Abstract
There are many restrictions in conventional ways of Jewelry mass production which are Mokume Gane, Inlaid Technology based on a joining work of dissimilar metals. To overcome this, Multi-Casting using both Jewelry-Casting and CAD/CAM has presented. In experiment on Muti-Casting, second original sample which was produced by CAD/CAM is 5 % smaller than first one. The first and second castings are brass and silver, respectively. When making second sample, the temperature of flask was about $150{\sim}200^{\circ}C$ higher than the standard temperature of flask when making castings. Through the Multi-Casting, it was found that there was no trouble making dissimilar metals Jewelry which can be mass produced.
이종(異種)금속을 접합 가공하는 모꾸메가네기법, 상감기법 등의 기존 제작 방식은 주얼리 대량생산에 있어 표현 및 제작 상 많은 제한이 따른다. 이를 극복하기 위하여 기존의 정밀주조기법과 CAD/CAM방식을 융합한 다중(多重)주물 제작기법을 제시하였다. 주얼리 원본제작에 있어 CAD/CAM을 활용하여 2차 원본은 1차 원본보다 5 % 작게 제작하였다. 1차 황동 주조물에 2차로 은을 주조하여 실험하였으며, 2차 주조 시 통상적 주조의 플라스크 온도 보다 약 $150{\sim}200^{\circ}C$ 높게 주조하였다. 다중주물 방식을 통하여 대량생산이 가능한 이종(異種)금속의 주얼리를 손쉽게 제작할 수 있었다.