Development of Compressive Failure Strength for Composite Laminate Using Regression Analysis Method

회귀분석법에 의한 복합재료 적층판의 압축파손강도 개발

This paper provides the compressive failure strength value of composite laminate developed by using regression analysis method. Composite material in this document is a Carbon/Epoxy unidirection(UD) tape prepreg(Cycom G40-800/5276-1) cured at $350^{\circ}F(177^{\circ}C$). The operating temperature is -$-60^{\circ}F{\sim}+200^{\circ}F$($-55^{\circ}C{\sim}+95^{\circ}C$). A total of 56 compression tests were conducted on specimens from eight (8) distinct laminates that were laid up by standard angle layers ($0^{\circ}$, $+45^{\circ}$, $-45^{\circ}$ and $90^{\circ}$). The ASTM-D-6484 standard was used for test method. The regression analysis was performed with the response variable being the laminate ultimate fracture strength and the regressor variables being two ply orientations ($0^{\circ}$ and ${\pm}45^{\circ}$).

본 논문에서는 회귀분석법(regression analysis method)을 사용하여 개발된 복합재 적층판의 압축 파손강도값을 수록하였다. 본 논문에 사용된 복합재료는 $350^{\circ}F(177^{\circ}C$)에서 경화되는 Carbon/Epoxy UD Tape 프리프레그(Cycom G40-800/5276-1)이며 운용온도 범위는 $-60^{\circ}F{\sim}+200^{\circ}F$($-55^{\circ}C{\sim}+95^{\circ}C$)이다. 시편은 $0^{\circ}$, $+45^{\circ}$, $-45^{\circ}$ 및 $90^{\circ}$층으로 적층된 8종류의 노치없는 적층판으로 총 56개 시편으로 구성하였다. 시험방법은 ASTM-D-6484 규정을 사용하였다. 적층판의 압축 파손강도값은 적층판 내 $0^{\circ}$와 ${\pm}45^{\circ}$층의 적층비율을 변수로 하는 회귀 분석법(regression analysis method)을 사용하여 획득하였다.