Atmospheric corrosion rate and corrosivity categories of industrial metals in Asan area

아산지역에서 산업재료의 대기부식속도 측정

  • Kim, Jin-Hyung (Department of Meterials Engineering, Soonchunhyang University) ;
  • Lee, Jong-Kwon (Department of Meterials Engineering, Soonchunhyang University)
  • 김진형 (순천향대학교 신소재공학과) ;
  • 이종권 (순천향대학교 신소재공학과)
  • Received : 2013.07.04
  • Accepted : 2013.10.10
  • Published : 2013.10.31

Abstract

The atmospheric corrosion rate were measured in Asan area for four years according to ISO 9224. The tested metals chosen as the most frequently used in industry, aluminum were copper, carbon steel, weathgering steel, and galvanized steel. The assessed corrosivity categories was 3 in average. The corrosivity categories of asan area was higher than typical rural area and even urban area, whereas it slightly lower than marine area. The results were discussed, specially as the regional climatic characteristics.

4년간 아산지역에서 5가지 산업재료의 부식속도를 측정하였다. 이 연구는 전국의 21개 지역을 농촌, 해안, 공업도시로 구분하여 그 중 아산지역에서 시편을 대기에 노출 시켰을 때의 부식속도를 알아보고 이를 산업용으로 사용되는 금속의 Database로 하고자 하였다. 실험에 사용된 시편은 산업재료로 많이 사용되는 알루미늄, 구리, 탄소강, 내후성강, 아연도강이다. 탄소강과 내후성강의 부식속도와 무게감소량이 다른 금속에 비해 높았으며 sanding 처리한 시편의 부식속도가 sanding처리하지 않은 시편보다 부식속도가 낮게 나타났다. 아산 지역의 평균 Corrosion categories는 3으로 나타났다. 아산지역의 Corrosion categories는 해안지역보다는 낮게 나타났으며 농촌지역보다는 높게 나타났다. 염화물 이온의 농도가 커짐에 따라 부식속도가 커지는 경향을 나타낸다.

Keywords

References

  1. ISO 9224/1992, Corrosion of metals and alloys corrosivity of atmospheres - Guiding values for the corrosivity categories.
  2. J.C.Kim, J.Y.Ahn, A.Y.Shin, M.Y.Sung, S.A.Noh, J.S.Son, J.H.Park, S.J.Lee, "The Study for a Regional Scale Variation of Acid Deposition and Its Impact on the Ecosystem", National Institude of Environmental Research 2010
  3. Johan Tidblad, Atmospheric corrosion of metals in 2010-2039 and 2070-2099, Atmospheric Environment 55, 1-6, 2012 DOI: http://dx.doi.org/10.1016/j.atmosenv.2012.02.081
  4. Yuantai Ma, Ying Li, Fuhui Wang, The atmosperic corrosion kinetics of low carbon steel in a tropical marine environment, Corrosion Science 52, 1796-1800, 2010 DOI: http://dx.doi.org/10.1016/j.corsci.2010.01.022
  5. F.Corvo, J.Minotas, J.Delgado, C.Arroyave, Changes in atmospheric corrosion rate caused by chloride ions depending on rain regime, Corrosion Science 47, 883-892, 2005 DOI: http://dx.doi.org/10.1016/j.corsci.2004.06.003
  6. Antonio R. Mendoza, Francisco Corvo, Outdoor and indoor atmospheric corrosion of non-ferrous metals, Corrosion science 42, 1123-1147, 2000 DOI: http://dx.doi.org/10.1016/S0010-938X(99)00135-3
  7. Tran Thi Ngoc Lan, Nguyen Thi Phuong Thoa, R. Nishimura, Y. Tsujino, M. Yokoi, Y. Maeda, Atmospheric corrosion of carbon steel under field exposure in the southern part of Vietnam, Corrosion science 48 179-192 2006 DOI: http://dx.doi.org/10.1016/j.corsci.2004.11.018