Interfacial degradation of thermal barrier coatings in isothermal and cyclic oxidation test

  • Jeon, Seol (School of Materials Science and Engineering, Pusan National University) ;
  • Lee, Heesoo (School of Materials Science and Engineering, Pusan National University) ;
  • Choi, Youngkue (School of Materials Science and Engineering, Pusan National University) ;
  • Shin, Hyun-Gyoo (Mateiral Technology Center, Korea Testing Laboratory) ;
  • Jeong, Young-Keun (Department of Applied Hybrid Materials, Pusan National University)
  • 투고 : 2014.06.26
  • 심사 : 2014.07.18
  • 발행 : 2014.08.31
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

The degradation mechanisms of thermal barrier coatings (TBCs) were investigated in different thermal fatigue condition in terms of microstructural analyses. The isothermal and cyclic oxidation tests were conducted to atmospheric plasma sprayed-TBCs on NIMONIC 263 substrates. The delamination occurred by the oxide layer formation at the interface, the Ni/Cr-based oxide was formed after Al-based oxide layer grew up to ${\sim}10{\mu}m$ in the isothermal condition. In the cyclic oxidation with dwell time, the failure occurred earlier (500 hr) than in the isothermal oxidation (900 hr) at same temperature. The thickness of Al-based oxide layer of the delaminated specimen in the cyclic condition was ${\sim}4{\mu}m$ and the interfacial cracks were observed. The acoustic emission method revealed that the cracks generated during the cooling step. It was considered that the specimens were prevented from the formation of the Al-based oxide by cooling treatment, and the degradation mode in the cyclic test was dominantly interfacial cracking by the difference of thermal expansion coefficients of the coating layers.

