Surface microhardness of three thicknesses of mineral trioxide aggregate in different setting conditions

  • Shokouhinejad, Noushin (Department of Endodontics, School of Dentistry and Dental Research Center, Dentistry Research Institute, Tehran University of Medical Sciences) ;
  • Jafargholizadeh, Leila (School of Dentistry, Tehran University of Medical Sciences) ;
  • Khoshkhounejad, Mehrfam (Department of Endodontics, School of Dentistry and Dental Research Center, Dentistry Research Institute, Tehran University of Medical Sciences) ;
  • Nekoofar, Mohammad Hossein (Department of Endodontics, School of Dentistry and Dental Research Center, Dentistry Research Institute, Tehran University of Medical Sciences) ;
  • Raoof, Maryam (Department of Endodontics, School of Dentistry, Oral and Dental Diseases Research Center, Kerman University of Medical Sciences)
  • Received : 2014.03.29
  • Accepted : 2014.05.27
  • Published : 2014.11.29

Abstract

Objectives: This study aimed to compare the surface microhardness of mineral trioxide aggregate (MTA) samples having different thicknesses and exposed to human blood from one side and with or without a moist cotton pellet on the other side. Materials and Methods: Ninety cylindrical molds with three heights of 2, 4, and 6 mm were fabricated. In group 1 (dry condition), molds with heights of 2, 4, and 6 mm (10 molds of each) were filled with ProRoot MTA (Dentsply Tulsa Dental), and the upper surface of the material was not exposed to any additional moisture. In groups 2 and 3, a distilled water- or phosphate-buffered saline (PBS)-moistened cotton pellet was placed on the upper side of MTA, respectively. The lower side of the molds in all the groups was in contact with human blood-wetted foams. After 4 day, the Vickers microhardness of the upper surface of MTA was measured. Results: In the dry condition, the 4 and 6 mm-thick MTA samples showed significantly lower microhardness than the 2 mm-thick samples (p = 0.003 and p = 0.001, respectively). However, when a distilled water- or PBS-moistened cotton pellet was placed over the MTA, no significant difference was found between the surface microhardness of samples having the abovementioned three thicknesses of the material (p = 0.210 and p = 0.112, respectively). Conclusions: It could be concluded that a moist cotton pellet must be placed over the 4 to 6 mm-thick MTA for better hydration of the material. However, this might not be necessary when 2 mm-thick MTA is used.

