Abstract
Herein, life time prediction based on the deterioration of physical properties of chloroprene rubber (CR)aged by heat and seawater was performed. CR samples were experienced an accelerated test at $80^{\circ}C$, $100^{\circ}C$, $120^{\circ}C$ for heat aging, and $40^{\circ}C$, $60^{\circ}C$, $80^{\circ}C$ for seawater aging for 20,000 hrs. The change in tensile strength, maximum elongation,hardness was measured. As a result, the decrease in elongation was a major factor causing failure. The life time estimated using an Arrhenius model was 125 years at $23^{\circ}C$ for thermal aging and 9 years at $23^{\circ}C$ for seawater aging. SEM and elemental analysis reveal that cracks were generated and the content of oxygen was increased for CR agined by seawater. FT-IR spectrum shows the new C-O and C = O bonds were generated by the chemical reaction with seawater. Also, the glass transtion temperature was increased and the thermal decomposition was decreased by seawater aging.
본 연구에서는 클로로프렌 고무의 열 및 해수에 의한 노화 현상에 따른 물성 변화 및 사용 수명을 예측하였다. 가속 스트레스 수준은 열노화 $80^{\circ}C$, $100^{\circ}C$, $120^{\circ}C$, 해수침지노화 $40^{\circ}C$, $60^{\circ}C$, $80^{\circ}C$에서 2년 3개월(20,000Hr)동안 가속노화를 통해 인장시험을 수행하여 신장률, 인장강도, 경도를 통한 물성변화 측정을 하였다. 분석 결과신장율 저하가 가장 주된 고장지배모드임을 알 수 있었다. 아레누이스 식을 이용한 노화수명 예측 결과 열노화된 CR의 예측 수명은 $23^{\circ}C$에서 125년이며, 해수침지노화된 CR의 예측수명은 $23^{\circ}C$에서 9년이었다. SEM과 SEMEDS 분석 결과, 해수노화시편이 균열과 SEM-EDS에서는 산소의 농도가 증가하였으며, 이를 바탕으로 FT-IR에서는 해수와의 반응에 의하여 C-O와 C=O 결합이 생성되었음을 관찰하였다. 또한 DSC와 TGA 분석에서는 해수침지노화에 의하여 유리전이온도가 상승하며 분해온도가 낮아짐을 관찰하였다.