키워드

참고문헌

  1. J.R. Nicholls, M.J. Deakin and D.S. Rickerby, "A comparison between the erosion behaviour of thermal spray and electron beam physical vapour deposition thermal barrier coatings", Wear 233 (1999) 352.
  2. D. Stover and C. Funke, "Directions of the development of thermal barrier coatings in energy applications", J. Mater. Process. Technol. 92 (1999) 195.
  3. W. Beele, G. Marijnissen and A. Van Lieshout, "The evolution of thermal barrier coatings-status and upcoming solutions for today's key issues", Surf. Coat. Technol. 120 (1999) 61.
  4. B.G. Choi, S.Y. Kim, C.W. Park, J.H. Park, Y.P. Hong and K.B. Shim, "Effect of deposition pressure on the morphology of $TiO_2$ nanoparticles deposited on $Al_2O_3$ powders by pulsed laser deposition", J. Korean Cryst. Growth Cryst. Technol. 23 (2013) 167. https://doi.org/10.6111/JKCGCT.2013.23.4.167
  5. N.P. Padture, M. Gell and E.H. Jordan, "Thermal barrier coatings for gas-turbine engine applications", Sci. 296 (2002) 280. https://doi.org/10.1126/science.1068609
  6. H. Echsler, V. Shemet, M. Schutze, L. Singheiser and W.J. Quadakkers, "Cracking in and around the thermally grown oxide in thermal barrier coatings: A comparison of isothermal and cyclic oxidation", J. Mater. Sci. 41 (2006) 1047. https://doi.org/10.1007/s10853-005-3639-3
  7. A.G. Evans, D.R Mumm, J.W. Hutchinson, G.H. Meier and F.S. Pettit, "Mechanisms controlling the durability of thermal barrier coatings", Prog. Mater. Sci. (2001) 505.
  8. M. Ranjbar-far, J. Absi, G. Mariaux and D.S. Smith, "Crack propagation modeling on the interfaces of thermal barrier coating system with different thickness of the oxide layer and different interface morphologies", J. Mat. Design. 32 (2011) 4961. https://doi.org/10.1016/j.matdes.2011.05.039
  9. X.Q. Cao, R. Vassen, F. Tietz and D. Stoever, "New double-ceramic-layer thermal barrier coatings based on zirconia.rare earth composite oxides", J. Eur. Ceram. Soc. 26 (2006) 247. https://doi.org/10.1016/j.jeurceramsoc.2004.11.007
  10. W.R. Chen, X. Wu, B.R. Marple, R.S. Lima and P.C. Patnaik, "Pre-oxidation and TGO growth behaviour of an air-plasma-sprayed thermal barrier coating", Surf. Coat. Technol. 202 (2008) 3787. https://doi.org/10.1016/j.surfcoat.2008.01.021
  11. A. Afrasiabi, M. Saremi and A. Kobayashi, "A comparative study on hot corrosion resistance of three types of thermal barrier coatings: YSZ, YSZ $+Al_2O_3$ and YSZ/$Al_2O_3$", Mat. Sci. Eng. A 478 (2008) 264. https://doi.org/10.1016/j.msea.2007.06.001
  12. M. Ranjbar-Far, J. Absi, G. Mariaux and F. Dubois, "Simulation of the effect of material properties and interface roughness on the stress distribution in thermal barrier coatings using finite element method", J. Mat. Design. 31 (2010) 772. https://doi.org/10.1016/j.matdes.2009.08.005
  13. M. Bialas, "Finite element analysis of stress distribution in thermal barrier coatings", Surf. Coat. Technol. 202 (2008) 6002. https://doi.org/10.1016/j.surfcoat.2008.06.178
  14. W. Nelson, "Accelerated testing: statistical models, test plans, and data analysis", 344 (John Wiley & Sons, New York, 2009).
  15. J.H. Jung, S.J. Yon and J.W. Seok, "Cubic zirconia single crystal growth using shell by skull melting method," J. Korean Cryst. Growth Cryst. Technol. 23 (2013) 124. https://doi.org/10.6111/JKCGCT.2013.23.3.124
  16. H.G. Shin, Y.K. Choi, S. Jeon, M.S. Jeon and H.S. Lee, "Design of durability and lifetime assessment method under thermomechanical stress for thermal barrier coatings", Korean J. Met. Mater. 52 (2014, In press).
  17. A.V. Drozdov "Investigation on the microcracking of ceramic materials using the acoustic emission method", Strength of Mater. 46 (2014) 71. https://doi.org/10.1007/s11223-014-9517-y
  18. M. Saremi, A. Afrasiabi and A. Kobayashi, "Bond coat oxidation and hot corrosion behavior of plasma sprayed YSZ coting on Ni superalloy", J. Transaction of JWRI 36 (2007) 41.
  19. A.C. Fox and T.W. Clyne, "Oxygen transport by gas permeation through the zirconia layer in plasma sprayed thermal barrier coatings", Surf. Coat. Technol. 184 (2004) 311. https://doi.org/10.1016/j.surfcoat.2003.10.018
  20. A.G. Evans, D.R. Mumm, J.W. Hutchinson, G.H. Meier and F.S. Pettit, "Mechanisms controlling the durability of thermal barrier coatings", Progress in Mater. Sci. 46 (2001) 505. https://doi.org/10.1016/S0079-6425(00)00020-7
  21. C.H. Hsueh, P.F. Becher, E.R. Fulle, S.A. Lange and W.C. Carter, "Surface-roughness induced residual stresses in thermal barrier coatings: computer simulations", In Mater. Sci. Forum 308 (1999) 442.
  22. A.M. Limarga, R. Vassen and D.R. Clarke, "Stress distributions in plasma-sprayed thermal barrier coatings under thermal cycling in a temperature gradient", J. Appl. Mech. 78 (2011) 011003-1. https://doi.org/10.1115/1.4002209
  23. J. Toscano, A. Gil, T. Huttel, E. Wessel, D. Naumenko, L. Singheiser and W.J. Quadakkers, "Temperature dependence of phase relationships in different types of MCrAlY-coatings", Surf. Coat. Technol. 202 (2007) 603. https://doi.org/10.1016/j.surfcoat.2007.06.044
  24. J. Toscano, R. Vaaen, A. Gil, M. Subanovic, D. Naumenko, L. Singheiser and W.J. Quadakkers, "Parameters affecting TGO growth and adherence on MCrAlY-bond coats for TBC's", Surf. Coat. Technol. 201 (2006) 3906. https://doi.org/10.1016/j.surfcoat.2006.07.247
  25. W. Brandl, H.J. Grabke, D. Toma and J. Kruger, "The oxidation behaviour of sprayed MCrAlY coatings", Surf. Coat. Technol. 86 (1996) 41.
  26. K.A. Khor and Y.W. Gu, "Effects of residual stress on the performance of plasma sprayed functionally graded $ZrO_2$-NiCoCrAlY coatings", Mater. Sci. Eng. A 277 (2000) 64. https://doi.org/10.1016/S0921-5093(99)00565-1
  27. M. Daroonparvar, M.S. Hussain and M.A.M. Yajid, "The role of formation of continues thermally grown oxide layer on the nanostructured NiCrAlY bond coat during thermal exposure in air", Appl. Surf. Sci. 261 (2012) 287. https://doi.org/10.1016/j.apsusc.2012.08.002
  28. M. Daroonparvar, M.S. Hussain and M.A.M. Yajid, "The role of formation of continues thermally grown oxide layer on the nanostructured NiCrAlY bond coat during thermal exposure in air", Appl. Surf. Sci. 261 (2012) 287. https://doi.org/10.1016/j.apsusc.2012.08.002
  29. B. Gudmundsson and B.E. Jacobson, "Structure Formation and Interdiffusion in Vacuum Plasma Sprayed CoNiCrAlY Coatings on IN738LC", Mater. Sci. Eng. 100 (1988) 207. https://doi.org/10.1016/0025-5416(88)90258-3
  30. M. Schutze, "Protective oxide scales and their breakdown", D. R. Holmes, Ed., Vol. 1 (John Wiley & Sons, Chichester, 1997).