Abstract
The objective of this paper is to investigate experimentally the effect of replacement of recycled coarse aggregates with 5~13mm in size on a field applicability of concretes through Mock-up test. Seven different mock-up specimens were prepared with the size of $1200{\times}800{\times}800mm$ simulating column and wall. For the concrete mixtures, 24MPa, 27MPa and 40MPa of nominal strength were adopted with 30% and 70%(only for 24MPa) of 5~13mm recycled coarse aggregate (RCA) replacement and without 5~13mm RCA(Plain). For test items, slump, slump flow, compressive strength with different curing conditions, core drilling, rebound numbers and drying shrinkage were measured. Test results indicated that 30% of 5~13 mm RCA replacement resulted in increase in slump, slump flow and resistance against segregation, while air contents decreased compared to those of plain mixture. Compressive strength of concrete with 30% of 5~13mm RCA was shown to be higher than that of plain mixture due to optimum packing effect associated with presence of well graded aggregates. Rebound number of the mock-up specimen with 30% of 5~13mm RCA had lower fluctuation according to hitting location than that of plain mock-up specimen. It is believed from the results of the study that replacement of 30% of 5~13mm RCA brings desirable improvement in various aspect of concrete performance due to associated dense packing effect.
본 연구에서는 5~13mm 순환골재를 치환한 콘크리트의 현장 적용성을 평가하기 위하여 목업 시험체를 제작하여 콘크리트를 타설한 후 이들이 콘크리트의 제반특성에 미치는 영향을 실험적으로 고찰하고자 하였다. 기둥 및 벽체를 모사한 $1200{\times}800{\times}800mm$ 목업 시험체를 호칭강도 및 5~13mm 순환골재 치환율별로 7개 제작하였고, 24, 27 및 40MPa 급 호칭강도의 콘크리트에 5~13mm 순환골재 30%와 70%(24MPa만 해당)를 치환한 배합과 무치환배합을 선정하여 제조하였다. 실험항목으로 굳지않은 상태에서 슬럼프, 슬럼프플로, 블리딩을 측정하였고, 경화상태에서는 압축강도, 반발도, 코어강도 및 건조수축 길이변화율을 측정하였다. 연구결과 5~13mm 순환골재가 30% 치환된 경우 슬럼프, 슬럼프플로, 블리딩량은 플레인에 비해 향상되는 것으로 나타났고, 압축강도의 경우도 최밀 충전 효과에 기인하여 플레인보다 상승되는 것으로 나타났다. 목업 시험체의 높이별 반발도의 경우도 5~13mm 순환골재가 30%치환된 경우 상하간의 반발도차이가 감소되는 것을 알 수 있었다.