Development of Fabrication Method for Translucent Concrete and the Material Characteristics Associated with the Use of Mineral Admixture

반투명 콘크리트의 제조기법 개발과 무기혼화재 혼입에 따른 역학적 특성

As recent concrete products changed to pursue high class, high quality, and high strength, as translucent concrete was developed to meet esthetic effects and exhibition purpose of structures. This study aims at introducing fabrication methods of various shapes of translucent concrete and evaluating feasibility of using mineral admixture such as fly ash, ground granulated blast furnace slag and granulated glass throughout experimental tests. As the result, it was found that compressive strength of translucent concrete block at 28 days is 32.2MPa and higher elastic modulus and Poisson's ratio than ordinary concrete block, which means that translucent concrete is widely applicable to structural purpose. Application of fly ash as a replacement of cement showed lower strength of 85 to 96% than Portland cement. In the meanwhile, ground granulated blast furnace slag showed 82 to 96% depending on the amount of replacement. The use of granulated glass as replacement of optical fiber was not applicable due to invisibility of light in concrete.

최근 콘크리트제품에 대한 고급화, 고품질화 및 고강도화 등의 추구로 변화함에 따라 구조물의 미적효과와 전시 목적의 제품 고급화를 위해 반투명 콘크리트를 제작하였다. 본 연구에서는 반투명 콘크리트의 제조기법 개발을 통해 다양한 형상의 블록 제조방식을 소개하고, 또한 반투명 콘크리트의 물성 평가와 더불어 경제적인 반투명 콘크리트 제조를 위해 무기혼화재인 고로슬래그와 플라이애시의 활용 및 유리알갱이의 적용방안에 대해 검토하였다. 물성평가 결과, 반투명 콘크리트 블록의 28일 압축강도는 32.2MPa이고 탄성계수와 푸아송비는 일반 콘크리트 블록에 비해 증가되어 압축을 받는 부재일 경우 일반 콘크리트 구조물과 같이 구조적 용도로도 사용이 가능하다는 것을 알 수 있었다. 시멘트 대체재로써 플라이애시 적용하였을 때 동일 양의 광섬유를 포함한 반투명 콘크리트 블록의 28일 강도의 85~96%의 값을 보였으며, 고로슬래그 미분말을 적용하였을 때에는 82~96%의 값을 보였다. 또한, 광섬유대체재로서 유리알갱이를 적용한 결과, 빛의 투과효과가 전혀 나타나지 않아 대체효과가 전혀 없는 것으로 나타났다.