Compressive strength characteristics of cement treated sand prepared by static compaction method

  • 투고 : 2016.06.06
  • 심사 : 2017.01.12
  • 발행 : 2017.06.25
⟨ 이전 논문 다음 논문 ⟩

초록

An experimental program was conducted to investigate the effects of the static compaction pressure, cement content, water/cement ratio, and curing time on unconfined compressive strength (UCS) of the cement treated sand. UCS were conducted on samples prepared with 4 different cement/sand ratios and were compacted under the lowest and highest static pressures (8 MPa and 40 MPa). Each sample was cured for 7 and 28 days to observe the impact of curing time on UCS of cement treated samples. Results of the study showed the unconfined compressive strength of sand increased as the cement content (5% to 10%) of the cement-sand mixture and compaction pressure (8 MPa to 40 MPa) increased. UCS of sand soil increased 30% to 800% when cement content was increased from 2.5% to 10%. Impact of compaction pressure on UCS decreased with a reduction in cement contents. On the other hand, it was observed that as the water content the cement-sand mixture increased, the unconfined compressive strength showed tendency to decrease regardless of compaction pressure and cement content. When the curing time was extended from 7 days to 28 days, the unconfined compressive strengths of almost all the samples increased approximately by 2 or 3 times.

키워드

과제정보

연구 과제 주관 기관 : Gazi University

참고문헌

  1. ASTM D4253 (2015), Standard test method for maximum index density and unit weight of soils using a vibratory table; American Society for Testing and Materials, West Conshohocken, PA, USA.
  2. ASTM D4254 (2015), Standard test method for minimum index density and unit weight of soils and calculation of relative density; American Society for Testing and Materials, West Conshohocken, PA, USA.
  3. ASTM D854 (2015), Standard test method for specific gravity of soil solids by water pycnometer; American Society for Testing and Materials, West Conshohocken, PA, USA.
  4. Bahar, R., Benazzoug, M. and Kenai, S. (2004), "Performance of compacted cement-stabilised soil", Cement Concrete Compos., 26(7), 811-820. https://doi.org/10.1016/j.cemconcomp.2004.01.003
  5. Barzegari Kahnemouei, V. (2013), "İnvestigation of unconfined compressive strength of cement mixed sand compacted under various static pressures", M.Sc. Dissertation; Gazi University, Ankara, Turkey. [In Turkish]
  6. BS EN 197-1 (2011), Cement - Part 1: Composition; Specifications and conformity criteria for common cements, British Standards Institution.
  7. Consoli, N.C., Foppa, D. and Festugato, L. (2007), "Key parameters for strength control of artificially cemented soils", J. Geotech. Geoenviron. Eng., 133(2), 197-205. https://doi.org/10.1061/(ASCE)1090-0241(2007)133:2(197)
  8. Consoli, N., Viana da Fonseca, A. and Heineck, K. (2009), "Fundamental parameters for the stiffness and strength control of artificially cemented sand", J. Geotech. Geoenviron. Eng., 135(9), 1347-1353. https://doi.org/10.1061/(ASCE)GT.1943-5606.0000008
  9. Consoli, N., da Fonseca, A. and Silva, S. (2011a), "Voids/cement ratio controlling tensile strength of cement-treated soils", J. Geotech. Geoenviron. Eng., 137 (11), 1126-1131. https://doi.org/10.1061/(ASCE)GT.1943-5606.0000524
  10. Consoli, N., Cruz, R. and Floss, M. (2011b), "Variables controlling strength of artificially cemented sand: influence of curing time", J. Mater. Civ. Eng., 23(5), 692-696. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000205
  11. Das, B.M. and Dass, R.N. (1995), "Lightly cemented sand in tension and compression", Geotech. Geol. Eng., 13(3), 169-177. https://doi.org/10.1007/BF00456716
  12. Guettala, S. and Mezghiche, B. (2011), "Compressive strength and hydration with age of cement pastes containing dune sand powder", Constr. Build. Mater., 25(3), 1263-1269. https://doi.org/10.1016/j.conbuildmat.2010.09.026
  13. Ismail, M.A., Joer, H.A. and Sim, W. (2002), "Effect of cement type on shear behavior of cemented calcareous soil", J. Geotech. Geoenviron. Eng., 128(6), 520-529. https://doi.org/10.1061/(ASCE)1090-0241(2002)128:6(520)
  14. Lim, S. and Zollinger, D.G. (2003), "Estimation of the compressive strength and modulus of elasticity of cement-treated aggregate base materials", Transp. Res. Record, 1837, 30-38. https://doi.org/10.3141/1837-04
  15. Mohammad, L., Raghavandra, A. and Huang, B. (2000), "Laboratory performance evaluation of cementstabilized soil base mixtures", Transp. Res. Record: J. Transp. Res. Board, 1721, 19-28. https://doi.org/10.3141/1721-03
  16. Nakaraia, K. and Yoshidab, T. (2015), "Effect of carbonation on strength development of cement-treated Toyoura silica sand", Soils Found., 55(4), 857-865. https://doi.org/10.1016/j.sandf.2015.06.016
  17. Park, S. (2010), "Effect of wetting on unconfined compressive strength of cemented sands", J. Geotech. Geoenviron. Eng., 136(12), 1713-1720. https://doi.org/10.1061/(ASCE)GT.1943-5606.0000399
  18. Prusinski, J. and Bhattacharya, S. (1999), "Effectiveness of portland cement and lime in stabilizing clay soils", Transp. Res. Record, 1652, 215-227. https://doi.org/10.3141/1652-28
  19. Schnaid, F., Prietto, P.D.M. and Consoli, N.C. (2001), "Characterization of cemented sand in triaxial compression", J. Geotech. Geoenviron. Eng., 127(10), 857-868. https://doi.org/10.1061/(ASCE)1090-0241(2001)127:10(857)
  20. Su, Z., Tinjum, J.M. and Edil, T.B. (2014), "Freeze-thaw effect on the constrained modulus and ucs of cementitiously stabilized materials", Proceedings of Geo-Shanghai 2014, Shanghai, China, May.
  21. Ulker, E. (2010), "Comparison of compressive strength test procedures for blended cements", M.Sc. Dissertation; Middle East Technical University, Ankara, Turkey.
  22. Walker, P.J. (1995), "Strength, durability and shrinkage characteristics of cement stabilized soil blocks", Cement Concrete Compos., 17(4), 301-310. https://doi.org/10.1016/0958-9465(95)00019-9
  23. Wen, H., Martono, W. and Clyne, T.R. (2010), "Field evaluation of recycled pavement materials at MnROAD", Proceedings of Paving Materials and Pavement Analysis GeoShanghai, Shanghai, China, June.
  24. Yilmaz, Y. and Ozaydin, V. (2013), "Compaction and shear strength characteristics of colemanite ore waste modified active belite cement stabilized high plasticity soils", Eng. Geol. 155, 45-53. https://doi.org/10.1016/j.enggeo.2013.01.003