Effect of Welding Parameters on Bead Shape, Microstructure and Hardness of Galvanized Steel Pipe Welds with GMAW

아연도금강관의 GMAW에서 용접변수가 비드형상과 미세조직과 경도에 미치는 영향

  • Lim, Young-Min (School of Energy.Materials·Chemical, Korea University of Technology and Education) ;
  • Lee, Wan Kyu (Korea Association of Machinery Industry) ;
  • Kim, Se-Cheol (Korea Specialty Contractor Financial Cooperative) ;
  • Koh, Jin-Hyun (School of Energy.Materials·Chemical, Korea University of Technology and Education)
  • 임영민 (한국기술교육대학교 에너지.신소재.화학공학부) ;
  • 이완규 (한국기계산업진흥회 기술교육원) ;
  • 김세철 (전문건설공제조합 기술교육원) ;
  • 고진현 (한국기술교육대학교 에너지.신소재.화학공학부)
  • Received : 2012.10.31
  • Accepted : 2013.02.06
  • Published : 2013.02.28

Abstract

The present study was carried out to investigate the effects of welding parameters such as current, voltage and shielding gases on the bead shape, microstructures and hardness. It was confirmed that bead height was lowered and bead depth was increased with increasing voltages while height, depth and width of beads increased with welding currents. The hardness of weld metals with Ar+10% $O_2$ and Ar+20% $CO_2$ was low due to the formation of grain boundary and polygonal ferrites while that of weld metals with Ar+2% $O_2$ was high due to the presence of acicular, bainitic and sideplate ferrites.

본 연구에서는 아연도금강관 용접에 용접 전류, 전압과 보호가스가 용접 비드 형상과 미세조직과 경도에 미치는 영향을 조사하였다. 전압, 전류과 보호가스 종류 및 조성의 변화가 용접 비드의 높이와 너비, 용입깊이에 영향을 미침을 확인하였다. 비드높이에는 보호가스 Ar 가스, 용입에는 $CO_2$ 가스, 그리고 비드너비에는 Ar+$O_2$ 가스가 가장 큰 영향을 미쳤다. 용접부의 경도에서는 Ar+10% $O_2$ 와 Ar+20% $CO_2$ 가스 사용 시 결정립계 페라이트와 다각형 페라이트가 생성되어 낮았으며, Ar+2% $O_2$ 가스를 사용했을 때는 아시큘러 페라이트와 베이나이트적 페라이트와 사이드플레이트 페라이트가 생성되어 경도가 높았다.

Keywords

References

  1. S. M. Cho, K. J. Kim and B. W. Lee, 'The Waveform Control and Blowhole Generation in the Wave Pulse MIG Welding for the Galvanized Steel Sheets', KWJS, Vol. 23, No. 1, pp. 69-76, February, 2005.
  2. H. Y. Park, S. H. Lee, G. W. Eum, 'A Study of Weld Pool Flow Considering the Molten Droplets Effect in GMAW', KWJS, Vol 16, No. 2, pp.40-47, 1998.
  3. J. H. Koh, G. S. Kim, J. H. kim, G. S. Bang, Y. M. Yun, B. Y. Lee, S. Y. Lee, 'Modern Welding Technology', Fifth Edition, (2002), 192-205
  4. J. H. Koh, H. G. Park, S. S. Kim, Y. H. Hwang, Y. S. Seo, 'Irradiation Behavior of Reactor Pressure Vessel SA508 class 3 Steel Weld Metals', KWJS, Vol 28, No. 5, pp.69-74, 2010. DOI : http://dx.doi.org/10.5781/KWJS.2010.28.5.069
  5. H. S. Jung, 'Fundamental of Fusion Welding - Shielding Gases for Arc Welding', KWJS, Vol 19, No. 2, pp.138-141, 2001.
  6. S. H. Lee, J. Y. Lee, J. S. Kim, and B. Y. Lee, 'The Effect of External Electromagnetic Force in GMAW', KSME, pp. 1741-1745. 2003.
  7. J. Y. Choi, 'Hand Book on the Strength of Weld Joints', Gold Publishing Co., No. 4, pp. 35-40, 1997.
  8. K. D. Kyung, H. J. Chon, J. H. Lee, B. Y. Kang and H. J. Kim, 'Effect of Shielding gas Composition on Arc Stability and Transfer Mode of High Deposition GMA Welding', KWJS, Vol. 15, No. 1. pp. 64-70, 1997.
  9. J. W. Lee, W. H. Song, D. H. Seo, J. S. Lee, 'Effect of Heat Input on Girth Welds Properties of High Strain Steel Pipe', KWJS, Vol. 27, No. 6. pp. 25-30, 2009. DOI : http://dx.doi.org/10.5781/KWJS.2009.27.6.025