초록
In this study, $KNbO_3$-substituted (Li,Na,K)(Nb,Sb,Ta)$O_3$ ceramics were investigated to develop Pb-free composition ceramics for multilayer actuator and energy harvester applications. The X-ray diffraction analysis indicated that all samples were pure perovskite phase and no secondary phase was found. A tetragonality as a function of $KNbO_3$ substitution showed the maximum value at 1.5 mol% $KNbO_3$ and then decreased. The SEM image analysis showed the maximum grain size of $3.14{\mu}m$ at 1.5mol% $KNbO_3$. In the composition ceramics with 1.5 mol% $KNbO_3$ sintered at $1,100^{\circ}C$, excellent properties of density= 4.75 $g/cm^3$, electromechanical coupling factor ($k_p$)= 0.50 and piezoelectric constant($d_{33}$)= 290 pC/N were obtained, respectively, suitable for piezoelectric actuator and energy harvester applications.