Constraint-based fracture mechanics analysis of cylinders with internal circumferential cracks

  • Bach, Michael (Department of Mechanical and Aerospace Engineering, Carleton University) ;
  • Wang, Xin (Department of Mechanical and Aerospace Engineering, Carleton University)
  • 투고 : 2012.06.02
  • 심사 : 2013.07.03
  • 발행 : 2013.07.10

초록

In this paper, constraint-based fracture mechanics analyses of hollow cylinders with internal circumferential crack under tensile loading are conducted. Finite element analyses of the cracked cylinders are carried out to determine the fracture parameters including elastic T-stresses, and fully-plastic J-integrals. Linear elastic finite element analysis is conducted to obtain the T-stresses, and elastic-plastic analysis is conducted to obtain the fully plastic J-integrals. A wide range of cylinder geometries are studied, with cylinder radius ratios of $r_i/r_o$ = 0.2 to 0.8 and crack depth ratio a/t = 0.2 to 0.8. Fully plastic J-integrals are obtained for Ramberg-Osgood power law hardening material of n = 3, 5 and 10. These fracture parameters are then used to construct conventional and constraint-based failure assessment diagrams (FADs) to determine the maximum load carrying capacity of cracked cylinders. It is demonstrated that these tensile loaded cylinders with circumferential cracks are under low constraint conditions, and the load carrying capacity are higher when the low constraint effects are properly accounted for, using constraint-based FADs, comparing to the predictions from the conventional FADs.