Keywords

References

  1. Torabinejad M, Chivian N. Clinical applications of mineral trioxide aggregate. J Endod 1999;25:197-205. https://doi.org/10.1016/S0099-2399(99)80142-3
  2. Lee SJ, Monsef M, Torabinejad M. Sealing ability of a mineral trioxide aggregate for repair of lateral root perforations. J Endod 1993;19:541-544. https://doi.org/10.1016/S0099-2399(06)81282-3
  3. Dominguez MS, Witherspoon DE, Gutmann JL, Opperman LA. Histological and scanning electron microscopy assessment of various vital pulp-therapy materials. J Endod 2003;29:324-333. https://doi.org/10.1097/00004770-200305000-00003
  4. de Souza Costa CA, Duarte PT, de Souza PP, Giro EM, Hebling J. Cytotoxic effects and pulpal response caused by a mineral trioxide aggregate formulation and calcium hydroxide. Am J Dent 2008;21:255-261.
  5. Camp JH. Diagnosis dilemmas in vital pulp therapy: treatment for the toothache is changing, especially in young, immature teeth. Pediatr Dent 2008;30:197-205.
  6. Camilleri J, Montesin FE, Brady K, Sweeney R, Curtis RV, Ford TR. The constitution of mineral trioxide aggregate. Dent Mater 2005;21:297-303. https://doi.org/10.1016/j.dental.2004.05.010
  7. Walker MP, Diliberto A, Lee C. Effect of setting conditions on mineral trioxide aggregate flexural strength. J Endod 2006;32:334-336. https://doi.org/10.1016/j.joen.2005.09.012
  8. Witherspoon DE, Ham K. One-visit apexification: technique for inducing root-end barrier formation in apical closures. Pract Proced Aesthet Dent 2001;13:455-460.
  9. Matt GD, Thorpe JR, Strother JM, McClanahan SB. Comparative study of white and gray mineral trioxide aggregate (MTA) simulating a one- or two-step apical barrier technique. J Endod 2004;30:876-879. https://doi.org/10.1097/01.don.0000136213.93171.45
  10. Gancedo-Caravia L, Garcia-Barbero E. Influence of humidity and setting time on the push-out strength of mineral trioxide aggregate obturations. J Endod 2006;32:894-896. https://doi.org/10.1016/j.joen.2006.03.004
  11. Budig CG, Eleazer PD. In vitro comparison of the setting of dry ProRoot MTA by moisture absorbed through the root. J Endod 2008;34:712-714. https://doi.org/10.1016/j.joen.2008.03.004
  12. DeAngelis L, Chockalingam R, Hamidi-Ravari A, Hay S, Lum V, Sathorn C, Parashos P. In vitro assessment of mineral trioxide aggregate setting in the presence of interstitial fluid alone. J Endod 2013;39:402-405. https://doi.org/10.1016/j.joen.2012.11.010
  13. Eid AA, Komabayashi T, Watanabe E, Shiraishi T, Watanabe I. Characterization of the mineral trioxide aggregate-resin modified glass ionomer cement interface in different setting conditions. J Endod 2012;38:1126-1129. https://doi.org/10.1016/j.joen.2012.04.013
  14. Tsujimoto M, Tsujimoto Y, Ookubo A, Shiraishi T, Watanabe I, Yamada S, Hayashi Y. Timing for composite resin placement on mineral trioxide aggregate. J Endod 2013;39:1167-1170. https://doi.org/10.1016/j.joen.2013.06.009
  15. Sarkar NK, Caicedo R, Ritwik P, Moiseyeva R, Kawashima I. Physicochemical basis of the biologic properties of mineral trioxide aggregate. J Endod 2005;31:97-100. https://doi.org/10.1097/01.DON.0000133155.04468.41
  16. Reyes-Carmona JF, Felippe MS, Felippe WT. Biomineralization ability and interaction of mineral trioxide aggregate and white portland cement with dentin in a phosphate-containing fluid. J Endod 2009;35:731-736. https://doi.org/10.1016/j.joen.2009.02.011
  17. Shokouhinejad N, Nekoofar MH, Razmi H, Sajadi S, Davies TE, Saghiri MA, Gorjestani H, Dummer PM. Bioactivity of EndoSequence root repair material and bioaggregate. Int Endod J 2012;45:1127-1134. https://doi.org/10.1111/j.1365-2591.2012.02083.x
  18. Giuliani V, Baccetti T, Pace R, Pagavino G. The use of MTA in teeth with necrotic pulps and open apices. Dental Traumatol 2002;18:217-221. https://doi.org/10.1034/j.1600-9657.2002.02107.x
