Mechanical Properties of Forged Nimonic 80A Superalloy Fabricated by Vacuum Spray Casting

진공분무주조법에 의해 제조한 Nimonic 80A 초내열합금 단조재의 기계적 특성

  • Lee, Yun-Soo (School of Materials Science and Engineering, Inha University) ;
  • Hyun, Soong-Keun (School of Materials Science and Engineering, Inha University) ;
  • Jung, Dae-Hyun (Technical Research Laboratories, Glometal Co. Ltd.) ;
  • Byun, Joong-Sig (Technical Research Laboratories, Glometal Co. Ltd.)
  • 이윤수 (인하대학교 신소재공학부) ;
  • 현승균 (인하대학교 신소재공학부) ;
  • 정대현 ((주)글로메탈 기술연구소) ;
  • 변중식 ((주)글로메탈 기술연구소)
  • Received : 2011.10.10
  • Published : 2012.05.25
⟨ Previous Next ⟩

Abstract

This study investigates the effect of heat treatment on the mechanical properties of a forged Ni-based superalloy called Nimonic 80A. Nimonic 80A ingot samples were fabricated by vacuum spray casting to achieve a fine and homogenized microstructure. The ingot samples were subsequently hot-forged with the diameter of 220 mm at 1373 K. From the center to the surface of the forged Nimonic 80A, its average grain size decreased and its micro-Vickers hardness increased slightly. Solution treatment was carried out at 1353 K with 8 hours of air cooling followed by aging treatment, which was carried out in the range of 873-1073 K with various times from 0.5 to 256 hours. To set the optimum aging conditions, micro-Vickers hardness tests were performed. The maximum hardness value of 388.0 Hv was obtained by aging at 973 K for 32 hours. Also, tensile tests were performed for optimum aging conditions at room temperature and 873 K. The results can be used effectively to perform reasonable heat treatment of Nimonic 80A superalloy.

Keywords

Acknowledgement

Grant : 선박 엔진용 고균질 Ni계 초내열 부품소재

Supported by : 지식경제부

References

  1. S. Zhao, X. Xie, G. D. Smith, and S. J. Patel, Mater. Sci. Eng. A 355, 96 (2003). https://doi.org/10.1016/S0921-5093(03)00051-0
  2. A. Zielinski, H. Smolenska, W. Serbinski, W. Konczewicz, and A. Klimpel, J. Mater. Process. Technol. 164, 958 (2005).
  3. D. K. Kim, D. Y. Kim, S. H. Ryu, and D. J. Kim, J. Mater. Process. Technol. 133, 148 (2001).
  4. H. S. Jeong, J. R. Cho, and H. C. Park, J. Mater. Process. Technol. 162, 504 (2005).
  5. S. H. Kim, J. O. Ham, Y. B. Yun, and N. K. Park, J. Kor. Inst. Met. & Mater. 35, 1244 (1997).
  6. B. Tian, G. A. Zickler, C. Lind, and O. Paris, Acta Mater. 51, 4149 (2003). https://doi.org/10.1016/S1359-6454(03)00233-7
  7. N. D'Souza, R. Beanland, C. Hayward, and H. B. Dong, Acta Mater. 59, 1003 (2011). https://doi.org/10.1016/j.actamat.2010.10.031
  8. C. S. Han, C. H. Chun, and S. O. Han, J. Kor. Inst. Met. & Mater. 47, 11 (2009).
  9. Y. S. Na, I. S. Kim, S. M. Sohn, and N. K. Park, J. Kor. Inst. Met. & Mater. 37, 7 (1999).
  10. A. M. Brass, D. Roux, and J. Chene, Mater. Sci. Eng. A 323, 97 (2002). https://doi.org/10.1016/S0921-5093(01)01349-1
  11. K. Kakhi, Mater. Sci. Eng. A 278, 135 (2000). https://doi.org/10.1016/S0921-5093(99)00579-1
  12. K. G. Satyanarayana, S. N. Ojha, D. N. N. Kumar, and G. V. S. Sastry, Mater. Sci. Eng. A 304, 627 (2001).
  13. K. H. Baik, H. S. Kang, and H. K. Seok, J. Kor. Inst. Met. & Mater. 44, 329 (2006).
  14. A. K. Srivastava, R. C. Anandani, A. Dhar, and A. K. Gupta, Mater. Sci. Eng. A 304, 587 (2001).
  15. A. K. Srivastava, V. C. Srivastava, A. Gloter, and S. N. Ojha, Acta Mater. 54, 1741 (2006). https://doi.org/10.1016/j.actamat.2005.11.039
  16. T. Arai and S. Harper, Heat Treating. In:Metals Handbook Vol. 4, 796 ASM International, Metals Park, OH (1991).
  17. B. Cantor, K.H. Baik, and P.S. Grant, Prog. Mater. Sci. 42, 373 (1997). https://doi.org/10.1016/S0079-6425(97)00033-9
  18. D. H. Chang and S. I. Kang, Trans. of the KSME(A) 22, 767 (1998).
  19. J. W. Brooks, Mater. Des. 21, 297 (2000). https://doi.org/10.1016/S0261-3069(99)00069-2
  20. C. Stocker, M. Zimmermann and H. J. Christ, Int. J. Fatigue 33, 2 (2011). https://doi.org/10.1016/j.ijfatigue.2010.04.008
  21. M. V. Nathal, Metall. Trans. A 18, 1961 (1987). https://doi.org/10.1007/BF02647026
  22. Y. H. Park, Y. H. Park, I. M. Park, and K. M. Cho, Korean J. Met. Mater. 48, 957 (2010).
  23. Y. Xu, Q. Jin, X. Xiao, X. Cao, G. Jia, Y. Zhu, and H. Yin, Mater. Sci. Eng. A 528, 4600 (2011). https://doi.org/10.1016/j.msea.2011.02.072
  24. B. H. Kear and H. G. F. Wilsdorf, Trans. metall. Soc. AIME 224, 382 (1962).
  25. K. B. Rao, V. Seetharaman, S. L. Mannan and P. Rodriguez, J. Nucl. Mater. 102, 7 (1981). https://doi.org/10.1016/0022-3115(81)90540-7