Effects of foam core density and face-sheet thickness on the mechanical properties of aluminum foam sandwich

  • Yan, Chang (Key Laboratory of Road Construction Technology & Equipment of Chang'an University) ;
  • Song, Xuding (Key Laboratory of Road Construction Technology & Equipment of Chang'an University)
  • Received : 2016.05.29
  • Accepted : 2016.07.28
  • Published : 2016.08.10

Abstract

To study the effects of foam core density and face-sheet thickness on the mechanical properties and failure modes of aluminum foam sandwich (AFS) beam, especially when the aluminum foam core is made in aluminum alloy and the face sheet thickness is less than 1.5 mm, three-point bending tests were investigated experimentally by using WDW-50E electronic universal tensile testing machine. Load-displacement curves were recorded to understand the mechanical response and photographs were taken to capture the deformation process of the composite structures. Results demonstrated that when foam core was combined with face-sheet thickness of 0.8 mm, its carrying capacity improved with the increase of core density. But when the thickness of face-sheet increased from 0.8 mm to 1.2 mm, result was opposite. For AFS with the same core density, their carrying capacity increased with the face-sheet thickness, but failure modes of thin face-sheet AFS were completely different from the thick face-sheet AFS. There were three failure modes in the present research: yield damage of both core and bottom face-sheet (Failure mode I), yield damage of foam core (Failure mode II), debonding between the adhesive interface (Failure mode III).

Keywords

Acknowledgement

Supported by : Central Universities of China

References

  1. Ashby, M.F., Evans, A.G., Fleck, N.A., Gibson, L.J., Hutchinson, J.W. and Wadley, H.N.G. (2000), Metal Foams: A Design Guide Burlington, Butterworth-Heinemann, UK.
  2. Banhart, J. (2001), "Manufacture, characterisation and application of cellular metals andmetal foams", Prog. Mater. Sci., 46(6), 559-632. https://doi.org/10.1016/S0079-6425(00)00002-5
  3. Banhart, J. and Seeliger, H.W. (2008), "Aluminum foam sandwich panels: Manufacture, metallurgy and applications", Adv. Eng. Mater., 10(9), 793-802. https://doi.org/10.1002/adem.200800091
  4. Baumeister, J., Banhart, J. and Weber, M. (1997), "Aluminum foams for transport industry", Mater. Des., 18(4-6), 217-220. https://doi.org/10.1016/S0261-3069(97)00050-2
  5. Crupi, V., Epasto, G. and Guglielmino, E. (2013), "Comparison of aluminum sandwiches for lightweight shipstructures: Honeycomb vs. foam", Marine Struct., 30, 74-96. https://doi.org/10.1016/j.marstruc.2012.11.002
  6. D'Alessandro, V., Petrone, G., De Rosa, S. and Franco, F. (2014), "Modelling of aluminum foam sandwich panels", Smart Struct. Syst., Int. J., 13(4), 615-636. https://doi.org/10.12989/sss.2014.13.4.615
  7. Duarte, I., Vesenjak, M. and Krstulovic-Opara, L. (2014), "Variation of quasi-static and dynamic compressive properties in a single aluminum foam block", Mater. Sci. Eng. A, 616, 171-182. https://doi.org/10.1016/j.msea.2014.08.002
  8. Duarte, I., Vesenjak, M., Krstulovic-Opara, L., Anzel, I. and Ferreira, J.M.F. (2015), "Manufacturing and bending behavior of in situ foam-filled aluminum alloy tubes", Mater. Des., 66, 532-544. https://doi.org/10.1016/j.matdes.2014.04.082
  9. Duarte, I., Krstulovic-Opara, L. and Vesenjak, M. (2016), "Analysis of performance of in-situ carbon steel bar reinforced Al-alloy foams", Compos. Struct., 152, 432-443. https://doi.org/10.1016/j.compstruct.2016.05.061
  10. Gibson, L.J. (2000), "Mechanical behavior of metallic foams", Annual Review of Materials Science, 30(1), 191-227. https://doi.org/10.1146/annurev.matsci.30.1.191
  11. Gibson, L.J. and Ashby, M.F. (1997), Cellular Solids: Structure and Properties, Cambridge University Press, New York, NY, USA.
  12. Huang, L., Wang, H., Yang, D.H., Ye, F. and Lu, Z.P. (2012), "Effects of scandium additions on mechanical properties of cellular Al-based foams", Intermetallics, 28, 71-76. https://doi.org/10.1016/j.intermet.2012.03.050
  13. Kabir, K., Vodenitcharova, T. and Hoffman, M. (2014), "Response of aluminum foam-cored sandwich panels to bending load", Composites: Part B, 64, 24-32. https://doi.org/10.1016/j.compositesb.2014.04.003
  14. Liu, H., Cao, Z.K., Yao, G.C., Luo, H.J. and Zu, G.Y. (2013), "Performance of aluminum foam-steel panel sandwich composites subjectedto blast loading", Mater. Des., 47, 483-488. https://doi.org/10.1016/j.matdes.2012.12.003
  15. Lu, T.J. and Ong, J.M. (2001), "Characterization of close-celled cellular aluminum alloys", J. Mater. Sci., 36(11), 2773-2786. https://doi.org/10.1023/A:1017977216346
  16. McCormack, T.M., Miller, R., Kesler, O. and Gibson, L.J. (2001), "Failure of sandwich beams with metallic foam cores", Int. J. Sol. Struct., 38(28-29), 4901-4920. https://doi.org/10.1016/S0020-7683(00)00327-9
  17. Mohan, K., Hon, Y.T., Idapalapati, S. and Seowa, H.P. (2005), "Failure of sandwich beams consisting of alumina face sheet and aluminum foam core in bending", Mater. Sci. Eng. A, 409(1-2), 292-301. https://doi.org/10.1016/j.msea.2005.06.070
  18. Nammi, S.K., Myler, P. and Edwards, G. (2010), "Finite element analysis of closed-cell aluminum foam under quasi-static loading", Mater. Des., 31(2), 712-722. https://doi.org/10.1016/j.matdes.2009.08.010
  19. Ruan, D., Lu, G. and Wong, Y.C. (2010), "Quasi-static indentation tests on aluminum foam sandwich panels", Compos. Struct., 92(9), 2039-2046. https://doi.org/10.1016/j.compstruct.2009.11.014
  20. Styles, M., Compston, P. and Kalyanasundaram, S. (2008), "Finite element modeling of core thickness effects in aluminum foam/composite sandwich structure under flexural loading", Compos. Struct., 86(1-3), 227-232. https://doi.org/10.1016/j.compstruct.2008.03.024
  21. Thoma, K., Schafer, F., Hiermaier, S. and Schneider, E. (2004), "An approach to achieve progress in spacecraft shielding", Adv. Space Res., 34(5), 1063-1075. https://doi.org/10.1016/j.asr.2003.03.034
  22. Wang, N.Z., Chen, X., Li, A., Zhang, H.W. and Liu, Y. (2016), "Three-point bending performance of a new aluminum foam composite structure", Trans. Nonferrous Met. Soc. China, 26(2), 359-368. https://doi.org/10.1016/S1003-6326(16)64088-8
  23. Wei, L., Yao, G.C., Zhang, X.M. and Luo, H.J. (2003), "Preparation of Foam Aluminum by Powder Metallurgy Process", J. Northeastern Univ. (Natural Science), 24(11), 1071-1074.
  24. Zu, G., Song, B., Zhong, Z., Li, X., Mu, Y. and Yao, G. (2012), "Static three-point bending behavior of aluminum foam sandwich", J. Alloys Compounds, 540, 275-278. https://doi.org/10.1016/j.jallcom.2012.06.079
  25. Zu, G.Y., Lu, R.H., Li, X.B., Zhong, Z., Ma, X.J., Han, M.B. and Yao, G.C. (2013), "Three-point bending behavior of aluminum foam sandwich with steel panel", Trans. Nonferrous Met. Soc. China, 23(9), 2491-2495. https://doi.org/10.1016/S1003-6326(13)62759-4

