Experimental study on fatigue crack propagation of fiber metal laminates

  • Xie, Zonghong (School of Astronautics, Northwestern Polytechnical University) ;
  • Peng, Fei (School of Astronautics, Northwestern Polytechnical University) ;
  • Zhao, Tianjiao (AVIC the First Aircraft Institute)
  • 투고 : 2014.02.02
  • 심사 : 2014.05.03
  • 발행 : 2014.08.25
⟨ 이전 논문 다음 논문 ⟩

초록

This study aimed to investigate the fatigue crack growth behavior of a kind of fiber metal laminates (FML) under four different stress levels. The FML specimen consists of three 2024-T3 aluminum alloy sheets and two layers of glass/epoxy composite lamina. Tensile-tensile cyclic fatigue tests were conducted on centrally notched specimen at four stress levels with various maximum values. A digital camera system was used to take photos of the propagating cracks on both sides of the specimens. Image processing software was adopted to accurately measure the length of the cracks on each photo. The test results show that: (1) a-N and da/dN-a curves of FML specimens can be divided into transient crack growth segment, steady state crack growth segment and accelerated crack growth segment; (2) compared to 2024-T3 aluminum alloy, the fatigue properties of FML are much better; (3) da/dN-${\Delta}K$ curves of FML specimens can be divided into fatigue crack growth rate decrease segment and fatigue crack growth rate increase segment; (3) the maximum stress level has a large influence on a-N, da/dN-a and da/dN-${\Delta}K$ curves of FML specimens; (4) the fatigue crack growth rate da/dN presents a nonlinear accelerated increasing trend to the maximum stress level; (5) the maximum stress level has an almost linear relationship with the stress intensity factor ${\Delta}K$.

키워드

참고문헌

  1. Alderliesten, R. (2005), Fatigue Crack Propagation and Delamination Growth In Glare, Delft University Press, Delft, South Holland, The Netherlands.
  2. Alderliesten, R.C. and Homan, J.J. (2006), "Fatigue and damage tolerance issues of Glare in aircraft structures", Int. J. Fatigue, 28(10), 1116-1123. https://doi.org/10.1016/j.ijfatigue.2006.02.015
  3. Alderliesten, R. and Rans, C. (2009), "The meaning of threshold fatigue in fibre metal laminates", Int. J. Fatigue, 31(2), 213-222. https://doi.org/10.1016/j.ijfatigue.2008.09.008
  4. Burianek, D.A., Giannakopoulos, A.E. and Spearing, S.M. (2003), "Modeling of facesheet crack growth in titanium-graphite hybrid laminates, part I", Engng. Fract. Mech., 70(6), 775-798. https://doi.org/10.1016/S0013-7944(02)00086-3
  5. Chang, P.Y. and Yang, J.M. (2008), "Modeling of fatigue crack growth in notched fiber metal laminates", Int. J. Fatigue, 30(12), 2165-2174. https://doi.org/10.1016/j.ijfatigue.2008.05.023
  6. Chang, P.Y., Yeh, P.C. and Yang, J.M. (2008), "Fatigue crack initiation in hybrid boron/glass/aluminum fiber metal laminates", Mater. Sci. Engng. A, 496(1), 273-280. https://doi.org/10.1016/j.msea.2008.07.041
  7. Khan, S.U., Alderliesten, R.C. and Benedictus, R. (2009), "Post-stretching induced stress redistribution in fibre metal laminates for increased fatigue crack growth resistance", Compos. Sci. Technol., 69(3), 396-405. https://doi.org/10.1016/j.compscitech.2008.11.006
  8. Khan, S.U., Alderliesten, R.C. and Benedictus, R. (2011), "Delamination in fiber metal laminates (GLARE) during fatigue crack growth under variable amplitude loading", Int. J. Fatigue, 33(9), 1292-1303. https://doi.org/10.1016/j.ijfatigue.2011.04.002
  9. Ma, Y., Xia, Z.C. and Xiong, X.F. (2014), "Fatigue crack growth in fiber-metal laminates", Sci. China Phys., Mech. Astron., 57(1), 83-89. https://doi.org/10.1007/s11433-013-5336-6
  10. Pitzer, C. and Yang, J.M. (2008), Hybrid Metal Laminate (HML) Manufacturing Planning Evaluation and Assessment, University of California, Los Angeles, CA, USA.
  11. Rans, C.D., Alderliesten, R.C. and Benedictus, R. (2011), "Predicting the influence of temperature on fatigue crack propagation in fibre metal laminates", Engng. Fract. Mech., 78(10), 2193-2201. https://doi.org/10.1016/j.engfracmech.2011.04.005
  12. Sinmazcelik, T., Avcu, E., Bora, M.O. and Coban, O. (2011), "A review: Fibre metal laminates, background, bonding types and applied test methods", Mater. Des., 32(7), 3671-3685. https://doi.org/10.1016/j.matdes.2011.03.011
  13. Vermeeren, C.A.J.R. (2003), "An historic overview of the development of fibre metal laminates", Appl. Compos. Mater., 10(4-5), 189-205. https://doi.org/10.1023/A:1025533701806
  14. Vlot, A. (2001), Glare: History of the Development of a New Aircraft Material, Kluwer Academic Publishers, Dordrecht, South Holland, The Netherlands.
  15. Vlot, A. and Gunnink, J.W. (2001), Fibre Metal Laminates: An Introduction, Kluwer Academic Publishers, Dordrecht, South Holland, The Netherlands.

피인용 문헌

  1. Effect of normal load on the crack propagation from pre-existing joints using Particle Flow Code (PFC) vol.19, pp.1, 2014, https://doi.org/10.12989/cac.2017.19.1.099
  2. Dilatation characteristics of the coals with outburst proneness under cyclic loading conditions and the relevant applications vol.14, pp.5, 2018, https://doi.org/10.12989/gae.2018.14.5.459