질소 보호 가스 첨가가 하이퍼 듀플렉스 스테인리스 밀봉용접재의 마모부식 저항성에 미치는 영향

Influence of the nitrogen gas addition in the Ar shielding gas on the erosion-corrosion of tube-to-tube sheet welds of hyper duplex stainless steel

  • Kim, Hye-Jin (Department of Materials Science and Engineering, Yonsei University) ;
  • Jeon, Soon-Hyeok (Department of Materials Science and Engineering, Yonsei University) ;
  • Kim, Soon-Tae (Department of Materials Science and Engineering, Yonsei University) ;
  • Lee, In-Sung (Department of Materials Science and Engineering, Yonsei University) ;
  • Park, Yong-Soo (Department of Materials Science and Engineering, Yonsei University)
  • 투고 : 2014.04.25
  • 심사 : 2014.04.28
  • 발행 : 2014.04.30

초록

Duplex stainless steels with nearly equal fraction of the ferrite(${\alpha}$) phase and austenite(${\gamma}$) phase have been increasingly used for various applications such as power plants, desalination facilities due to their high resistance to corrosion, good weldability, and excellent mechanical properties. Hyper duplex stainless steel (HDSS) is defined as the future duplex stainless steel with a pitting resistance equivalent (PRE=wt.%Cr+3.3(wt.%Mo+0.5wt.%W)+30wt.%N) of above 50. However, when HDSS is welded with gas tungsten arc (GTA), incorporation of nitrogen in the Ar shielding gas are very important because the volume fraction of ${\alpha}$-phase and ${\gamma}$-phase is changed and harmful secondary phases can be formed in the welded zone. In other words, the balance of corrosion resistance between two phases and reduction of $Cr_2N$ are the key points of this study. The primary results of this study are as follows. The addition of $N_2$ to the Ar shielding gas provides phase balance under weld-cooling conditions and increases the transformation temperature of the ${\alpha}$-phase to ${\gamma}$-phase, increasing the fraction of ${\gamma}$-phase as well as decreasing the precipitation of $Cr_2N$. In the anodic polarization test, the addition of nitrogen gas in the Ar shielding gas improved values of the electrochemical parameters, compared to the Pure Ar. Also, in the erosion-corrosion test, the HDSS welded with shielding gas containing $N_2$ decreased the weight loss, compared to HDSS welded with the Ar pure gas. This result showed the resistance of erosion-corrosion was increased due to increasing the fraction of ${\gamma}$-phase and the stability of passive film according to the addition $N_2$ gas to the Ar shielding gas. As a result, the addition of nitrogen gas to the shielding gas improved the resistance of erosion-corrosion.

키워드

참고문헌

  1. J. Olson, S. Nordin, Proc. Duplex Stainless Steel '86, The Hague, Netherlands, p. 219 (1986).
  2. E. Perteneder, J. Tosch, P. Reiterer, G. Rabensteiner, Proc. Duplex Stainless Steel '86, The Hague, Netherlands, p. 48 (1986).
  3. B. A. Sprengard, Effect of nitrogen concentration in shielding gas on microstructure and mechanical properties of ATI 2003 lean duplex stainless steel autogenou plasma Ar welding, the University of Cincinnati (2011).
  4. H .L. Cao, S. Hertzman: Duplex Stainless Steels '91, Proc. Conf., Les Editions de Physique, Paris, France, p. 363 (1991).
  5. S. Atamert, J. E. King, Mater. Sci. Technol., 8, 896 (1992). https://doi.org/10.1179/mst.1992.8.10.896
  6. J. C. Lippold, W. A. Baselack, and I. Varol, Weld. J., 71, 1 (1992).
  7. G. G. Kolchin, B. S. Ermakov, R. I. Grechin, Y. V. Gladnev, SteelUSSR, 17, 235 (1987).
  8. L. A. Norstrom, S. Pettersson, Z. Werkstofftech., 12, 229 (1981). https://doi.org/10.1002/mawe.19810120703
  9. M. Jones, R. J. Llewelly, CORROSION/2007, March 11-15, NACE International, Nashville, Tennessee (2007).
  10. E. Hussain, A. Husain, Desalination183 (1-3), 227 (2005). https://doi.org/10.1016/j.desal.2005.02.051
  11. A. Neville, T. Hodgkiess, J. T. Dallas, Wear 186-187, 497 (1995). https://doi.org/10.1016/0043-1648(95)07145-8
  12. S. S. Rajahram, T. J. Harvey, J. C. Walker, S. C. Wang, R J. K Wood, Tribology International, 46, 161 (2012). https://doi.org/10.1016/j.triboint.2011.05.012
  13. X. C Lu, S. Z Li, X. X Jiang, T. C Zhang, Corrosion (Houston, TX, US) 51, 456 (1995). https://doi.org/10.5006/1.3293612
  14. TCS 2006 TCFE5-TCS Steels/Fe-Alloys Database, v5.0 (Provieded by Thermo-Calc Software).
  15. J.O. Andersson, T. Helander, L. Hoglund, P. Shi, B. Sundman, CALPHAD : Comput. Coupling Phase Diagrams Thermochem., 26, 272 (2002).
  16. Annual Book of ASTM Standards, ASTM E562-02, Standard test method for determining volume fraction by systematic manual point count.
  17. J. C. Lippold, D. J. Kotecki, Welding Metallugy and Weldability of Stainless steels, John Wiley & Sons, Inc. (2005).
  18. J. W. Abtibol Menezes, H. Abreu, S. Kundu, H. K. D. H. Bhadeshia, P. M. Kelly, Science and Technology of Welding & Joining 14, 4 (2009). https://doi.org/10.1179/136217108X341166
  19. Annual Book of ASTM Standards, ASTM G 5.

피인용 문헌

  1. Variation of Mechanical Properties and Corrosion Properties with Mo Contents of Hyper Duplex Stainless-Steel Welds pp.2005-4149, 2018, https://doi.org/10.1007/s12540-018-0166-8