Cited by

  1. Effects of epoxy resin liquidity on the mechanical properties of aluminum foam sandwich vol.32, pp.6, 2018, https://doi.org/10.1080/01694243.2017.1375173
  2. Flexural response of carbon fiber reinforced aluminum foam sandwich 2017, https://doi.org/10.1177/0021998317735166
  3. Analytical solutions for sandwich plates considering permeation effect by 3-D elasticity theory vol.25, pp.2, 2016, https://doi.org/10.12989/scs.2017.25.2.127
  4. Bending behavior of aluminum foam sandwich with 304 stainless steel face-sheet vol.25, pp.3, 2016, https://doi.org/10.12989/scs.2017.25.3.327
  5. Geometrically nonlinear analysis of sandwich beams under low velocity impact: analytical and experimental investigation vol.27, pp.3, 2016, https://doi.org/10.12989/scs.2018.27.3.273
  6. Effects of face-sheet materials on the flexural behavior of aluminum foam sandwich vol.29, pp.3, 2016, https://doi.org/10.12989/scs.2018.29.3.301
  7. Energy absorption of foam-filled lattice composite cylinders under lateral compressive loading vol.31, pp.2, 2016, https://doi.org/10.12989/scs.2019.31.2.133
  8. Viscoelastic behaviour investigation and new developed laboratory slamming test on foam core sandwich vol.22, pp.6, 2016, https://doi.org/10.1177/1099636218792729
  9. Effect of infill pattern, density and material type of 3D printed cubic structure under quasi-static loading vol.235, pp.19, 2016, https://doi.org/10.1177/0954406220971667