The Mechanical Properties of Porous Concrete using Recycled Asphalt Aggregate

아스팔트순환골재를 이용한 투수성 콘크리트의 역학적 특성

  • 이동욱 (제주대학교 토목공학과(해양과환경연구소)) ;
  • 윤중만 (안산공과대학 건설정보시스템과) ;
  • 김남식 (제주대학교 토목공학과) ;
  • 강영민 ((주)SM기술단)
  • Received : 2011.03.03
  • Accepted : 2011.03.23
  • Published : 2011.03.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, it is analyzed that mechanical properties and required strength of porous concrete according to the mixing ratio of cement, fine aggregate, and water/cement ratio in order to evaluate mechanical properties of porous concrete using recycled asphalt aggregate. Recycled asphalt aggregates of 13 mm were used without modification of aggregate grading to extend porous concrete application. The water/concrete ratio was poor mix and the range of compressive strength was 18.2 to 19.5 MPa. The average value of permeability showed 8.0E-02 cm/sec.

본 연구에서는 아스팔트순환골재를 이용한 투수성 콘크리트의 역학적 특성을 알아보기 위하여 투수성 콘크리트의 단위시멘트량, 잔골재 비율, 물시멘트(w/c)비의 혼합율 변화에 따른 역학적 특성과 구조체로서 요구되는 소요강도에 대하여 분석하고자 하였다. 순환골재의 사용성을 높이기 위하여 입도조정 없이 13mm 아스팔트순환골재를 사용하였으며, 물시멘트비는 빈배합이 되도록 결정하였다. 분석결과 압축강도는 18.2~19.5Mpa을 보였으며 투수계수는 평균적으로 8.0E-02cm/sec 값을 나타내었다.

Keywords

References

  1. 이용남 (2008), 투수콘크리트의 공극막힘현상에 의한 투수성 검토, 석사학위논문, 제주대학교, pp.48-62.
  2. 유승경 (2007), "순환골재를 이용한 투수성 콘크리트의 역학특성", 한국토목섬유학회논문집, 제6권, 제2호, pp.17-20.
  3. 환경부 (2007), 2006년도 건설폐기물 재활용통계조사 보고서, 환경부 보고서, pp.1-239.
  4. Braja M. Das (2006), Principles of Geotechnical Engineering, 구미서관, 서울.