Abstract
For surface modification, bulk metallic glass coatings were fabricated using metallic glass powder and a mixture of a self-fluxing alloy or/and hard metal alloys with a heat-resisting property using a high velocity oxy-fuel coating thermal spraying process. Microstructural analyses and mechanical tests were carried out using X-ray diffraction, a scanning electron microscope, an atomic force microscope, a three-dimensional optical profiler, and nanoindenation. As a result, the monolithic metallic glass coating was found to consist of solid particle and lamellae regions that included many pores. Second phase-reinforced composite coatings with a self-fluxing alloy or/and hard metal alloy additives were employed with in-situ $Cr_2Ni_3$ precipitate or/and ex-situ WC particles in an amorphous matrix. The mechanical behaviors of the solid particles and lamella regions showed large hardness and elastic modulus differences. The mechanical properties of the particle regions in the metallic glass composite coatings were superior to those of the lamellae regions in the monolithic metallic glass coatings, but indicated similar trends in matrix region of all the coating layers.
비정질합금이 가지고 있는 우수한 기계적 성질과 화학적 특성을 부품소재에 표면개질을 목적으로 고속화염 용사법으로 대면적 코팅층을 형성하였고 내열성이 높은 자융성합금과 초경합금 성분들을 적절히 혼합하여 비정질기지 복합재료를 제조하여 코팅들의 미세조직 관찰과 나노인덴테이션을 이용한 미세표면의 기계적 거동을 분석하였다. 각 코팅층의 미세조직을 관찰한 결과, 단일상 비정질 코팅에는 미용융 입자와 lamellae 영역이 존재하고 자융성합금이 고용된 복합재에는 in-situ $Cr_2Ni_3$ 석출물, 자융성합금과 초경합금성분이 함께 혼합된 코팅층은 석출물과 ex-situ WC 강화입자가 공존하였다. 이들 미세표면의 기계적 거동은 제 2 상이 고용된 비정질 기지 복합재의 코팅층의 기계적 특성이 전체적으로 향상되었다.