Preparation of Polyvinylpyrrolidone/AgBF4/Al(NO3)3 Electrolyte Membranes for Facilitated Gas Transport

기체 촉진수송을 위한 polyvinylpyrrolidone/AgBF4/Al(NO3)3 전해질 분리막 제조

  • 윤기완 (상명대학교 자연과학대학 화학과) ;
  • 강상욱 (상명대학교 자연과학대학 화학과)
  • Received : 2016.01.11
  • Accepted : 2016.02.02
  • Published : 2016.02.29
Download PDF
⟨ Previous Next ⟩

Abstract

Polyvinylpyrrolidone (PVP), which is glassy polymer to have amide functional group, was induced to fabricate the facilitated olefin transport membranes for olefin/paraffin separation. Separation performance for the mixed gas consisting of propylene and propane (50 : 50 vol%) was measured by gas chromatography and bubble flow meter. The properties of membranes were confirmed by scanning electron microscope and FT-IR. The results of long-term separation tests showed the selectivity of 15 and permeance of 1.3 GPU. The membranes was compared with poly(2-ethyl-2-oxazoline) $(POZ)/AgBF_4/Al(NO_3)_3$ membranes and the characteristics were confirmed as polymer matrix for facilitated transport membranes.

올레핀/파라핀 혼합 기체의 분리를 위한 올레핀 촉진 수송 분리막의 제조를 위해 amide 작용기를 가지며 glassy한 특성을 보이는 polyvinylpyrrolidone (PVP) 고분자를 분리막의 matrix로서 사용하였다. 분리막의 기체 투과 실험은 propylene과 propane 50 : 50의 부피비로 혼합된 기체를 사용하였고, bubble meter와 gas chromatography를 사용해 투과도와 선택도를 측정하였다. 또한 SEM image와 FT-IR을 통해 막의 특성을 조사하였다. 100시간의 장시간 성능 측정 결과 선택도는 약 15, 투과도는 약 1.3 GPU 이상을 각각 유지하였다. 기존의 poly(2-ethyl-2-oxazoline) $(POZ)/AgBF_4/Al(NO_3)_3$ 분리막과 비교함으로써, 고분자 matrix로서의 PVP 특성을 확인하였다.

Keywords

References

  1. R. T. Yang and E. S. Kikkinides, "New sorbents for olefin paraffin separations by adsorption via Pi-complexation", AIChE J., 41, 509 (1995). https://doi.org/10.1002/aic.690410309
  2. T. Ren, M. Patel, and K. Blok, E, "Olefins from conventional and heavy feedstocks: Energy use in steam cracking and alternative processes", Energy, 31, 42 (2006).
  3. J. Ploegmakers, S. Japip, and K. Nijmeijer, "Mixed matrix membranes containing MOF's for ethylene/ethane separation", J. Membr. Sci., 428, 331 (2013). https://doi.org/10.1016/j.memsci.2012.11.013
  4. I. Tiscornia, S. Irusta, C. Tellz. J. Coronas, and J. Santamaria, "Separation of propylene/propane mixtures by titanosilicate ETS-10 membranes prepared in one-step seeded hydrothermal synthesis", J. Membr. Sci., 311, 326 (2008). https://doi.org/10.1016/j.memsci.2007.12.028
  5. R. L. Burns and W. J. Koros, "Defining the challenges for C3H6/C3H8 separation using polymeric membranes", J. Membr. Sci., 211, 299 (2003). https://doi.org/10.1016/S0376-7388(02)00430-1
  6. C. A. Grande and A. E. Rodrigues, "Propane/propylene separation by pressure swing adsorption using zeolite 4A", Ind. Eng. Chem. Res., 44, 8815 (2005). https://doi.org/10.1021/ie050671b
  7. D. F. Sanders, Z. P. Smith, R. Guo, L. M. Robenson, and J. E. McGrath, "Energy-efficient polymeric gas separation membranes for a sustainable future: A review", Polymer, 54, 4729 (2013). https://doi.org/10.1016/j.polymer.2013.05.075
  8. L. G. Wu, J. N. Shen, H. L. Chen, and C. J. Gao, "$CO_2$ facilitated transport through a membrane of acrylamide and maleic anhydride copolymer", Desalination, 193, 313 (2006). https://doi.org/10.1016/j.desal.2005.04.146
  9. S. U. Hong, J. Won, and Y. S. Kang, "Polymer-salt complexes containing silver ions and their application to facilitated olefin transport membranes", Adv. Mater., 12, 968 (2000). https://doi.org/10.1002/1521-4095(200006)12:13<968::AID-ADMA968>3.0.CO;2-W
  10. Y. S. Kang, J. H. Kim, J. Won, and H. S. Kim, "Solid-state facilitated membranes for separation of olefins/paraffins and oxygen/nitrogen", Materials science of membranes for gas and vapor seperation Wiley, Chichester, 16 (2006).
  11. J. H. Kim, B. R. Min, K. B. Lee, J. Won, and Y. S. Kang, "Coordination structure of various ligands in crosslinked PVA to silver ions for facilitated olefin transport", Chem. Commun., 22, 2732-2733 (2002).
  12. S. W. Kang, J. H. Kim, J. Won, and Y. S. Kang, "Suppression of silver ion reduction by Al($NO_3)_3$ complex and its application to highly stabilized olefin transport membranes", J. Membr. Sci., 445, 156 (2013). https://doi.org/10.1016/j.memsci.2013.06.010
  13. D. E. Song, Y. S. Kang, and S. W. Kang, "Highly permeable ans stabilized olefin transport membranes based on a poly(ethylene oxide) matrix and Al($NO_3)_3$", J. Membr. Sci., 474, 273 (2015). https://doi.org/10.1016/j.memsci.2014.09.050
  14. B. Jose, J. H. Ryu, B. G. Lee, H. J. Lee, Y. S. Kang, and H. S. Kim, "Effect of phthalates on the stability and performance of AgBF4-PVP membranes for olefin/paraffin separation", Chem. Commun, 17, 2046 (2001).).