Study on the Pervaporation Seperation of Aqueous 1-Butanol Mixture Using Composite PEI/PDMS Membrane

1-Butanol / 물 혼합액의 PEI/PDMS 복합막 모듈을 이용한 투과증발 파일럿 분리특성

  • 천봉수 (한남대학교 대덕밸리캠퍼스 화학공학과) ;
  • 이충섭 ((주)에어레인) ;
  • 하성용 ((주)에어레인) ;
  • 임지원 (한남대학교 대덕밸리캠퍼스 화학공학과)
  • Received : 2015.08.03
  • Accepted : 2015.08.24
  • Published : 2015.08.31

Abstract

To determine the pervaporation separation characteristics of 1-butanol/water mixtures, PEI/PDMS hollow fiber membrane module commercialized by Airrane Co. was subjected to both lab and pilot tests. The 1% 1-butanol of 1-butanol/water feed mixture was used. The flux of $133g/m^2hr$ and separation factor of 23.4 at $30^{\circ}C$ were obtained whereas the $505g/m^2hr$ and 5.1 were measured at $50^{\circ}C$. When compared with the performance of the hollow fiber PDMS membrane by Nagasep Co., the higher flux of $10{\sim}20g/m^2hr$ was obtained by the module of Airrane Co. In order to realized the durability of Airrane Co. module, the long-term test of 35 days has been conducted and as a result, the flux $510{\sim}520g/m^2hr$ and separation factor 20~25 were maintained with the initial values.

1-부탄올/물의 투과증발 분리특성을 알아보기 위해 (주)에어레인사에서 개발한 PEI 중공사막에 PDMS로 코팅한 복합막 모듈을 이용하여 랩테스트와 파일럿테스트를 실시하였다. 공급액으로는 물과 1-부탄올을 각각 99 : 1로 혼합하여 사용하였다. 실험 결과로 $30^{\circ}C$에서 투과도 $132.7g/m^2hr$, 선택도 23.4로 높은 선택도를, $50^{\circ}C$에서 투과도 $505.1g/m^2hr$, 선택도 5.1로 높은 투과도를 얻을 수 있었으며 일본의 나가셉사에서 개발한 지지체가 없는 PDMS 막 모듈과 비교했을 때 (주)에어레인사에서 개발한 복합막 모듈이 약 $10{\sim}20g/m^2hr$의 높은 투과도를 나타내었다. 테스트를 진행한 복합막 모듈의 내구성을 알아보기 위하여 약 35일간의 장기테스트를 진행하였고 그 결과 약 $510{\sim}520g/m^2hr$의 투과도와 20~25의 선택도로 초기 측정량과 큰 차이가 없음을 나타내었다.