키워드

참고문헌

  1. ABAQUS, User's Manual (2008), Version 6.8, Habbitt, Karlsson& Sorensen Inc.
  2. Ainsworth, R.A. and O'Dowd, N.P. (1995), "Constraint in the failure assessment diagram approach for fracture assessment", ASME Journal of Pressure Vessel Technology, 117, 260-267. https://doi.org/10.1115/1.2842121
  3. Ainsworth, R.A., Sattari-Far, I., Sherry, A.H., Hooton, D.G. and Hadley, I. (2000), "Methods for including constraint effects within SINTAP procedures", Engineering Fracture Mechanics, 67, 563-571. https://doi.org/10.1016/S0013-7944(00)00074-6
  4. Anderson, T.L. (1991), "Fracture mechanics: fundamentals and applications", Boca Raton: CRC Press, 91, 283-298.
  5. ASME, Boiler and Pressure Vessel Code, Section II, Materials, 2001 Edition.
  6. Betegon, C. and Hancock, J.W. (1991), "Two-parameter characterization of elastic-plastic crack tip fields", ASME Journal of Applied Mechanics, 58, 104-110. https://doi.org/10.1115/1.2897135
  7. Bilby, B.A., Cardew, G.E., Goldthorpe, M.R. and Howard, I.C. (1986), "A finite element investigation of the effect of specimen geometry on the fields of stress and strain at the tips of stationary cracks", Size Effect in Fracture, London: Mechanical Engineering Publications Limited, 37-46.
  8. BS97910 (1999), "Guide on methods for assessing the acceptability of flawsin metallic structures", British Standards Institution.
  9. Du, Z.Z. and Hancock, J.W. (1991), "The effect of non-singular stresses on crack tip constraint", Journal of Mechanical Physics and Solids, 39, 555-567. https://doi.org/10.1016/0022-5096(91)90041-L
  10. Gonzalez-Albuixech, V.F., Giner, E., Fernandez-Seaz, J. and Fernandez-Canteli, A. (2011), "Influence of the T33-stress on the 3D stress state around corner cracks in an elastic plate", Engineering Fracture Mechanics, 78, 412-427. https://doi.org/10.1016/j.engfracmech.2010.11.003
  11. He, M.Y. and Hutchinson, J.W. (1981), "The penny-shaped crack and the plane strain crack in an infinite body of power-law material", ASME Journal of Applied Mechanics, 48, 830-840. https://doi.org/10.1115/1.3157742
  12. Kumar, V., German, M.D. and Shih, C.F. (1981), "An engineering approach for elastic-plastic fracture analysis", EPRI Report NP-1931, Electric Power Research Institute, Palo Alto, CA.
  13. Larsson, S.G. and Carlsson, A.J. (1973), "Influence of non-singular stress terms and specimen geometry on small-scale yielding at crack-tips in elastic-plastic materials", Journal of the Mechanics and Physics of Solids, 21, 447-473. https://doi.org/10.1016/0022-5096(73)90012-4
  14. Lewis, T. and Wang, X. (2008), "The T-stress solutions for through-wall circumferential cracksin cylinders subjected to general loading conditions", Engineering Fracture Mechanics, 75, 3206-3225. https://doi.org/10.1016/j.engfracmech.2007.12.001
  15. Lidbury, D.P.G., Sherry, A.H., Bass, B.R. et al. (2006), "Validation of constraint-based methodology in structural integrity of ferritic steels for nuclear reaction pressure vessels", Fatigue and Fracture of Engineering Materials and Structures, 29, 829-849. https://doi.org/10.1111/j.1460-2695.2006.01057.x
  16. Meshii, T. and Tanaka, T. (2010), "Experimental T33-stress formulation of test specimen thickness effect on fracture toughness in the transition temperature region", Engineering Fracture Mechanics, 77, 867-877. https://doi.org/10.1016/j.engfracmech.2010.01.014
  17. Meshii, T., Tanaka, T. and Lu, K. (2010), "T-stress solutions for a semi-elliptical axial surface crack in a cylinder subjected to mode I non-uniform stress distributions", Engineering Fracture Mechanics, 77,2467-2478. https://doi.org/10.1016/j.engfracmech.2010.06.007
  18. Nakamura, T. and Parks, D.M. (1992), "Determination of elastic T-stress along three dimensional crack fronts using an interaction integral", International Journal of Solids and Structure, 29, 1597-1611. https://doi.org/10.1016/0020-7683(92)90011-H
  19. Qian, X. (2010), "KI-T estimations for embedded flaws in pipes - Part I: axially orientated cracks", International Journal of Pressure Vessels and Piping, 87, 134-149. https://doi.org/10.1016/j.ijpvp.2010.03.003
  20. Qu, J. and Wang, X. (2006), "Solutions of T-stress for quarter-elliptical corner cracks in finite thickness plates subject to tension and bending", International Journal of Pressure Vessels and Piping, 83, 593-606. https://doi.org/10.1016/j.ijpvp.2006.04.003
  21. R6 (1997), "Assessment of the integrity of structures containing defects, procedure R6, Revision 3", Nuclear Electric Ltd, Gloucester, U.K.
  22. Rice, J.R. (1974), "Limitations to the small scale yielding approximation for crack tip plasticity", Journal of the Mechanics and Physics of Solids, 22, 17-26. https://doi.org/10.1016/0022-5096(74)90010-6
  23. Sherry, A.H., France, C.C. and Goldthorpe, M.R. (1995), "Compendium of T-stress solutions for two and three dimensional cracked geometries", Fatigue Fracture Engineering Material Structure, 18, 141-155. https://doi.org/10.1111/j.1460-2695.1995.tb00148.x
  24. Sherry, A.H., Wilkes. M.A., Beardsmore, D.W. and Lidbury, D.P.G. (2005), "Material constraint parameters for the assessment of shallow defects in structural components?Part I: Parameter solutions", Engineering Fracture Mechanics,72, 2373-2395. https://doi.org/10.1016/j.engfracmech.2004.12.009
  25. Wang, X. (2002), "Elastic T-stress for cracks in test specimens subjectedto non-uniform stress distributions",Engineering Fracture Mechanics, 69, 1339-1352. https://doi.org/10.1016/S0013-7944(01)00149-7
  26. Wang, X. (2004), "Elastic T-stress solutions for penny-shaped cracks under tension and bending",Engineering Fracture Mechanics, 71, 2283-2298. https://doi.org/10.1016/j.engfracmech.2004.02.001
  27. Wang, X. (2006), "Fully plastic J-integral solutions for surface cracked plates under biaxial loading", Engineering Fracture Mechanics, 73, 1581-1595. https://doi.org/10.1016/j.engfracmech.2005.12.014
  28. Williams, M.L. (1957), "On the stress distribution at the base of a stationary crack", ASME Journal of Applied Mechanics, 24, 111-114.

피인용 문헌

  1. A modified hybrid method to estimate fracture resistance curve for pipes with a circumferential surface crack 2018, https://doi.org/10.1016/j.engfracmech.2017.05.046
  2. Modeling and optimization of a cracked pipeline under pressure by an interactive method: design of experiments 2017, https://doi.org/10.1007/s12008-017-0385-0
  3. Probabilistic Fracture Mechanics for Analysis of Longitudinal Cracks in Pipes Under Internal Pressure vol.18, pp.6, 2018, https://doi.org/10.1007/s11668-018-0564-8
  4. Failure Analyses of Propagation of Cracks in Repaired Pipe Under Internal Pressure vol.19, pp.1, 2019, https://doi.org/10.1007/s11668-019-00592-3