;173 (Supplement 1:48-50. https://doi.org/10.7205/MILMED.173.Supplement_1.48
  25. Johansen E, Parks HF. Electron-microscopic observations on soft carious human dentin. J Dent Res 1961;40:235-248. https://doi.org/10.1177/00220345610400020501
  26. Ricketts DNJ, Pitts NB. Traditional operative treatment options. In: Pitts NB, editor. Detection, assessment, diagnosis and monitoring of caries. Basel: Karger Medical and Scientific Publishers; 2009. p164-173.
  27. Andersson A, Skold-Larsson K, Hallgren A, Petersson LG, Twetman S. Effect of a dental cream containing amorphous cream phosphate complexes on white spot lesion regression assessed by laser fluorescence. Oral Health Prev Dent 2007;5:229-233.
  28. Aimutis WR. Bioactive properties of milk proteins with particular focus on anticariogenesis. J Nutr 2004;134:989S-995S. https://doi.org/10.1093/jn/134.4.989S
  29. Reynolds EC. Remineralization of enamel subsurface lesions by casein phosphopeptide-stabilized calcium phosphate solutions. J Dent Res 1997;76:1587-1595. https://doi.org/10.1177/00220345970760091101
  30. Nakajima M, Kunawarote S, Prasansuttiporn T, Tagami J. Bonding to caries-affected dentin. Jpn Dent Sci Rev 2011;47:102-114. https://doi.org/10.1016/j.jdsr.2011.03.002
  31. McCabe JF, Carrick TE, Sidhu SK. Determining low levels of fluoride released from resin based dental materials. Eur J Oral Sci 2002;110:380-384. https://doi.org/10.1034/j.1600-0722.2002.21275.x
  32. Attar N, Turgut MD. Fluoride release and uptake capacities of fluoride-releasing restorative materials. Oper Dent 2003;28:395-402.
  33. De Moor RJ, Verbeeck RM, De Maeyer EA. Fluoride release profiles of restorative glass ionomer formulations. Dent Mater 1996;12:88-95. https://doi.org/10.1016/S0109-5641(96)80074-1
  34. Preston AJ, Agalamanyi EA, Higham SM, Mair LH. The recharge of esthetic dental restorative materials with fluoride in vitro-two years' results. Dent Mater 2003;19:32-37. https://doi.org/10.1016/S0109-5641(02)00011-8
  35. Strother JM, Kohn DH, Dennison JB, Clarkson BH. Fluoride release and re-uptake in direct tooth colored restorative materials. Dent Mater 1998;14:129-136. https://doi.org/10.1016/S0109-5641(98)00019-0
  36. Karantakis P, Helvatjoglou-Antoniades M, Theodoridou-Pahini S, Papadogiannis Y. Fluoride release from three glass ionomers, a compomer, and a composite resin in water, artificial saliva, and lactic acid. Oper Dent 2000;25:20-25.
  37. Smith DC. Composition and characteristics of glass ionomer cements. J Am Dent Assoc 1990;120:20-22. https://doi.org/10.14219/jada.archive.1990.0002
  38. Forsten L. Resin-modified glass ionomer cements: fluoride release and uptake. Acta Odontol Scand 1995;53:222-225. https://doi.org/10.3109/00016359509005976
  39. Knight GM, McIntyre JM, Craig GG, Mulyani , Zilm PS, Gully NJ. Differences between normal and demineralized dentine pretreated with silver fluoride and potassium iodide after an in vitro challenge by Streptococcus mutans. Aust Dent J 2007;52:16-21. https://doi.org/10.1111/j.1834-7819.2007.tb00460.x
  40. Mashiko R, Inoue G, Nikaido T, Tagami J. Morphological evaluation of artificial caries-affected dentin after applying FCP-COMPLEX. J Oral Sci 2017;59:343-350. https://doi.org/10.2334/josnusd.16-0312
  41. Mazzaoui SA, Burrow MF, Tyas MJ, Dashper SG, Eakins D, Reynolds EC. Incorporation of casein phosphopeptide-amorphous calcium phosphate into a glass-ionomer cement. J Dent Res 2003;82:914-918. https://doi.org/10.1177/154405910308201113
  42. Wang Y, Spencer P, Walker MP. Chemical profile of adhesive/caries-affected dentin interfaces using Raman microspectroscopy. J Biomed Mater Res A 2007;81:279-286.
  43. Yoshida Y, Van Meerbeek B, Nakayama Y, Snauwaert J, Hellemans L, Lambrechts P, Vanherle G, Wakasa K. Evidence of chemical bonding at biomaterial-hard tissue interfaces. J Dent Res 2000;79:709-714. https://doi.org/10.1177/00220345000790020301
  44. Adebayo OA, Burrow MF, Tyas MJ. Dentine bonding after CPP-ACP paste treatment with and without conditioning. J Dent 2008;36:1013-1024. https://doi.org/10.1016/j.jdent.2008.08.011
  45. Choi K, Oshida Y, Platt JA, Cochran MA, Matis BA, Yi K. Microtensile bond strength of glass ionomer cements to artificially created carious dentin. Oper Dent 2006;31:590-597. https://doi.org/10.2341/05-108
  46. Sattabanasuk V, Burrow MF, Shimada Y, Tagami J. Resin bonding to dentine after casein phosphopeptideamorphous calcium phosphate (CPP-ACP) treatments. J Adhes Sci Technol 2009;23:1149-1161. https://doi.org/10.1163/156856109X432686

피인용 문헌

  1. Microshear Bond Strength of Nanoparticle-Incorporated Conventional and Resin-Modified Glass Ionomer to Caries-Affected Dentin vol.2021, pp.None, 2018, https://doi.org/10.1155/2021/5565556