Effect of metal alkoxide ratio and TiO2 composition on the synthesis of crystalline LAS glass by Sol-Gel method

졸-겔법에 의한 LAS계 결정화 유리합성에 미치는 금속 알콕사이드와 TiO2 조성비의 영향

  • Seo, Kwang-Seok (Department of Environmental & Energy Engineering, Department. of Chemistry, Gachon University) ;
  • Chun, Kyung-Soo (Department of Environmental & Energy Engineering, Department. of Chemistry, Gachon University)
  • 서광석 (가천대학교 환경에너지공학과, 나노화학과) ;
  • 전경수 (가천대학교 환경에너지공학과, 나노화학과)
  • Received : 2012.12.14
  • Accepted : 2013.06.04
  • Published : 2013.06.25
Download PDF
⟨ Previous Next ⟩

Abstract

For the synthesis of crystalline LAS glass by sol-gel method, the effect of operation conditions including metal alkoxide ratio, nucleating agent composition and heat treatment on the crystalline properties was experimentally investigated. The gelation time and crystallization temperature were proportionally affected by the mole ratio of TEOS in metal alkoxides solution. The addition of $TiO_2$ had an influence on the increasing of the gelation time, but the crystallization temperature was rarely dependent on the adding of nucleating agent. The crystallinity of LAS glass was improved by the nucleating agent under same heat treatment conditions.

졸-겔법에 의한 LAS계 결정화 유리합성공정에서 출발물질로 사용된 금속 알콕사이드의 조성비, 조핵제의 첨가량 및 열처리조건이 생성된 유리의 결정화 특성에 미치는 영향을 조사하였다. LAS 유리전구체의 겔화시간은 $TiO_2$의 첨가량이 늘어남에 비례하였고, 금속 알콕사이드 중의 TEOS의 몰비가 증가함에 따라서 폭발적으로 증가하였다. 또한 TEOS의 조성비가 커지면 LAS계 유리의 결정화 온도는 증가 하였지만, $TiO_2$ 첨가량의 영향은 미미하였다. 그리고 $TiO_2$의 첨가량이 늘어나면 낮은 온도에서도 결정성이 증가하는 것으로 나타나 이는 조핵제가 LAS계 결정화 유리의 결정성을 향상시키는 것으로 판단되었다.

Keywords

References

  1. K. S. Chun, Anal. Sci. Technol., 25, 3-6 (2012). https://doi.org/10.5806/AST.2012.25.1.003
  2. K. S. Chun and Y. H. Lee, Anal. Sci. Technol., 21(2), 123-128 (2008).
  3. M. A. Aegeter, Sol-Gel Science and Technology, World Sci., 137-139 (1989).
  4. J. S. Yang, J. Mat. Sci., 25, 1773-1778 (1990). https://doi.org/10.1007/BF01045383
  5. Y. W. Park, J. Korean Ceram. Soc., 29(6), 431-440 (1992).
  6. H. Dislish and P. Hinz, J. Non-Crystal. Solids, 48, 11-16 (1982). https://doi.org/10.1016/0022-3093(82)90242-3
  7. T. Lopez, M. Asomoza, L. Razo and R. Gomez, J. Non-Crystal. Solids, 108, 45-48 (1989). https://doi.org/10.1016/0022-3093(89)90331-1
  8. R. Roy and M. Della, J. Am. Ceram., Soc., 33(5), 152-159 (1950). https://doi.org/10.1111/j.1151-2916.1950.tb12780.x
  9. J. S. Yang, Science and Technology of New Glasses, p263-268 (1991).
  10. G. H. Beall and D. A. Duke, J. Mat. Sci., 4, 340-345 (1969). https://doi.org/10.1007/BF00550404
  11. J. M. Lee, Ph. D. Thesis, Yeonsei Univ., Seoul, Korea (1981).
  12. W. F. Mcclune, International Centre for Diffraction Data, JCPDS, (Pennsylvania), 1981.
  13. J. S. Yang and S. Sakka, J. Korean Ceram. Soc., 25, 541-551 (1988).
  14. W. T. Minehan, G. L. Messing and C. G. Pantanoet, J. Non-Crystal. Solids, 108, 163-168 (1989). https://doi.org/10.1016/0022-3093(89)90579-6