초록
Background: TlBr is of considerable technological importance for radiation detection applications where detecting high-energy photons such as X-rays and ${\gamma}$-rays are of prime importance. However, there were few reports on investigating optical properties of TlBr itself for deeper understandings of this material and for making better radiation detection devices. Thus, in this paper, we report on the optical characterizations of TlBr single crystals. Spectroscopic ellipsometry (SE) and photoluminescence (PL) measurements at RT were performed for this work. Materials and Methods: A 2-inch TlBr single crystalline ingot was grown by using the vertical Bridgman furnace. SE measurements were performed at RT within the photon energy range from 1.1 to 6.5 eV. PL measurements were performed at RT by using a home-made PL system equipped with a 266 nm-laser and a spectrometer. Results and Discussion: Dielectric responses from SE analysis were shown to be slightly different among the different samples possibly due to the different structural/optical properties. Also from the PL measurements, it was observed that the peak intensities of the middle samples were significantly higher than those of the other two samples. With the given values for permittivity of free space (${\varepsilon}_0=8.854{\times}10^{-12}F{\cdot}m^{-1}$), thickness (d = 1 mm), and area ($A=10{\times}10mm^2$) of the TlBr sample, capacitances of TlBr were 6.9 pF (at $h{\nu}=3eV$) and 4.4 pF (at $h{\nu}=6eV$), respectively. Conclusion: SE and PL measurement and analysis were performed to characterize TlBr samples from the optical perspective. It was observed that dielectric responses of different TlBr samples were slightly different due to the different material properties. PL measurements showed that the middle sample exhibited much stronger PL emission peaks due to the better material quality. From the SE analysis, optical, dielectric constants were extracted, and calculated capacitances were in the few pF range.