Abrasion Resistance and Surface Hardness of Gold Plated Carbonized Board

도금처리 탄화보드의 내마모성 및 표면경도

  • Hwang, Sung-Wook (Division of Wood Processing, Department of Forest Products, Korea Forest Research Institute) ;
  • Park, Sang-Bum (Division of Wood Processing, Department of Forest Products, Korea Forest Research Institute) ;
  • Lee, Won-Hee (Department of Wood Science & Technology, College of Agriculture & Life Science, Kyungpook National University)
  • 황성욱 (국립산림과학원 임산공학부 목재가공과) ;
  • 박상범 (국립산림과학원 임산공학부 목재가공과) ;
  • 이원희 (경북대학교 임산공학과)
  • Received : 2012.09.14
  • Accepted : 2012.10.16
  • Published : 2012.10.25
Download PDF
⟨ Previous Next ⟩

Abstract

This research was performed to evaluate surface performance of gold plated carbonized board. After the carbonization at $850^{\circ}C$, volume, weight, and density decreased by 65.25%, 71.35% and 17.64%, respectively. Abrasion resistance and surface hardness of non-carbonized board exhibited the highest values of 0.093 g/100 revolution and 26.43 N/$mm^2$, respectively. Gold plated carbonized board showed intermediate values, 0.587 g/100 revolution of abrasion resistance and 24.35 N/$mm^2$ of surface hardness. Carbonized board showed the lowest values, 0.863 g of abrasion resistance and 21.50 N/$mm^2$, of surface hardness. These results were thought to reflect propertional relationship between abrasion resistance and surface hardness. Abrasion resistance and surface hardness of carbonized board appeared able to be improved by surface treatment such as plating.