The Fundamental Properties of Alkali-Activated Slag Cement (AASC) Mortar with Different Water-Binder Ratios and Fine Aggregate-Binder Ratios

물-결합재 비와 잔골재-결합재 비에 따른 알칼리 활성화 슬래그 모르타르의 기초특성

  • 김태완 (부산대학교 생산기술연구소) ;
  • 함형길 (부산대학교 토목공학과) ;
  • 이성행 (부산대학교 토목공학과) ;
  • 엄장섭 (창신대학교 토목공학과)
  • Received : 2013.03.13
  • Accepted : 2013.07.12
  • Published : 2013.09.30
Download PDF
⟨ Previous Next ⟩

Abstract

This study investigates the fundamental properties of the water-binder (W/B) ratio and fine aggregate-binder (F/B) ratio in the alkali-activated slag cement (AASC) mortar. The W/B ratios are 0.35, 0.40, 0.45, and 0.50, respectively. And then the F/B ratios varied between 1.00 and 3.00 at a constant increment of 0.25. The alkali activator was an 2M and 4M NaOH. The measured mechanical properties were compared, flow, compressive strength, absorption, ultra sonic velocity, and dry shrinkage. The flow, compressive strength, absorption, ultra sonic velocity and dry shrinkage decreased with increases W/B ratio. The compressive strength decreases with increase F/B ratio at same W/B ratio. Also, at certain value of F/B ratio significant increase in strength is observed. And S2 (river sand 2) had lower physical properties than S1 (river sand 1) due to the fineness modulus. The results of experiments indicated that the mechanical properties of AASC depended on the W/B ratio and F/B ratio. The optimum range for W/B ratios and F/B ratios of AASC is suggested that the F/B ratios by 1.75~2.50 at each W/B ratios. Moreover, the W/(B+F) ratios between 0.13 and 0.14 had a beneficial effect on the design of AASC mortar.

본 연구는 물-결합재 비 (W/B)와 잔골재-결합재 비 (F/B)에 따른 알칼리 활성화 슬래그 시멘트 (AASC)의 기초 특성에 관한 연구이다. W/B 비는 0.35, 0.40, 0.45, 그리고 0.50를 선정하였다. 그리고 F/B 비는 1.00에서 3.00까지 0.25 크기로 고려하였다. 알칼리 활성화제는 2M과 4M의 NaOH를 사용하였다. 실험은 플로우, 흡수율, 압축강도, 초음파 속도 그리고 건조수축을 측정하여 비교하였다. 플로우, 압축강도, 흡수율, 초음파 속도 그리고 건조수축 모두 W/B 비가 증가하면 감소하였다. 압축강도는 동일 W/B 비에서 F/B 비가 증가할수록 감소하였다. 또한 특정 F/B 비에서 강도가 증가하는 것을 볼 수 있었다. 그리고 S2 (river sand 2)는 S1 (river sand 1)보다 낮은 물리적 특성을 나타냈는데, 이는 조립률 때문으로 판단된다. 본 실험의 결과 AASC의 공학적 특성은 W/B 비와 F/B 비가 영향을 주는 것으로 판단된다. 최적의 F/B 비는 각 W/B 비에 대해 1.75~2.50 인 것으로 생각된다. 또한 W/(B+F) 비가 0.13과 0.14 사이일 때 AASC 모르타르의 배합설계가 효과적일 것으로 판단된다.

