Effects of loading conditions on the fatigue failure characteristics in a polycarbonate

  • Okayasu, Mitsuhiro (Department of Materials Science and Engineering, Ehime University) ;
  • Yano, Kei (Department of Materials Science and Engineering, Ehime University) ;
  • Shiraishi, Tetsuro (Department of Materials Science and Engineering, Ehime University)
  • 투고 : 2014.05.03
  • 심사 : 2014.06.24
  • 발행 : 2014.11.27

초록

In this study, fatigue properties and crack growth characteristics of a polycarbonate (PC) were examined during cyclic loading at various mean stress (${\sigma}_{amp}$) and stress amplitude (${\sigma}_{mean}$) conditions. Different S vs. N and da/dN vs. ${\Delta}K$ relations were obtained depending on the loading condition. The higher fatigue strength and the higher resistance of crack growth are seen for the PC samples cyclically loaded at the higher mean stress and lower stress amplitude due to the low crack driving force. Non-linear S - N relationship was detected in the examination of the fatigue properties with changing the mean stress. This is attributed to the different crack growth rate (longer fatigue life): the sample loaded at the high mean stress with lower stress amplitude. Even if the higher stress amplitude, the low fatigue properties are obtained for the sample loaded at the higher mean stress. This was due to the accumulated strain energy to the sample, where severe plastic deformation occurs instead of crack growth (plasticity-induced crack closure). Shear bands and discontinuous crack growth band (DGB) are observed clearly on the fracture surfaces of the sample cyclically loaded at the high stress amplitude, where the lower the ${\sigma}_{mean}$, the narrower the shear band and DGB. On the other hand, final fracture occurred instantly immediately after the short crack growth occurs in the PC sample loaded at the high mean with the low ${\sigma}_{amp}$, i.e., tear fracture, in which the shear bands and DGB are not seen clearly.

키워드

과제정보

연구 과제 주관 기관 : Ehime University

참고문헌

  1. Bucknall, C.B. (2007), "New criterion for craze initiation", Polymer, 48, 1030-1041. https://doi.org/10.1016/j.polymer.2006.12.033
  2. Bucknall, C.B. (2012), "Role of surface chain mobility in crazing", Polymer, 53, 4778-4786. https://doi.org/10.1016/j.polymer.2012.08.034
  3. Fang, QZ., Wang, T.J. and Li, H.M. (2008), "Overload-induced retardation of fatigue crack growth in polycarbonate", Int. J. Fatigue, 30, 1419-1429. https://doi.org/10.1016/j.ijfatigue.2007.10.005
  4. Fang, Q.Z., Wang, T.J. and Li, H.M. (2007), "Overload effect of the fatigue crack propagation of PC/ABS alloy", Polymer 48, 6691-6706. https://doi.org/10.1016/j.polymer.2007.08.048
  5. James, M.N., Christopher, C.J., Lu, Y. and Patterson, E.A. (2012), "Fatigue crack growth and craze-induced crack tip shielding in polycarbonate", Polymer, 53, 1558-1570. https://doi.org/10.1016/j.polymer.2012.01.032
  6. Krongauz, V.A., Bosnjak, C.P. and Chudnovsky, A. (2009), "Use of photochromic spiropyran as a molecular probe of large strain in polycarbonate", High Energy Chem., 43, 400-405. https://doi.org/10.1134/S0018143909050117
  7. Kumai, S., Hu, J., Higo, Y. and Nunomura, S. (1996), "Effects of dendrite cell size and particle distribution on the near-threshold fatigue crack growth behavior of cast Al-SiCp composites", Acta Mater., 44, 2249-2257. https://doi.org/10.1016/1359-6454(95)00357-6
  8. Li, X., Hristov, H.A., Yee, A.F. and Gidley, D.W. (1995), "Influence of cyclic fatigue on the mechanical properties of amorphous polycarbonate", Polymer, 36, 759-765. https://doi.org/10.1016/0032-3861(95)93105-U
  9. Mills, N.J. and Walker, N. (1980), "Fatigue crack initiation in glassy plastics in high strain fatigue tests", J. Mater. Sci., 15, 1832-1840. https://doi.org/10.1007/BF00550604
  10. Mishnaevsky, Jr. L. and Brondsted, P. (2007), "Modeling of fatigue damage evolution on the basis of the kinetic concept of strength", Int. J. Fract. , 144, 149-158. https://doi.org/10.1007/s10704-007-9086-1
  11. Okayasu, M. and Yoshie, S. (2010), "Mechanical Properties of $Al-Si_{13}-Ni_{1.4}-Mg_{1.4}-Cu_1 $ Alloys Produced by the Ohno Continuous Casting Process", Mat. Sci. Eng. A, 527, 3120-3126. https://doi.org/10.1016/j.msea.2010.01.071
  12. Pitman, G. and Ward, I.M. (1980), "The molecular weight dependence of fatigue crack propagation in polycarbonate", J. Mater. Sci., 15, 635-645. https://doi.org/10.1007/BF00551728
  13. Pruitt, L. and Rondinone, D. (1996), "The effect of specimen thickness and stress ratio on the fatigue behavior of polycarbonate", Polym. Eng. Sci., 36, 1300-1305. https://doi.org/10.1002/pen.10524
  14. Puchi-Cabrera, E.S., Staia, M.H., Quinto, D.T., Villalobos-Gutierres, C. and Ochoa-Perez, E. (2007), "Fatigue properties of a SAE4340 steel coated with TiCN by PAPVD", Int. J. Fatigue, 29, 471-480. https://doi.org/10.1016/j.ijfatigue.2006.05.003
  15. Radon, J.C., Chauban, P. and Culver, L.E. (1976), "The influence of temperature and frequency on fatigue crack propagation in polymers", Colloid Polym. Sci., 254, 382-388. https://doi.org/10.1007/BF01382119
  16. Rae, P.J., Brown, E.N. and Orler, E.B. (2007), "The mechanical properties of poly (ether - ether - ketone)(PEEK) with emphasis on the large compressive strain response", Polymer, 48, 598-615. https://doi.org/10.1016/j.polymer.2006.11.032
  17. Singh, K.D., Parry, M.R. and Sinclair, I. (2011), "Variable amplitude fatigue growth behavior -a short overview", J. Mech. Sci. Tech., 25, 663-673. https://doi.org/10.1007/s12206-011-0132-6
  18. Skibo, M.D., Hertzberg, R.W., Manson, J.A. and Kim, S.L. (1977), "On the generality of discontinuous fatigue crack growth in glassy polymers", J. Mater. Sci., 15, 531-542.
  19. Wang, B., Lu, H., Tan, G. and Chen, W. (2003), "Strength of damaged polycarbonate after fatigue", Theor. Appl. Fract. Mech. 39, 163-168. https://doi.org/10.1016/S0167-8442(02)00156-8

피인용 문헌

  1. Design and analysis of low velocity impact on thermoplastic hat section with curvilinear profile vol.6, pp.1, 2017, https://doi.org/10.12989/amr.2017.6.1.065