Abstract
In the present work, PLA/PBS blends with poly(lactic acid) (PLA) and poly(butylene succinate) (PBS) at different contents were processed by using a twin-screw extruder and an injection molding machine, and then their mechanical, thermal and morphological properties were investigated. The mechanical properties such as flexural strength, flexural modulus, tensile strength and tensile modulus and thermal properties such as melting behavior, dynamic mechanical thermal properties and thermal stability significantly depended on the contents of PLA and PBS. However, the heat deflection temperature of the blends was not significantly influenced by the contents of PLA and PBS. Also, the fracture surfaces of PLA/PBS blends were changed from a brittle pattern to a ductile pattern with increasing the PBS contents.
본 연구에서는 이축압출기와 사출기를 사용하여 폴리유산(PLA)와 폴리부틸렌숙시네이트(PBS) 수지의 함량비를 달리하여 PLA/PBS 블랜드를 제조하고, 그들의 기계적, 열적 특성 및 모폴로지를 조사하였다. PLA/PBS 블랜드의 굴곡강도, 굴곡탄성률, 인장강도 및 인장탄성률과 같은 기계적 특성, 그리고 용융거동, 동역학적 열특성 및 열안정성과 같은 열적 특성이 PLA와 PBS 함량비에 크게 의존하였다. 그러나 PLA/PBS 블랜드의 열변형온도는 PLA 또는 PBS 함량 변화에 크게 영향을 받지 않았다. 또한 PLA/PBS 블랜드의 파단면은 PBS 함량이 증가함에 따라 brittle 양상으로부터 ductile 양상으로 변화되었다.