Keywords

References

  1. Atis, C. D., Bilim, C., Celik, O., Karahan, O., "Influence of activator on the strength and drying shrinkage of alkaliactivated slag mortar", Construction and Building Materials, Vol. 23, 2009, pp.548-555. https://doi.org/10.1016/j.conbuildmat.2007.10.011
  2. Bernal, S. A., Mejia de Gutierrez, R., Pedraza, A. L., Provis, J. L., Rodriguez, E. D., Delvasto, S., "Effect of binder content on the performance of alkali-actiated slag concretes", Cement and Concrete Research, Vol. 41, 2011, pp.1-8. https://doi.org/10.1016/j.cemconres.2010.08.017
  3. Bilim, C., Karahan, O., Atis, C. D., Ilkentapar, S., "Influence of admixtures on the properties of alkali-activated slag mortars subjected to different curing conditions", Materials and Design, Vol. 44, 2013, pp.540-547. https://doi.org/10.1016/j.matdes.2012.08.049
  4. Burciaga-Diaz, O., Diaz-Guillen, M. R., Fuentes, A. F., Escalante-Garcia, J. I., "Mortars of alkali-activated blast furnace slag with high aggregate : binder ratios", Construction and Building Materials, Vol. 44, 2013, pp.607-614. https://doi.org/10.1016/j.conbuildmat.2013.03.057
  5. Chi, M., Huang, R., "Binding mechanism and properties of alkali-activated fly ash/slag mortars", Construction and Building Materials, Vol. 40, 2013, pp.291-298. https://doi.org/10.1016/j.conbuildmat.2012.11.003
  6. Collins, F., Sanjayan, J. G., "Effect of pore size distribution on drying shrinkage of alkali-activated slag concrete", Cement and Concrete Research, Vol. 30, 2000, pp.1401-1406. https://doi.org/10.1016/S0008-8846(00)00327-6
  7. Han, C. G., Shin, B. C., Kim, G. C., Lee, S. T., "Influence of Grading and Grade Shape in Aggregate on the Strength and Absorption of Cement Mortar Products", Journal of the Korea Concrete Institute, Vol. 12, No. 1, 2000, pp.45-51 (in Korean).
  8. Joseph, B., Mathew, G., "Influence of aggregate content on the behavior of fly ash based geopolymer concrete", Sharif University of Technology, Vol. 19, 2012, pp.1188-1194.
  9. Kang, S. T., Ryu, G. S., Koh, K. T., Lee, J. H., "Optimum Mix Design of Alkali-Activated Cement Mortar Using Bottom Ash as Binder", Journal of the Korea Concrete Institute, Vol. 23, No. 4, 2011, pp.487-494 (in Korean). https://doi.org/10.4334/JKCI.2011.23.4.487
  10. Kim, T. W., Park, H. J., Seo, K. Y., "Influence of Blended Activators on the Physical Properties of Alkali-activated Slag Mortar", Journal of the Korea Institute for Structural Maintenance and Inspection, Vol. 16, 2012, pp.26-33 (in Korean). https://doi.org/10.11112/jksmi.2012.16.6.026
  11. Lee, W. K. W., J. van Deventer, J. S., "The interface between natural siliceous aggregates and geopolymers", Cement and Concrete Research, Vol. 34, 2004, pp.195-206. https://doi.org/10.1016/S0008-8846(03)00250-3
  12. Lee, Y. J., Jee, N. Y., Kim, J. H., "The Experimental Study for Application of Alkali Activated Slag Concrete", Journal of the Architectural Institute of Korea, Vol. 23, No. 2, 2007, pp.99-106 (in Korean).
  13. Li, C., Sun, H., Li, L., "A review: The comparison between alkali-activated slag (Si+Ca) and metakaolin (Si+Al) cements", Cement and Concrete Research, Vol. 40, 2010, pp.1341-1349. https://doi.org/10.1016/j.cemconres.2010.03.020
  14. Neto, A. A. M, Cjncotto,M. A., Repette, W., "Drying and autogenous shrinkage of pastes and mortars with activated slag cement", Cement and Concrete Research, Vol. 38, 2008, pp.565-574. https://doi.org/10.1016/j.cemconres.2007.11.002
  15. Pacheco-Torgal, F., Castro-Gomes, J., Jalali, S., "Alkali-activated binders: A review: Part 1. Historical background, terminology, reaction mechanism and hydration products", Construction and Building Materials, Vol. 22, 2008, pp.1305-1314. https://doi.org/10.1016/j.conbuildmat.2007.10.015
  16. Pacheco-Torgal, F., Castro-Gomes, J., Jalali, S., "Investigations about the effect of aggregates on strength and microstructure of geopolymeric mine waste mud binders", Cement and Concrete Research, Vol. 37, 2007, pp.933-941. https://doi.org/10.1016/j.cemconres.2007.02.006
  17. Ruiz-Santaquiteria, C., Skibsted, J., Fernandez-Jimenez, A., Palomo, A., "Alkaline solution/binder ratio as a determining factor in the alkaline activation of aluminosilicates", Cement and Concrete Research, Vol. 42, 2012, pp.1242-1251. https://doi.org/10.1016/j.cemconres.2012.05.019
  18. Yang, K. H., Cho, A. R., Song, J. K., "Effect of water-binder ratio on the mechanical properties of calcium hydroxide-based alkali-activated slag concrete", Construction and Building Materials, Vol. 29, 2012, pp.504-511. https://doi.org/10.1016/j.conbuildmat.2011.10.062
  19. Yang, K. H., Song, J. K., Lee, K. S., Ashraf F. Ashour, "Flow and Compressive Strength of Alkali-Activated Mortars", ACI Materials Journal, Vol. 106, 2009, pp.50-57.

Cited by

  1. Influence of slag content and water-binder ratio on leaching behavior of cement pastes vol.129, 2016, https://doi.org/10.1016/j.conbuildmat.2016.11.003
  2. The Fundamental Study of Strength and Drying Shrinkage on Alkali-activated Slag Cement Mortar with Different Entering Point of Fine Aggregate vol.18, pp.2, 2014, https://doi.org/10.11112/jksmi.2014.18.2.117