미생물을 혼입한 콘크리트의 전기적 염화물 침투 저항 및 강도 특성 평가

An Assessment of Properties on Electrical Chloride Penetration Resistance and Compressive Strength of Micro-organism Mixed Concrete

  • 김화중 (경북대 건축토목공학부) ;
  • 김태훈 (경북대 건설환경에너지공학부 대학원) ;
  • 박성식 (경북대 건축토목공학부)
  • 투고 : 2015.08.17
  • 심사 : 2015.12.17
  • 발행 : 2015.12.30

초록

In recent years, river sand depletion has caused the increase of sea sand use. Chloride which exists in the sea sand promotes the rebar corrosion and causes degradation of durability in the RC concrete structures. In case of offshore RC structures, chloride causes the rebar corrosion and the salt damage which generates concrete cracks, although high quality river aggregates are used for the building construction. In this study, the concretes were produced by using a microorganism and the compressive strength test and the chloride ion penetration test were performed. Two tests(compressive strength, chloride ion penetration resistance) were carried out for performance evaluation of concrete. ${\phi}100mm{\times}200mm$ size specimens were made and 5 types of mixing water(2F-1, 5B, Urea medium, Marine broth medium and Ordinary water) were used to make concrete specimens and compressive strength test. All specimens were cured for 7, 28days. To evaluate chloride ion penetration resistance, ${\phi}100mm{\times}200mm$ specimens were cut and ${\phi}100mm{\times}50mm$ samples were prepared. The electrical chloride ion penetration testing method were performed in order to measure the chloride ion resistance and the test was progressed according to the contents of ASTM C1202-12. SEM and porosimeter analysis were performed in order to identify the microstructures of specimens. As a result of the tests, 2F-1 group had superior compressive strength and chloride ion penetration resistance to the others. Through this research, it was tried to examine the potential for reducing the defects of concrete and applying the micro-organism as a natural admixture material.

키워드

과제정보

연구 과제 주관 기관 : 경북대학교, 국토교통부

참고문헌

  1. Kim, S. (2012). The Influence of calcite nano material on microorganism mixed mortar, Journal of architectural institute of korea, 28(5), 77-85.
  2. Kim, S. (2015). Evaluation of compressive strength characteristic on micro-organism mixed blast furnace slag mortar, Journal of architectural institute of korea, 31(2), 721-28.
  3. Park, S. (2012). Application of alkaliphilic biofilm -forming bacteria to improve compressive strength of cement-sand mortar, Journal of microbiology and biotechnology, 22(3), 385-389. https://doi.org/10.4014/jmb.1110.10009
  4. Willem, D. M. (2010). Microbial carbonate precipitation in construction materials, Journal of Ecological Engineering, 36, 118-136. https://doi.org/10.1016/j.ecoleng.2009.02.006
  5. Yoon, J. (2003). An experimental study on salt damage resistance of high durable concrete, Journal of the korea institute of building construction, 3(3), 73-81. (Received Aug. 17 2015 Revised Oct. 6 2015 Accepted Dec. 17 2015) https://doi.org/10.5345/JKIC.2003.3.3.073