  19. Hachmeister DR, Schindler WG, Walker WA 3rd, Thomas DD. The sealing ability and retention characteristics of mineral trioxide aggregate in a model of apexification. J Endod 2002;28:386-390. https://doi.org/10.1097/00004770-200205000-00010
  20. Lee YL, Lee BS, Lin FH, Yun Lin A, Lan WH, Lin CP. Effects of physiological environments on the hydration behavior of mineral trioxide aggregate. Biomaterials 2004;25:787-793. https://doi.org/10.1016/S0142-9612(03)00591-X
  21. Nekoofar MH, Adusei G, Sheykhrezae MS, Hayes SJ, Bryant ST, Dummer PM. The effect of condensation pressure on selected physical properties of mineral trioxide aggregate. Int Endod J 2007;40:453-461. https://doi.org/10.1111/j.1365-2591.2007.01236.x
  22. Danesh G, Dammaschke T, Gerth HU, Zandbiglari T, Schafer E. A comparative study of selected properties of ProRoot mineral trioxide aggregate and two Portland cements. Int Endod J 2006;39:213-219. https://doi.org/10.1111/j.1365-2591.2006.01076.x
  23. Namazikhah MS, Nekoofar MH, Sheykhrezae MS, Salariyeh S, Hayes SJ, Bryant ST, Mohammadi MM, Dummer PM. The effect of pH on surface hardness and microstructure of mineral trioxide aggregate. Int Endod J 2008;41:108-116.
  24. Kayahan MB, Nekoofar MH, Kazandag M, Canpolat C, Malkondu O, Kaptan F, Dummer PM. Effect of acid-etching procedure on selected physical properties of mineral trioxide aggregate. Int Endod J 2009;42:1004-1014. https://doi.org/10.1111/j.1365-2591.2009.01610.x
  25. Chandler H. Hardness testing. 2nd ed. Materials Park, OH: ASM International; 1999. p1-13.
  26. Nekoofar MH, Oloomi K, Sheykhrezae MS, Tabor R, Stone DF, Dummer PM. An evaluation of the effect of blood and human serum on the surface microhardness and surface microstructure of mineral trioxide aggregate. Int Endod J 2010;43:849-858. https://doi.org/10.1111/j.1365-2591.2010.01750.x
  27. Oloomi K, Saberi E, Mokhtari H, Mokhtari Zonouzi HR, Nosrat A, Nekoofar MH, Dummer PM. Evaluation of the effect of blood contamination on the compressive strength of MTA modified with hydration accelerators. Restor Dent Endod 2013;38:128-133. https://doi.org/10.5395/rde.2013.38.3.128
  28. Vanderweele RA, Schwartz SA, Beeson TJ. Effect of blood contamination on retention characteristics of MTA when mixed with different liquids. J Endod 2006;32:421-424. https://doi.org/10.1016/j.joen.2005.09.007
  29. Chang SW. Chemical characteristics of mineral trioxide aggregate and its hydration reaction. Restor Dent Endod 2012;37:188-193. https://doi.org/10.5395/rde.2012.37.4.188
  30. Pelliccioni GA, Vellani CP, Gatto MR, Gandolfi MG, Marchetti C, Prati C. Proroot mineral trioxide aggregate cement used as a retrograde filling without addition of water: an in vitro evaluation of its microleakage. J Endod 2007;33:1082-1085. https://doi.org/10.1016/j.joen.2007.04.009
  31. Tay FR, Pashley DH, Rueggeberg FA, Loushine RJ, Weller RN. Calcium phosphate phase transformation produced by the interaction of the portland cement component of white mineral trioxide aggregate with a phosphate-containing fluid. J Endod 2007;33:1347-1351. https://doi.org/10.1016/j.joen.2007.07.008
  32. Gandolfi MG, Ciapetti G, Taddei P, Perut F, Tinti A, Cardoso MV, Van Meerbeek B, Prati C. Apatite formation on bioactive calcium-silicate cements for dentistry affects surface topography and human marrow stromal cells proliferation. Dent Mater 2010;26:974-992. https://doi.org/10.1016/j.dental.2010.06.002

Cited by

  1. Evaluation of the bioactivity of fluoride-enriched mineral trioxide aggregate on osteoblasts vol.51, pp.8, 2018, https://doi.org/10.1111/iej.12905
  2. Antimicrobial and antibiofilm activities of MTA supplemented with bismuth lipophilic nanoparticles vol.36, pp.4, 2014, https://doi.org/10.4012/dmj.2016-259
  3. Assessment of Mineral Trioxide Aggregate Setting in Simulated Root Canal with Different Root Canal Wall Thickness: In Vitro Study vol.11, pp.4, 2021, https://doi.org/10.3390/app11041727