Effect of Equal Channel Angular Pressing on the Pitting Corrosion Resistance of Hard Anodized Al5052 Alloy

경질양극산화를 실시한 Al5052합금의 내공식성에 미치는 ECAP의 영향

  • Son, Injoon (Department of Materials Science and Metallurgical Engineering, Kyungpook National University)
  • 손인준 (경북대학교 신소재공학부 금속신소재공학전공)
  • Received : 2015.08.18
  • Accepted : 2015.08.28
  • Published : 2015.08.31
Download PDF
⟨ Previous Next ⟩

Abstract

The effect of equal channel angular pressing (ECAP) on the pitting corrosion resistance of hard anodized Al5052 alloy was investigated. The degree of internal stress generated in anodic oxide films during hard anodization was also evaluated with a strain gauge method. The pitting corrosion resistance of hard anodized Al5052 alloy was greatly decreased by ECAP. Cracks occurred in the anodic oxide film during hard anodization and these cracks were larger and deeper in the alloy with ECAP than without. The pitting corrosion was accelerated by cracks. The internal stress present in the anodic oxide films was compressive and the stress was higher in the alloys with ECAP than without, resulting in an increased likelihood of cracks. The pitting corrosion resistance of hard anodized Al5052 alloy was improved by annealing at the range of 473-573K after ECAP processed at room temperature for four passes. The compressive internal stress gradually decreased with increasing annealing temperature. It is assumed that the improvement in the pitting corrosion resistance of hard anodized Al5052 alloy by annealing may be attributed to a decrease in the likelihood of cracks due to the decreased internal stresses in anodic oxide films.

Keywords

References

  1. Z. Horita, K. Ohashi, T. Fujita, K. Kaneko, T.G. Langdon, Adv. Mater., 17 (2005) 1599. https://doi.org/10.1002/adma.200500069
  2. R. Z. Valiev, T. G. Langdon, Prog. Mater. Sci., 51 (2006) 881. https://doi.org/10.1016/j.pmatsci.2006.02.003
  3. Y. Iwahashi, J. Wang, Z. Horita, M. Nemoto, T. G Langdon, Scripta Mater., 35 (1996) 143. https://doi.org/10.1016/1359-6462(96)00107-8
  4. N. J. Petch, J. Iron Steel Inst., 174 (1953) 25.
  5. V. M. Segal, V. I. Reznikov, A.E. Drobyshevsky, V.I. Kopylov, Russian Metallurgy (metally), 1 (1981) 99.
  6. N. A. Smirnova, V. I. Levit, V. I. Pilyugin, R. I. Kuznetsov, L. S. Davydova, V. A. Sazonova, Fiz. Met. Metalloved., 61 (1986) 1170.
  7. J. Richert, M. Richert, Aluminum, 8 (1986) 604.
  8. Y. Saito, H. Utsunomiya, N. Tsuji, T. Sakai, R. Hong, J. Japan Inst. Metals, 63 (1999) 790. https://doi.org/10.2320/jinstmet1952.63.6_790
  9. R. Z. Valiev, N. A. Krasilnikov, N. K. Tsenev, Mater. Sci. Eng., A137 (1991) 35.
  10. R. Z. Valiev, R. K. Islamgaliev, I. V. Alexandrov, Prog. Mater. Sci., 45 (2000) 103. https://doi.org/10.1016/S0079-6425(99)00007-9
  11. J. R. Davis, Corrosion of Aluminum and Aluminum Alloys, ASM International, UAS (1999) 45.
  12. Z. Horita, M. Furukawa, M. Nemoto, T. G. Langdon, Mater. Sci. Tech., 16 (2000) 1239. https://doi.org/10.1179/026708300101507091
  13. Z. Horita, T. Fujinami, M. Nemoto, T. G. Langdon, Metallurgical and Mater. Trans. A., 31A (2000) 691.
  14. M. Seo, K. Ueno, J. Finish. Soc. Jpn., 51 (2000) 365 https://doi.org/10.4139/sfj.51.365
  15. I. J. Son, H, Nakano, S. Oue, S. Kobayashi, H. Fukushima, Z. Horita, Mater. Trans., 49 (2008) 2656. https://doi.org/10.2320/matertrans.MRA2008230
  16. V. V. Stolyarov, R. Lapovok, I. G. Brodova, P. F. Thomson, Mater. Sci. Eng., A357 (2003) 159.
  17. Atef. Korchef, Y. Champion, N. Njah, J. Alloy Compd., 427 (2007) 176. https://doi.org/10.1016/j.jallcom.2006.03.010
  18. N. B. Pilling, R. E. Bedworth, J. Inst. Metals, 29 (1923) 529.

Cited by

  1. Effect of Current Density on Porous Film Formation in Two-Step Anodizing for Al Alloy vol.49, pp.2, 2016, https://doi.org/10.5695/JKISE.2016.49.2.125
  2. Electrochemical Damage Characteristics of Anodized 5083 Aluminum Alloy with Flow Rate in Seawater vol.49, pp.4, 2016, https://doi.org/10.5695/JKISE.2016.49.4.349