Zr기 비정질 합금 다이캐스팅 주조품의 부식 특성에 미치는 블라스팅 처리의 영향

The Effect of Blasting Treatment on the Corrosion Characteristics in the Zr-based Amorphous Alloy Die Castings

  • 이병철 ((주)퍼포먼스머티리얼코리아) ;
  • 김성규 (부경대학교 신소재시스템공학과) ;
  • 박봉규 (부경대학교 신소재시스템공학과) ;
  • 배차헌 ((주)엠씨엠) ;
  • 박흥일 (부경대학교 신소재시스템공학과)
  • Lee, Byung-Chul (Performance Material Korea Co. Ltd.) ;
  • Kim, Sung-Gyoo (Department of Materials System Engineering, Pukyung National University) ;
  • Park, Bong-Gyu (Department of Materials System Engineering, Pukyung National University) ;
  • Bae, Cha-Hurn (Modern Casting and Metals. Co., Ltd.) ;
  • Park, Heung-Il (Department of Materials System Engineering, Pukyung National University)
  • 투고 : 2014.01.07
  • 심사 : 2014.04.25
  • 발행 : 2014.04.30
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

A Zr-based amorphous alloy specimen was produced by vacuum die casting process. The salt spray test was carried out using the specimens in the as-cast, $Al_2O_3$ and $ZrO_2$ particle blasted state. Using these specimens, the SEM-EDX and XRD analyses, DSC measurement and bending strength test were conducted. After the salt spray test, the specimens were not experienced phase change and thermal characteristics of the alloys were remained unchanged. In the as-cast specimen, corrosion products were not observed. However, in the $Al_2O_3$ particle blasted specimen, pitting corrosion occurred and the detected corrosion products were $ZrCl_2$ and $NaZrO_3$. Due to the salt spray test, bending strength of the $Al_2O_3$ blasted specimens showed about 100 MPa lower strength than the other specimens. The bending fracture surface was vein pattern which was shown typically in the amorphous alloys.

키워드

참고문헌

  1. A. Inoue, Acta Mater., "Stabilization of metallic supercooled liquid and bulk amorphous alloys", 48 (2000) 279-306. https://doi.org/10.1016/S1359-6454(99)00300-6
  2. A. Inoue, Sci. Rep. Res. Inst. Tohoku Univ., Ser. A42 (1996) 1.
  3. A. Leonard, L. Q. Xing, M. Heilmaier, A. Gebert, J. Eckert and L. Schultz. Nanostruct. Mater., "Effect of Crystalline Precipitations on the Mechanical Behavior of Bulk Glasee Forming Zr-based Alloys", 10 (1998) 805-817. https://doi.org/10.1016/S0965-9773(98)00117-2
  4. A. Gerbert, K. Buchholz, A. M. El-Aziz and J. Eckert, Mater. Sci. Eng., "Hot water corrosion behaviour of Zr-Cu-Al-Ni bulk metallic glass", A316 (2001) 60-65.
  5. S. Hiromoto, A. P. Tsai, M. Sumita and T. Hanawa, Mater, Trans. JIM, "Corrosion behaviour of $Zr_{65}Al_{7.5}Ni_{10}Cu_{17.5}$ bulk metallic glass", 42 (2001) 656-659. https://doi.org/10.2320/matertrans.42.656
  6. B. A. Green, R. V. Steward, I. Kim, C. K. Choi, P. K. Liaw, K. D. Kim and Y. Yokoyama, Intermetallics, "In-situ observation of pitting corrosion of the $Zr_{50}Cu_{40}Al_{10}$ bulk metallic glass", 17 (2009) p568-571. https://doi.org/10.1016/j.intermet.2008.12.011
  7. V. Schroeder and R. O. Ritchie, Acta Mater., "Stress-corrosion fatigue-crack growth in a Zr-based bulk amorphous metal", 54 (2006) 1785-1794. https://doi.org/10.1016/j.actamat.2005.12.006
  8. A. Inoue, T. Shibata and T. Zhang, Mater. Trans., JIM, "Effect of Additional Elements on Glass Transition Behavior and Glass Formation Tendency of Zr-Al-Cu-Ni Alloys", 36 (1995) 1420-1426. https://doi.org/10.2320/matertrans1989.36.1420
  9. A. Inoue. "Bulk Amorphous Alloys", Transtech Publications, Zurich, (1998).
  10. H. Choi-Yim and W. L. Johnson. Appl. Phys. Lett., "Bulk metallic glass matrix composites", 71 (1997) 3808-3810. https://doi.org/10.1063/1.120512
  11. C. C. Hays, J. Schroers, U. Geyer, S. Bissuyt, N. Stein and W. L. Johnson, J. Metastable and Nanocrystalline Mater., "Glass forming ability in the Zr-Nb-Ni-Cu-Al bulk metallic glasses", 8 (1999) 103-108.