Abstract
In this study, to replace a complicated process such as in the rubber component used in the adhesive of the shoe buffing, pretreatment with primers, we studied mechanical properties and adhesive properties with rubber compound added propanamine and 1,6-Hexanediamine. The adhesive properties rubber specimen added propanamine did not occurrence, but The adhesive properties rubber specimen added 1,6-Hexanediamine was occurrence. Also, the contact angle was decreased compared to not added NBR. And rubber compound added 6-Hexanediamine was smaller than the contact angle was evaluated in comparison to the added propanamine. $NH_2$ group on the rubber surface were confirmed with a peak at $1450{\sim}1550cm^{-1}$ in FT-IR spectrum. Rubber compound added propanamine and 1,6-Hexanediamine was reduced mechanical properties and decreased NBS resistance.
본 연구에서는 신발에 사용되는 부품 중 겉창용 고무 접착에 있어서 buffing, 프라이머 처리와 같은 전처리 공정을 생략하기 위하여, propanamine과 1,6-Hexanediamine와 같은 아민류의 첨가제가 적용된 고무 성형물에 대한 접착특성과 기계적 특성을 고찰하였다. Propanamine과 1,6-Hexanediamine이 첨가되지 않은 고무 시편과 propanamine이 첨가된 고무 시편은 접착성이 발현되지 않았지만 1,6-Hexanediamine이 첨가된 고무 시편의 경우 접착성 효과가 개선되었다. 또한 propanamine과 1,6-Hexanediamine이 첨가된 경우 접촉각이 감소하였으며, 1,6-Hexanediamine이 첨가된 고무 시편이 propanamine이 첨가된 시편에 비해 작은 접촉각을 나타내었다. 고무 표면의 $-NH_2$에 대한 피크는 $1450{\sim}1550cm^{-1}$의 그룹에서 FT-IR 분석 결과로 확인하였다. propanamine과 1,6-Hexanediamine이 첨가된 경우 기계적 특성 저하와 마모 특성이 감소하였다.