Keywords

References

  1. C. Robert, J. Thomas, "The economics of gasoline ethanol blends", American petroleum institute, 45, 36 (1988).
  2. A. Baudot and M. Marin, "Dairy aroma compounds recovery by pervaporation", J. Membr. Sci., 50, 285 (1990). https://doi.org/10.1016/S0376-7388(00)80626-2
  3. R. A. Leonard, "Recent advances in centrifugal contactor design", Sep. Sci. Technol., 23, 1473 (1988). https://doi.org/10.1080/01496398808075643
  4. S. S. Kim and H. Y. Kim, "Preparation of pervaporation composite membrane for butanol separation", Membr. J., 19, 54-62 (2009).
  5. R. Y. M. Huang (Ed.), "Pervaporation membrane separation processes", Elsevier, Amsterdam (1991).
  6. X. Feng and R. Y. M. Huang, "Liquid separation by membrane pervaporation: a review", Ind. Eng. Chem. Tes., 36, 1048 (1997). https://doi.org/10.1021/ie960189g
  7. US Department of Energy, "Office of energy research, Office of program analysis", Membrane separation system., Contract No. DE-AC01-88ER30133 (1990).
  8. B. Smitha, D. Suhanya, S. Sridhar, and M. Ramakrishna, "Separation of organic-organic mixtures by pervaporation: a review", J. Membr. Sci., 241, 1 (2004). https://doi.org/10.1016/j.memsci.2004.03.042
  9. D. Roizard, R. Clement, P. Lochon, J. Kerres, and G. Eigenberger, "Synthesis, characterization and transport properties of a new siloxane-phosphazene copolymer. Extraction of n-butanol from water by pervaporation", J. Membr. Sci., 113, 151 (1996). https://doi.org/10.1016/0376-7388(95)00243-X
  10. X. Feng and R. Y. M. Huang, "Blended chitosan and polyvinyl alcohol membranes for the pervaporation dehydration of isopropanol", J. Membr. Sci., 280, 815 (2006). https://doi.org/10.1016/j.memsci.2006.03.001
  11. A. A. Kittur, S. M. Tambe, S. S. Kulkarni, and M. Y. Kariduraganavar, "Pervaporation separation of water-acetic acid mixtures through NaY zeolite in corporated sodium alginate membranes", J. Appl. Polym. Sci., 94, 2101 (2004). https://doi.org/10.1002/app.21149
  12. H. I. Shaban, "Using pervaporation technique to separate water from organic", Chem. Eng. Process, 35, 429 (1996). https://doi.org/10.1016/S0255-2701(96)04154-2
  13. J. Sekulic, J. T. Elshof, and D. H. A. Blank, "Selctive Pervaporation of water through a non-selective microporous titania membrane by a dynamically induced molecular sieving mechanism", Langmuir, 21, 508 (2005). https://doi.org/10.1021/la047458p
  14. H. S. Choi, Y. T. Park, S. T. Nam, J. H. Jeon, and S. L. Lee, "The preparation of a Polyimide membrane for the Separation of Water-Acetic Acid Mixture through Pervaporation", Membr. J., 9, 215-220 (1999).
  15. J. Jegal and K. H. Lee, "polymeric Materials for Pervaporation Membranes". Membr. J., 7, 157 (1997).
  16. C. O. Kweon and G. C. Paik, "A study on the removal of chlorinated organic hydrocarbon com-punds in wastewater using RTV (Room Tempera-ture Vulcanizing)-Silicon rubber (PDMS) membrane by pervaporation", J. Korea Society of Environ-ment Aidministation., 5, 385 (1999).
  17. D. P. Queiroz and M. N. D'Pinho, "Structural characteristics and gas permeation properties of polydimethylsiloxane/poly (propylene oxide) urethane/urea bi-soft segment membranes", J. Polymer, 46, 2346 (2005). https://doi.org/10.1016/j.polymer.2004.12.056
  18. B. D. Ratner, "Surface characterization of bio-materials by electron spectroscopy for chemical analysis", Analysis of Biomedical Engineering, 11, 313 (1983). https://doi.org/10.1007/BF02363290
  19. J.-W. Rhim and Y.-K. Kim, "Pervaporation separa-tion of MTBE-Methanol mixtures using cross-linked PVA membranes", J. Appl. Polym. Sci., 75, 1699 (2000). https://doi.org/10.1002/(SICI)1097-4628(20000401)75:14<1699::AID-APP3>3.0.CO;2-O
  20. J. Chen, J. Li., J. Chen, Y. Z. Lin, and X. Wang, "Pervaporation separation of ethyl thioether/heptanemixtures by polyethylene glycol membranes", Separation and Purification Technology., 66, 3 (2009).
  21. K. Y. Jee, E. J. Jeon, N. W. Kim, and Y. T. Lee, "Pervaporation of PVDF/PDMS composite membrane and separation of n-butanol/water mixtures by pervaporation", Membr. J., 19, 212 (2009).
  22. J. Huang and M. M. Meagher, "Pervaporative recovery of n-butanol from aqueous solutions and ABE fermentation broth using thin-film silicalite-film silicone composite membranes", J. Membr. Sci., 192, 231 (2001). https://doi.org/10.1016/S0376-7388(01)00507-5
  23. J. S. Kim, C. S. Lee, E. H. Cho, and J. W. Rhim, "Pervaporation separation of isopropyl alcohol-water mixtures using poly(dimethyl siloxane) membrane", Membr. J., 23, 245-250 (2013).
  24. S. J. Choe and T. K. Ahn, "Miscibility in aromatic polybenzimidazole/polyetherimide blends", J. Polymer, 15, 57-66 (1991).