EVALUATION OF GALVANIC CORROSION BEHAVIOR OF SA-508 LOW ALLOY STEEL AND TYPE 309L STAINLESS STEEL CLADDING OF REACTOR PRESSURE VESSEL UNDER SIMULATED PRIMARY WATER ENVIRONMENT

  • Received : 2011.09.22
  • Accepted : 2011.11.14
  • Published : 2012.10.25
Download PDF
⟨ Previous Next ⟩

Abstract

The article presented is concerned with an evaluation of the corrosion behavior of SA-508 low alloy steel (LAS) and Type 309L stainless steel (SS) cladding of a reactor pressure vessel under the simulated primary water chemistry of a pressurized water reactor (PWR). The uniform corrosion and galvanic corrosion rates of SA-508 LAS and Type 309L SS were measured in three different control conditions: power operation, shutdown, and power operation followed by shutdown. In all conditions, the dissimilar metal coupling of SA-508 LAS and Type 309L SS exhibited higher corrosion rates than the SA-508 base metal itself due to severe galvanic corrosion near the cladding interface, while the corrosion of Type 309L in the primary water environment was minimal. The galvanic corrosion rate of the SA-508 LAS and Type 309L SS couple measured under the simulated power operation condition was much lower than that measured in the simulated shutdown condition due to the formation of magnetite on the metal surface in a reducing environment. Based on the experimental results, the corrosion rate of SA-508 LAS clad with Type 309L SS was estimated as a function of operating cycle simulated for a typical PWR.

Keywords

References

  1. W.H. Bamford, R.D. Rishel, "A Review of Cracking Associated with Weld Deposited Cladding in Operating PWR Plants", WCAP-15338-A, Westinghouse (2002).
  2. W.H. Bamford, N.A. Palm, "Service Experience with Alloy 600 and Associated Welds in Operating PWRs, Including Repair Activities and Regulatory and Code Actions", Proc. 14th Int. Conf. on Env. Deg. of Mater. in Nucl. Power Syst., p. 1525, Virginia Beach, USA, Aug. 23-27, 2009.
  3. J.H. Park, O.K. Chopra, K. Natesan, W.J. Shack, "Boric Acid Corrosion of Light Water Reactor Pressure Vessel Materials", Proc. 12th Int. Conf. on Env. Deg. of Mater. in Nucl. Power Syst., p. 459, Salt Lake City, USA, Aug. 14- 18, 2005.
  4. A. Roth, E. Nowak, M. Widera, U. Ilg, U. Wesseling, R. Zimmer, "Recent In-Service Experience with Degradation of Low Alloy Steel Components Due to Localized Corrosion and Environmentally Assisted Cracking in German PWR Plants", Proc. 12th Int. Conf. on Env. Deg. of Mater. in Nucl. Power Syst., p. 795, Salt Lake City, USA, Aug. 14- 18, 2005.
  5. H. Xu, S. Fyfitch, J.W. Hyres, "Boric Acid Corrosion Laboratory Investigation of the Davis-Besse Reactor Pressure Vessel Head", Proc. 12th Int. Conf. on Env. Deg. of Mater. in Nucl. Power Syst., p. 855, Salt Lake City, USA, Aug. 14-18, 2005.
  6. A. Roth, J. Hickling, "Crack Initiation due to Environmentally Assisted Cracking in Carbon and Low-Alloy Steels Exposed to High-Temperature Water", Proc. 13th Int. Conf. on Env. Deg. of Mater. in Nucl. Power Syst., paper no. 29, Whistler, Canada, Aug. 19-23, 2007.
  7. S. Fyfitch, H. Xu, "Boric Acid Corrosion Laboratory Investigation of Carbon and Low-Alloy Steels in PWR Systems", Proc. 13th Int. Conf. on Env. Deg. of Mater. in Nucl. Power Syst., paper no. 70, Whistler, Canada, Aug. 19-23, 2007.
  8. ASME Section IX, "Qualification Standard for Welding and Brazing Procedures, Welders, Brazers, and Welding and Brazing Operators", BPVC-IX-2010 BPVC Section IX-Welding and Brazing Qualifications, NY, ASME International, 2010.
  9. D.A. Jones, Principles and Prevention of Corrosion, 2nd ed.. p. 31, Prentice Hall, Upper Saddle River (1996).
  10. D. Godfrey, "Iron Oxides and Rust (Hydrated Iron Oxides) in Tribology, Lub. Eng., 55, 33 (1999).

Cited by

  1. Dynamic Boric Acid Corrosion of Low Alloy Steel for Reactor Pressure Vessel of PWR using Mockup Test vol.12, pp.2, 2013, https://doi.org/10.14773/cst.2013.12.2.085